Niobium powder, sintered body thereof and capacitor using the same

[0001] 1. Technical Field to Which the Invention Belongs

[0002] The present invention relates to a niobium powder capable of producing a capacitor having a large capacitance per unit mass and good heat resistance property, and also relates to a sintered body using the powder and a capacitor using the sintered body.

[0003] 2. Background Art

[0004] Capacitors for use in electronic instruments such as potable telephone and personal computer are demanded to have a small size and a large capacitance. Among these capacitors, a tantalum capacitor is preferred because of its large capacitance for the size and good performance. In this tantalum capacitor, a sintered body of tantalum powder is generally used for the anode material. In order to increase the capacitance of the tantalum capacitor, it is necessary to increase the mass of the sintered body or use a sintered body increased in the surface area by pulverizing the tantalum powder.

[0005] The method of increasing the mass of the sintered body necessarily involves enlargement of the capacitor shape and cannot satisfy the requirement for downsizing. On the other hand, in the method of pulverizing tantalum powder to increase the specific surface area, the pore size of the tantalum sintered body decreases or closed pores increase at the stage of sintering and this makes it difficult to impregnate a cathode agent in the later step. As one of means for solving these problems, a capacitor using a sintered body of a material having a dielectric constant larger than that of tantalum is being studied. Niobium is known as the material having a larger dielectric constant. Niobium and tantalum belong to the same group and therefore, tantalum is present as an impurity in niobium.

[0006] JP-A-13-307963 (the term JP-A as used herein means an unexamined published Japanese patent application) discloses that when a niobium powder is purified to obtain a niobium powder reduced in the tantalum content to 700 mass ppm or less, and a sintered body and then a capacitor are produced using this powder, the CV value or capacitance is not decreased. However, if a purification step is provided in the production process, the production time of niobium powder is prolonged or the recovery decreases.

[0007] An object of the present invention is to provide a capacitor having a large capacitance per unit mass and good heat resistance property, a sintered body of giving the capacitor, and a niobium powder of giving the sintered body.

[0008] As a result of extensive investigations, the present inventors have found that the above-described object can be attained by adjusting the niobium powder composition to a specific range of not necessarily requiring the purification of the niobium powder.

[0009] More specifically, the present invention relates to the following inventions.

[0010] (1) A niobium powder having Mg and Zr contents each of 50 to 400 mass ppm, a W content of 20 to 200 mass ppm and a Ta content of 300 to 3,000 mass ppm, with the contents of elements other than oxygen, nitrogen, hydrogen, Mg, Zr, W and Ta, each being 50 mass ppm or less.

[0011] (2) The niobium powder as described in 1 above, wherein the oxygen content is from 4,000 to 100,000 mass ppm.

[0012] (3) The niobium powder as described in 1 or 2 above, wherein the nitrogen content is from 20 to 200,000 mass ppm.

[0013] (4) The niobium powder as described in 1 to 3 above, wherein the hydrogen content is from 5 to 200 mass ppm.

[0014] (5) The niobium powder as described in 1 to 4 above, wherein the average particle size of primary powder is from 0.1 to 5 m.

[0015] (6) The niobium powder as described in 5 above, wherein the average particle size of secondary powder obtained by granulating the primary powder is from 50 to 300 m.

[0016] (7) The niobium powder as described in 1 to 6 above, wherein the BET specific surface area is from 0.5 to 40 m²/g.

[0017] (8) The niobium powder as described in 1 to 7 above, wherein the CV value is from 80,000 to 200,000 FV/g.

[0018] (9) A sintered body using the niobium powder described in any one of 1 to 8 above.

[0019] (10) The sintered body as described in 9 above, wherein the specific surface area is from 0.5 to 7 m²/g.

[0020] (11) A capacitor comprising the niobium sintered body described in 9 or 10 above as one part electrode, a dielectric material formed on the surface of the sintered body, and another part electrode provided on the dielectric material.

[0021] (12) The capacitor as described in 11 above, wherein the dielectric material mainly comprises niobium oxide.

[0022] (13) The capacitor as described in 11 above, wherein the another part electrode is at least one material selected from the group consisting of an electrolytic solution, an organic semiconductor and an inorganic semiconductor.

[0023] (14) The capacitor as described in 13 above, wherein the another part electrode is an organic semiconductor and the organic semiconductor is at least one material selected from the group consisting of an organic semiconductor comprising a benzopyrroline tetramer and chloranile, an organic semiconductor mainly comprising tetrathiotetracene, an organic semiconductor mainly comprising tetracyanoquino-dimethane, and an electrically conducting polymer.

