Hard film and hard film-coated tool

[0001] The present invention relates to a hard film having excellent wear resistance, adhesion and high-temperature oxidation resistance, which is formed on cemented carbide, high-speed steel, die steel, etc., particularly to a hard film for being formed on wear-resistant members requiring high hardness such as cutting tools, forming dies, bearings, dies and rolls, and heat-resistant members such as internal combustion engine parts. The present invention also relates to a tool coated with such a hard film.

[0002] As hard films having high-temperature oxidation resistance, various hard films of AlCr were proposed. Japanese Patent 3027502 discloses a wear-resistant amorphous hard film with high-hardness having a composition represented by the general formula of (Al_aM_b)_100-cX_c, wherein M is at least one element selected from the group consisting of Ti, Ta, V, Cr, Zr, Nb, Mo, Hf, W. Fe, Co, Ni, Cu and Mn, X is at least one element selected from the group consisting of N, O and C, and a, b and c are atomic % meeting 60% 98.5%, 1.5%b40%, 0%<c65%, and a b100%. However, this amorphous film has a Knoop hardness of about 21 GPa at most, insufficient in wear resistance and adhesion.

[0003] Japanese Patent 3039381 discloses a method comprising generating a vapor mixture of Al and Cr from a target composed of 25-50 atomic % of Al and 75-50 atomic % of Cr disposed in a vacuum chamber by arc discharge, and simultaneously introducing a nitrogen gas into the vacuum chamber to cause a reaction between the vapor mixture and the nitrogen gas, thereby forming an AlCrN composite hard film having excellent high-temperature oxidation resistance that prevents oxidation even at 800-900 C. on a substrate. Also, JP 2002-160129 A discloses a method for surface-treating a tool, comprising forming an intermediate layer of Ti, Cr, Si or Al on a substrate surface, and coating the intermediate layer with a hard film of AlCrN. These hard films are made of AlCr nitride having a high-temperature oxidation resistance of about 1000 C. However, they do not have oxidation resistance exceeding 1000 C. Further, these hard films had as insufficient hardness Hv as about 21 GPa, poor in wear resistance.

[0004] Accordingly, an object of the present invention is to provide a hard film having excellent adhesion, hardness, high-temperature oxidation resistance and wear resistance.

[0005] Another object of the present invention is to provide a tool coated with such a hard film.

[0006] The first hard film of the present invention is formed by an arc-discharge ion-plating method, and has a composition comprising metal components represented by Al_xCr_1-x, wherein x is an atomic ratio meeting 0.45x0.75, and non-metal components represented by N_1---BCO, wherein , and are respectively atomic ratios meeting 0 50.15, 00.3, and 0.010.25, with the maximum X-ray diffraction intensity in a (200) face or a (111) face, and with the binding energy of Al and/or Cr to oxygen in a range of 525-535 eV in an X-ray photoelectron spectroscopy.

[0007] In the first hard film, x is preferably 0.5-0.7. is preferably 0-0.12, more preferably 0-0.08. is preferably 0-0.2, more preferably 0-0.1. is preferably 0.01-0.2.

[0008] The second hard film of the present invention is formed by an arc-discharge ion-plating method, and has a composition comprising metal components represented by Al_xCr_1-x-ySi_y wherein x and y are respectively atomic ratios meeting 0.45x0.75, and 0<y0.35, and non-metal components represented by N_1---BCO, wherein , and are respectively atomic ratios meeting 0 0.15, 00.35, and 0.25, with the binding energy of Al, Cr and/or Si to oxygen in a range of 525-535 eV in an X-ray photoelectron spectroscopy.

[0009] In the second hard film, x is preferably 0.5-0.7. The upper limit of y is preferably 0.2, and the lower limit of y is preferably 0.005, more preferably 0.01. is preferably 0-0.12, more preferably 0-0.08. is preferably 0-0.2, more preferably 0-0.1. is preferably 0.01-0.25, more preferably 0.01-0.2.

[0010] In the second hard film, Si preferably exists in the form of a nitride, an oxide and a metal, and when the relative intensities of the Si metal and its nitride and oxide determined by X-ray photoelectron spectroscopy are represented by I(Si), I(SiN) and I(SiO), respectively, with I(Si)I(SiN)I(SiO)100%, I(SiN) is preferably 52% or more. This hard film preferably has a crystal structure having the maximum X-ray diffraction intensity in a (200) face or a (111) face.

[0011] The third hard film of the present invention is formed by an arc-discharge ion-plating method, and has a composition comprising metal components represented by Al_xCr_1-x-ySi_y, wherein x and y are respectively atomic ratios meeting 0.45x0.75, 0 y0.35, and 0.5xy<1, and non-metal components represented by N_1---BCO, wherein , and are respectively atomic ratios meeting 00.15, 00.35, and 0.003 0.25, and an NaCl-type crystal structure, with a half width of 2at an X-ray diffraction peak corresponding to a (111) face or a (200) face being 0.5-2.0, the above hard film containing oxygen more in grain boundaries than in crystal grains.