[0024] (15) The capacitor as described in 14 above, wherein the electrically conducting polymer is at least one member selected from polypyrrole, polythiophene, polyaniline and substitution derivatives thereof.

[0025] (16) The capacitor as described in 14 above, wherein the electrically conducting polymer is an electrically conducting polymer obtained by doping a dopant into a polymer comprising a repeating unit represented by the following formula (1) or (2):

[0026] Chem.1

[0027] (wherein R¹ to R⁴ each independently represents a monovalent group selected from the group consisting of a hydrogen atom, a linear or branched, saturated or unsaturated alkyl, alkoxy or alkylester group having from 1 to 10 carbon atoms, a halogen atom, a nitro group, a cyano group, a primary, secondary or tertiary amino group, a CF₃ group, a phenyl group and a substituted phenyl group; the pair of hydrocarbon chains R¹ and R² and the pair of hydrocarbon chains R³ and R⁴ each may combine at an arbitrary position to form a divalent chain for forming at least one 3-, 4-, 5-, 6- or 7-membered saturated or unsaturated hydrocarbon cyclic structure together with the carbon atoms substituted by these groups; the cyclic bond chain may contain a bond of carbonyl, ether, ester, amide, sulfide, sulfinyl, sulfonyl or imino at an arbitrary position; X represents an oxygen atom, a sulfur atom or a nitrogen atom; R⁵ is present only when X is a nitrogen atom, and independently represents hydrogen or a linear or branched, saturated or unsaturated alkyl group having from 1 to 10 carbon atoms).

[0028] (17) The capacitor as described in 16 above, wherein the electrically conducting polymer is an electrically conducting polymer comprising a repeating unit represented by the following formula (3):

[0029] Chem. 2

[0030] (wherein R⁶ and R⁷ each independently represents a hydrogen atom, a linear or branched, saturated or unsaturated alkyl group having from 1 to 6 carbon atoms, or a substituent for forming at least one 5-, 6- or 7-membered saturated hydrocarbon cyclic structure containing two oxygen elements when the alkyl groups are combined with each other at an arbitrary position; and the cyclic structure includes a structure having a vinylene bond which may be substituted, and a phenylene structure which may be substituted).

[0031] (18) The capacitor as described in 14 above, wherein the electrically conducting polymer is an electrically conducting polymer obtained by doping a dopant to poly (3,4-ethylenedioxythiophene).

[0032] (19) The capacitor as described in 11 above, wherein the another part electrode is formed of a material having at least partially a layer structure.

[0033] (20) The capacitor as described in 11 above, wherein the another part electrode is a material containing an organic sulfonate anion as a dopant.

[0034] (21) An electronic circuit using the capacitor described in any one of 11 to 20 above.

[0035] (22) An electronic instrument using the capacitor described in any one of 11 to 20 above.

[0036] One embodiment for obtaining the niobium powder of the present invention is described below.

[0037] For the production of the niobium powder of the present invention, a generally available niobium raw material can be used. For example, the niobium powder of the present invention can be obtained by reducing niobium halide with magnesium or sodium, reducing potassium niobium fluoride with sodium, electrolyzing potassium niobium fluoride with a molten salt (NaClKCl) on a nickel cathode, reducing niobium pentoxide with an alkali metal, an alkaline earth metal, a carbon or a hydrogen, or introducing hydrogen into a niobium ingot and then pulverizing/dehydrogenating the ingot.

[0038] The niobium powder of the present invention has a tantalum content of 300 to 3,000 mass ppm (usually from 700 to 3,000 mass ppm but may be from 300 to 700 mass ppm).

[0039] By controlling the contents of specific elements described later to respective specific ranges, the CV value or capacitance of the sintered body or capacitor using the niobium power can be prevented from reduction without intentionally reducing the tantalum content to 700 mass ppm or less as described in JP-A-13-307963. Furthermore, the capacitor using the niobium powder advantageously exhibits a good value in the high-temperature load test.

[0040] The niobium powder of the present invention comprises Mg and Zr each in a content of 50 to 400 mass ppm and W in a content of 20 to 200 mass ppm. The contents of elements other than oxygen, nitrogen, hydrogen, Mg, Zr, W and Ta each is 50 mass ppm or less. If the contents of these elements are out of their respective ranges, it is difficult to maintain good results in all of those CV value, capacitance and high-temperature load test value.

[0041] The niobium powder comprising Mg, Zr and W elements in those contents of the present invention may be obtained, for example, by mixing respective elements or a compound containing these elements with the above-described niobium powder. Niobium powder generally obtained scarcely comprises Mg and Zr each in a content of 400 mass ppm, W in a content of 200 mass ppm or more, Ta in a content of 3,000 mass ppm or more, and elements other than oxygen, nitrogen, hydrogen, Mg, Zr, W and Ta, each in a content of 50 mass ppm. For obtaining the niobium powder of the present invention, this may be attained by adding Mg, Zr and W and the niobium powder need not be purified, therefore, the niobium powder can be produced in a high yield without spending much time.

[0042] As for the timing of adding these elements to the niobium powder, the elements may be added after the production of the above-described powder or at an arbitrary stage during the production, however, the preferred timing for mixing is desirably determined in advance by a preliminary test. Also, at least one apparatus for obtaining the niobium powder may be made of a construction material containing those specific elements and designed such that the elements each in a predetermined amount are mixed in the niobium powder by the abrasion with the apparatus at the production of niobium powder.

[0043] The niobium powder obtained as such usually contains hydrogen and carbon each in a content of 5 to 200 mass ppm. The niobium powder of the present invention forms a natural oxide film in air at room temperature. In this case, the amount of oxygen contained is usually from 4,000 to 100,000 mass ppm, though this varies depending on the particle size of niobium powder. The oxygen content may be decreased by reducing the natural oxide film of niobium using a reducing agent such as magnesium, calcium or hydrogen. For example, a niobium powder having an oxygen content of 8,000 mass ppm or 80,000 mass ppm may be reduced to obtain a niobium powder having an oxygen content of 5,000 mass ppm.

[0044] In the present invention, the niobium powder and/or the secondary powder which is described later may be partially nitrided before use. The niobium powder can be partially nitrided, for example, by nitriding the niobium powder in a nitrogen gas atmosphere. In this case, the amount of nitrogen is preferably set to 20 to 200,000 mass ppm and for producing a capacitor having a good leakage current value, more preferably from 100 to 30,000 mass ppm. The nitrided amount as used herein means the amount of nitrogen chemically bonded to the niobium powder but not the amount of nitrogen adsorbed to the niobium powder.

[0045] The nitridation of the niobium powder may be performed by any one of liquid nitridation, ion nitridation and gas nitridation or by a combination of these methods. The gas nitridation in a nitrogen gas atmosphere is preferred because the apparatus is simple and the operation is easy. For example, the gas nitridation in a nitrogen gas atmosphere can be attained by allowing the niobium powder to stand in a nitrogen gas atmosphere. A niobium powder having an objective nitrided amount can be obtained by the nitridation at an atmosphere temperature of 2,000 C. or less for a standing time of several hours or less. The treatment time can be shortened by treating the niobium powder at a higher temperature. The nitrided amount of the niobium powder can be controlled under the conditions determined by a preliminary test for confirming the nitridation temperature and nitridation time of the material to be nitrided.

[0046] The average particle size of the powder of the present invention is from 0.1 m to less than 5 m, preferably from 0.2 m to less than 2 m. If the average particle size is 5 m or more, the sintered body obtained itself has a small CV value and a capacitor having a large capacitance cannot be produced, therefore, this is not preferred, whereas if it is less than 0.1 m, the another electrode material cannot be easily impregnated and the capacitance is disadvantageously rather decreased. The powder of the present invention having an average particle size within the above-described range has a specific surface area of 0.5 to 40 m²/g. The powder for capacitors of the present invention may be granulated to a predetermined size and used in the form a secondary powder.

[0047] The granulation may be performed by a conventionally known method. Examples of the method include a method where the powder is left standing in a vacuum at a high temperature of 500 to 2,000 C. and then subjected to wet or dry cracking, a method where the powder is mixed with an appropriate binder such as acrylic resin or polyvinyl alcohol and then cracked, and a method where the powder is mixed with an appropriate compound such as acrylic resin or camphor, left standing in a vacuum at a high temperature and then subjected to wet or dry cracking. The particle size of the granulated powder can be freely varied by the degree of granulation and cracking, however, a granulated powder having an average particle size of 50 to 300 m is usually used. After the granulation and cracking, the powder may be classified. Also, an appropriate amount of the powder before granulation may be added to the granulated powder. The granulated powder produced as such usually has a BET specific surface area of 0.4 to 20 m²/g.