[0012] In the third hard film, x is preferably 0.5-0.7. y is preferably 0-0.2, more preferably 0-0.1. is preferably 0-0.12, more preferably 0-0.08. is preferably 0-0.2, more preferably 0-0.1. is preferably 0.01-0.25, more preferably 0.01-0.2.

[0013] The third hard film preferably has the binding energy of Al, Cr and/or Si to oxygen in a range of 525-535 eV in an X-ray photoelectron spectroscopy. The third hard film preferably has the maximum oxygen concentration in a region of depth within 500 nm from the outermost surface. It preferably meets 0.3<I(200)/I(111)<12, wherein I(111) and I(200) are the X-ray diffraction intensities of a (111) face and a (200) face, respectively.

[0014] In the first to third hard films, a ratio of the total amount of non-metal elements (NBCO) to the total amount of metal elements (AlCr or AlCrSi) is stoichiometrically more than 1, preferably 1.1 or more. The upper limit of this ratio is preferably 1.7. If this ratio exceeded 1.7, then the hard film would have low peeling resistance.

[0015] From the aspect of balance between wear resistance and adhesion, the elastic recovery ratio E of the hard film of the present invention is preferably 28-42%, more preferably 30-40%. Particularly, the elastic recovery ratios E of the first and second hard films are preferably 30-40%, and the elastic recovery ratio E of the third hard film is preferably 28%-40%. The elastic recovery ratio E may be determined by the equation of 100-(contact depth)/(the maximum displacement at the maximum load). The contact depth and the maximum displacement at the maximum load can be determined by a nano-indentation method (W. C. Oliverand, G. M. Pharr: J. Mater. Res., Vol. 7, NO. 6, June 1992, pp. 1564-1583).

[0016] FIG. 1 is a graph showing the binding energy of CrO and AlO in Example 1;

[0017] FIG. 2 is a graph showing the binding energy of CrN and CrO in Example 1;

[0018] FIG. 3 is a graph showing the binding energy of AlN and AlO in Example 1;

[0019] FIG. 4 is a graph showing the X-ray diffraction in Example 1;

[0020] FIG. 5 is a graph showing the relation between the amount of Al and hardness in the AlCrNO film and the AlCrN film;

[0021] FIG. 6 is a graph showing the relation between displacement and load in Example 5 and Comparative Example 5;

[0022] FIG. 7 is a graph showing a wide spectrum profile of the X-ray photoelectron spectroscopy in Example 10;

[0023] FIG. 8 is a graph showing the X-ray diffraction in Example 10;

[0024] FIG. 9 is a graph showing a narrow spectrum profile of the X-ray photoelectron spectroscopy in Example 12;

[0025] FIG. 10 is a graph showing a narrow spectrum profile of the X-ray photoelectron spectroscopy in Example 16;

[0026] FIG. 11 is a graph showing the relation between displacement and load in Example 17 and Comparative Example 5;

[0027] FIG. 12 is a graph showing the relation between the amount of Al and hardness in the AlCrSiNO film and the AlCrN film;

[0028] FIG. 13 is an electron field emission transmission electron micrograph showing the cross section of the hard film of Example 25;

[0029] FIG. 14 is a graph showing the analysis results by electron-beam energy-loss spectroscopy in a region of the crystal grain 2 in FIG. 13;

[0030] FIG. 15 is a graph showing the analysis results by electron-beam energy-loss spectroscopy in a portion shown by the arrow in the boundaries in FIG. 13;

[0031] FIG. 16 is a graph showing the X-ray photoelectron spectrum of the hard film of Example 25;

[0032] FIG. 17 is a graph showing the element analysis results of the hard film of Example 25 by X-ray photoelectron spectroscopy in a film thickness direction; and

[0033] FIG. 18 is a graph showing the O_ls spectra of X-ray photoelectron spectroscopy measured every 24 minutes in Example 25.

[0034] 1 Hard Film

[0035] (A) Composition

[0036] (1) First Hard Film

[0037] The first hard film has a composition comprising metal components represented by Al_xCr_1-x, wherein x is an atomic ratio meeting 0.45x0.75, and non-metal components represented by N_1---BCO, wherein , and respectively atomic ratios meeting 0<co. 15, 0 S<0.35, and 0.00.25.

[0038] When the amount x of Al is less than 0.45, there are no sufficient effects of improving the hardness and high-temperature oxidation resistance of the hard film. On the other hand, when x exceeds 0.75, the hard film has an excess residual compression stress, resulting in self-destruction immediately after coating and thus drastic decrease in strength. The preferred range of x is 0.5-0.7.

[0039] The addition of boron is preferable because it provides the hard film with improved resistance to deposit to a mating member, and a decreased friction coefficient at high temperatures. However, when the amount a of boron exceeds 0.15, the film becomes brittle. The upper limit of is preferably 0.12, more preferably 0.08.

[0040] The addition of carbon is effective to increase the hardness of the hard film and reduce the friction coefficient thereof at room temperature. When the amount of carbon exceeds 0.35, the film becomes brittle. The upper limit of is preferably 0.2, more preferably 0.1.