[0048] When a sintered body is produced from the niobium powder of the present invention as described later and electrochemically formed in an aqueous 0.1% phosphoric acid solution at 80 C. and a predetermined voltage for 300 minutes, the sintered body exhibits a CV value of 80,000 to 200,000 FV/g (this is a value measured in a 30% aqueous solution of sulfuric acid at room temperature and 120 Hz with 1.5 V bias for 30 seconds).

[0049] The sintered body of the present invention can be produced by sintering the above-described powder. One example of the production method for the sintered body is described below, however, the production method of the sintered body is not limited to this example. For example, the sintered body is obtained by press-molding the powder into a predetermined shape and heating the molded article at 500 to 2,000 C. under 10¹ to 10⁴ Pa for a few minutes to a few hours. The sintered body of the present invention usually has a specific surface area of 0.5 to 7 m²/g.

[0050] By preparing a lead wire comprising a valve-acting metal such as niobium or tantalum and having an appropriate shape and an appropriate length, the lead wire may be integrally molded at the press-molding of the powder while inserting a part of the lead wire inside the molded article, so that the lead wire can work out to an outgoing lead of the sintered body.

[0051] Using the above-described sintered body as one part electrode, a capacitor can be produced by interposing a dielectric material between this one part electrode and another part electrode (counter electrode). Examples of the dielectric material of the capacitor include dielectric materials mainly comprising niobium oxide or tantalum oxide. The dielectric material mainly comprising niobium oxide can be obtained, for example, by electrochemically forming the niobium sintered body as one part electrode in an electrolytic solution. For electrochemically forming the niobium electrode in an electrolytic solution, an aqueous protonic acid solution is generally used, such as an aqueous 0.1% acetic acid or sulfuric acid solution. In the case of obtaining a dielectric material mainly comprising niobium oxide by electrochemically forming the niobium electrode in an electrolytic solution, the capacitor of the present invention is an electrolytic capacitor and the niobium side serves as an anode.

[0052] The another part electrode in the capacitor of the present invention is at least one compound selected from an organic semiconductor and an inorganic semiconductor. Specific examples of the organic semiconductor include an organic semiconductor comprising a benzopyrroline tetramer and chloranile, an organic semiconductor mainly comprising tetrathiotetracene, an organic semiconductor mainly comprising tetracyanoquinodimethane, and an organic semiconductor mainly comprising an electrically conducting polymer obtained by doping a dopant into a polymer comprising a repeating unit represented by following formula (1) or (2):

[0053] Chem. 3

[0054] wherein R¹ to R⁴₁, which may be the same or different, each represents hydrogen, an alkyl group having from 1 to 6 carbon atoms or an alkoxy group having from 1 to 6 carbon atoms, X represents an oxygen atom, a sulfur atom or a nitrogen atom, R⁵ is present only when X is a nitrogen atom, and represents hydrogen or an alkyl group having from 1 to 6 carbon atoms, and each of the pairs R¹ and R², and R³ and R⁴ may combine with each other to be cyclic.

[0055] In the present invention, the electrically conducting polymer comprising a repeating unit represented by formula (1) is preferably an electrically conducting polymer comprising a structure unit represented by the following formula (3) as a repeating unit:

[0056] 4

[0057] wherein R⁶ and R⁷ each independently represents a hydrogen atom, a linear or branched, saturated or unsaturated alkyl group having from 1 to 6 carbon atoms, or a substituent for forming at least one 5-, 6- or 7-membered saturated hydrocarbon cyclic structure containing two oxygen elements when the alkyl groups are combined with each other at an arbitrary position; and the cyclic structure includes a structure having a vinylene bond which may be substituted, and a phenylene structure which may be substituted. The electrically conducting polymer containing such a chemical structure is electrically charged and a dopant is doped thereto. For the dopant, known dopants can be used without limitation.

[0058] Examples of the polymer containing a repeating unit represented by any one of formulae (1) to (3) include polyaniline, polyoxyphenylene, polyphenylene sulfide, polythiophene, polyfuran, polypyrrole, polymethylpyrrole, and substitution derivatives and copolymers thereof. Among these, preferred are polypyrrole, polythiophene and substitution derivatives thereof (e.g., poly(3,4-ethylenedioxythiophene)).

[0059] Specific examples of the inorganic semiconductor include an inorganic semiconductor mainly comprising lead dioxide or manganese dioxide, and an inorganic semiconductor comprising tri-iron tetroxide. These semiconductors may be used individually or in combination of two or more thereof.

[0060] When the organic or inorganic semiconductor used has an electrical conductivity of 10² to 10³ S/cm, the produced capacitor can have a smaller impedance value and can be more increased in the capacitance at a high frequency.

[0061] In the case where the another part electrode is solid, an electrically conducting layer may be provided thereon so as to attain good electrical contact with an exterior outgoing lead (for example, lead frame). The electrically conducting layer can be formed, for example, by the solidification of an electrically conducting paste, plating, metallization or formation of a heat-resistant electrically conducting resin film. Preferred examples of the electrically conducting paste include silver paste, copper paste, aluminum paste, carbon paste and nickel paste, and these may be used individually or in combination of two or more thereof. In the case of using two or more kinds of pastes, the pastes may be mixed or may be superposed one on another as separate layers. The electrically conducting paste applied is then solidified by allowing it to stand in air or under heating. Examples of the plating include nickel plating, copper plating, silver plating and aluminum plating. Examples of the vapor-deposited metal include aluminum, nickel, copper and silver.

[0062] More specifically, for example, carbon paste and silver paste are stacked in this order on the another part electrode and the whole is molded with a material such as epoxy resin, thereby fabricating a capacitor. The capacitor may have a niobium or tantalum lead which is sintered and molded integrally with the above-described sintered body or welded afterward.

[0063] The thus-fabricated capacitor of the present invention is jacketed using, for example, resin mold, resin case, metallic jacket case, dipping of resin or laminate film, and then used as a capacitor product for various uses.

[0064] The present invention is described in greater detail below by referring to Examples.

[0065] The nitrided amount of the powder of the present invention was determined using a nitrogen-oxygen analyzer manufactured by LEKO. The CV value of the sintered body was determined from a product of an electrical formation voltage of 20 V and a capacitance measured in 30% sulfuric acid after the electrochemical formation in an aqueous 0.1% phosphoric acid solution at 80 C. for 300 minutes with an applied voltage of 20 V. As for the contents of elements other than oxygen and nitrogen in the niobium powder, Si and P were determined from ICP-AES, C and S were determined from high-frequency combustion/IR, and other elements were determined from ICP-AES. The high-temperature load test value of the capacitor was expressed by the number of units of which capacitance exceeded 20% of the initial value when the produced capacitor was left standing at 85 C. and 4V for 1,000 hours. The number of samples for the determination of CV value and high-temperature load test value of the capacitor using the niobium powder was 30 in each Example.

[0066] A niobium ingot having a Ta content of 1,200 mass ppm was hydrogenated and then wet pulverized to obtain a niobium powder having an average particle size of 0.78 m and a specific surface area of 4.6 m²/g. Thereto, magnesium, zirconium oxide and ammonium tungstate were added to have Mg, Zr and W contents shown in Table 1. This powder was vacuum-heated at 1,200 C., taken out, cracked and classified to obtain a granulated powder (also called a secondary powder) having an average particle size of 90 m and a specific surface area of 1.5 m²/g. This granulated particle was left standing in a nitrogen stream at 400 C. for 3 hours, thereby obtaining a partially nitrided niobium powder. The contents of respective elements in the obtained niobium powder were such that nitrogen was 2,500 mass ppm, oxygen was 32,000 mass ppm, hydrogen was 100 mass ppm, and the element other than oxygen, nitrogen, hydrogen, Mg, Zr, W and Ta was 40 mass ppm. This granulated powder was molded into a size of 1.83.54.0 mm (a niobium wire having a diameter of 0.3 mm was molded together and used as the lead) and then sintered at 1,300 C. under reduced pressure of 710⁵ Pa to obtain a sintered body having a specific surface area of 0.8 m²/g (the CV value of this sintered is shown in Table 1). Then, the sintered body was electrochemically formed in an aqueous 0.1% phosphoric acid solution at 80 C. and 20 V for 300 minutes. Subsequently, polypyrrole was deposited in pores inside the sintered body and on the surface thereof by repeating a reaction between pyrrole and an oxidizing agent in the presence of a dopant using ammonium persulfate as the oxidizing agent and sodium anthraquinonesulfonate as the dopant, and thereby another part electrode was formed. Furthermore, carbon paste and silver paste were stacked in this order and the whole was molded with an epoxy resin to produce a capacitor. The measured values of Examples and Comparative Examples are shown in Table 1.

[0067] Capacitors were produced in the same manner as in Examples 1 to 3 and Comparative Examples 1 to 3 except that niobium ingots each having a tantalum content shown in Table 1 were used and another part electrode composed of a lead dioxide and lead sulfate mixture containing 98 mass % of lead oxide was formed by repeating a reaction between an aqueous lead acetate solution and an aqueous ammonium persulfate solution in pores of the sintered body. In Comparative Examples 10, 11 and 12, Mg, Zr and W each was added to have the same content as in Examples 1, 2 and 3.

[0068] The same procedure as in Examples 1 to 5 and Comparative Examples 1 to 3 was performed except that the niobium powder was produced by reducing niobium penta-chloride having mixed therein 0.5% of tantalum penta-chloride using magnesium, and nitrided by allowing it to stand in a nitrogen stream at 450 C. for 3 hours.

[0069] The niobium powder obtained had an average particle size of 0.53 to 0.78 m and a specific surface area of 7.1 m²/g, and the granulated powder obtained had an average particle size of 120 m and a specific surface area of 1.7 m²/g. The content of nitrogen was 8,500 mass ppm, the content of oxygen was 9,000 mass ppm, the content of hydrogen was 140 mass ppm, and the contents of elements other than oxygen, nitrogen, hydrogen, Mg, Zr, W and Ta each was 40 mass ppm. The sintered body had a specific surface area of 1.3 m²/g. Using the sintered body obtained, capacitors were produced in the same manner as in Examples 1 to 5 and Comparative Examples 1 to 3.

	TABLE 1
	Contents of Elements		Capacitance	Value of High-
	in Niobium Powder,		of	Temperature
	mass ppm	CV Value,	Capacitor,	Load Test,
	Ta	Mg	Zr	W	FV/g	F	units
Example 1	1200	50	50	25	86000	300	0/30
Example 2	1200	190	150	59	87000	310	0/30
Example 3	1200	220	190	90	86000	305	0/30
Example 4	1200	340	220	190	86000	300	0/30
Example 5	1200	190	380	80	85000	305	0/30
Comparative	1200	420	190	120	86000	295	4/30
Example 1
Comparative	1200	160	410	30	86000	290	2/30
Example 2
Comparative	1200	220	160	220	85000	290	6/30
Example 3
Example 6	350	55	50	30	84000	300	0/30
Example 7	350	200	150	65	85000	305	0/30
Example 8	350	220	180	90	86000	310	0/30
Comparative	350	430	190	120	84000	300	3/30
Example 4
Comparative	350	230	160	220	84000	3100	2/30
Example 5
Example 9	2200	60	60	30	86000	310	0/30
Example 10	2200	190	160	60	85000	300	0/30
Example 11	2200	230	210	90	84000	310	0/30
Comparative	2200	430	180	110	86000	300	3/30
Example 6
Comparative	2200	230	160	220	85000	295	4/30
Example 7
Example 12	2900	55	55	30	86000	315	0/30
Example 13	2900	200	160	65	86000	315	0/30
Example 14	2900	230	180	90	86000	315	0/30
Comparative	2900	440	180	130	85000	295	3/30
Example 8
Comparative	2900	230	160	230	86000	295	4/30
Example 9
Comparative	3300	60	55	30	77000	260	3/30
Example 10
Comparative	3300	210	170	70	76000	255	3/30
Example 11
Comparative	220	240	180	100	86000	260	5/30
Example 12
Example 15	1300	53	57	28	138000	475	0/30
Example 16	1300	190	160	65	135000	475	0/30
Example 17	1300	245	190	90	136000	480	0/30
Example 18	1300	330	210	189	137000	480	0/30
Example 19	1300	185	390	85	138000	470	0/30
Comparative	1300	410	140	110	137000	460	2/30
Example 13
Comparative	1300	180	430	90	138000	465	3/30
Example 14
Comparative	1300	220	160	225	137000	460	3/30
Example 15

[0070] From comparison of Examples 1 to 5 with Comparative Examples 1 to 3, comparison of Examples 6 to 8 with Comparative Examples 4 and 5, comparison of Examples 9 to 11 with Comparative Examples 6 and 7, comparison of Examples 12 to 14 with Comparative Examples 8 and 9 and comparison of Examples 15 to 19 with Comparative Examples 13 to 15, and from results in Comparative Examples 10 to 12, it is seen that the sintered body and capacitor produced from a niobium powder where the contents of specific metals are controlled to respective specific amounts exhibit good results in the CV value, capacitance and high-temperature load test value, namely, heat resistance.

[0071] A niobium powder for capacitors, which can be produced in a high yield without spending much time, is provided and a capacitor having a large capacitance per unit mass and good heat resistance property can be produced by using this powder in the capacitor.