[0041] Oxygen has effects of improving the hardness, high-temperature oxidation resistance and wear resistance of the hard film, as well as the adhesion of the hard film to a substrate. To achieve such effects, the amount of oxygen should be 0.01-0.25. When is less than 0.01, the addition of oxygen does not provide sufficient effects. On the other hand, when exceeds 0.25, the film has extremely decreased hardness, resulting in poor wear resistance. is preferably 0.01-0.2, particularly 0.02-0.2.

[0042] A ratio of the total amount of non-metal elements (NBCO) to the total amount of metal elements (AlCr) is stoichiometrically more than 1, preferably 1.1 or more. The upper limit of this ratio is preferably 1.7.

[0043] (2) Second Hard Film

[0044] The second hard film has a composition comprising metal components represented by Al_xCr_1-X-YSi_y and non-metal components represented by N_1---BCO. The composition of the second hard film is the same as that of the first hard film except that the former contains Si. Accordingly, explanation will thus be made only on Si. The other elements may be the same as in the first hard film. With respect to the structure and characteristics, too, the second hard film may be the same as the first hard film unless otherwise mentioned.

[0045] The addition of Si makes the hard film harder, drastically improving its wear resistance. The amount y of Si is generally 0.35 or less, preferably 0.2 or less. When y is more than 0.35, the hard film has an excess residual compression stress, which may cause self-destruction and form hexagonal crystals immediately after coating, resulting in drastic decrease in strength. The lower limit of y is preferably 0.005, more preferably 0.01.

[0046] A ratio of the total amount of non-metal elements (NBCO) to the total amount of metal elements (AlCrSi) is stoichiometrically more than 1, preferably 1.1 or more. The upper limit of this ratio is preferably 1.7.

[0047] (3) Third Hard Film

[0048] The third hard film has a composition comprising metal components represented by Al_xCr_1-x-ySi_y, wherein x and y are respectively atomic ratios meeting 0.45x0.75, 0y0.35, and 0.5xy<1, and non-metal components represented by N_1---BCO, wherein , and are respectively atomic ratios meeting 00.15, 00.35, and 0.003 0.25. The composition of the third hard film is the same as that of the first hard film except for the inclusion of Si and the content of 0. Accordingly, the amounts of Si and O will be explained here. With respect to the amounts of the other elements, the third hard film may be the same as the first hard film, and with respect to the structure and characteristics, they may be the same unless otherwise mentioned.

[0049] The addition of Si provides the hard film with higher hardness, drastically improving its wear resistance. The amount y of Si is generally 0-0.35, preferably 0-0.2, more preferably 0-0.1. When y exceeds 0.35, a residual compression stress in the hard film becomes excessive, which may cause self-destruction and form hexagonal crystals immediately after coating, resulting in drastic decrease in strength. Because the lower limit of y is 0, the third hard film may contain no Si.

[0050] The amount of oxygen is 0.003-0.25. When is less than 0.003, there is no effect by the addition of oxygen. On the other hand, when is more than 0.25, the film has extremely low hardness, and thus poor wear resistance. The preferred lower limit of is 0.01, while its preferred upper limit is 0.2.

[0051] A ratio of the total amount of non-metal elements (NBCO) to the total amount of metal elements (AlCrSi) is stoichiometrically more than 1, preferably 1.1 or more. The upper limit of this ratio is preferably 1.7.

[0052] (B) Crystal Structure and Characteristics

[0053] (1) Crystal Structure

[0054] Any of the hard films of the present invention has the maximum X-ray diffraction intensity in a (200) face or a (111) face. The half width of 2 in the X-ray diffraction peak corresponding to the (111) face or the (200) face is preferably 0.5-2.0. A ratio I(200)/I(111) of the X-ray diffraction intensities of the (111) face and the (200) face is preferably 0.3-12. When I(200)/I(111) is less than 0.3, the hard film has such low crystallinity that irregular wear conspicuous in the conventional amorphous hard films is likely to occur. On the other hand, when I(200)/I(111) exceeds 12, the film hardness decreases, resulting in the deterioration of wear resistance. It is thus clear that any of the hard films of the present invention has an NaCl-type crystal structure. Because of such crystal structure, the hard films have excellent toughness and adhesion to a substrate.

[0055] In the case of the hard film containing Si, I(SiN) is preferably 52% or more, when the relative intensities of the Si metal and its nitride and oxide determined by X-ray photoelectron spectroscopy are represented by I(Si), I(SiN) and I(SiO), respectively, with I(Si)I(SiN)I(SiO)100%. The hard film meeting this condition has high hardness and thus excellent wear resistance.

[0056] (2) Bonding to Oxygen

[0057] When a residual compression stress increases in the hard film, the film hardness generally becomes higher, and its adhesion to a substrate tends to deteriorate. Because hardness and adhesion are thus in a trade-off relation, high hardness has conventionally been sought while sacrificing the adhesion to a substrate to some extent. According to the present invention, oxygen is added to a film of AlCr or AlCrSi, and controlled to exist more in grain boundaries than in crystal grains, to suppress the diffusion of oxygen into the hard film from outside, thereby drastically improving oxidation resistance. As a result, it is possible to provide a hard film having high hardness, extremely decreased residual compression stress, and extremely, improved adhesion to a substrate.

[0058] The hard film of the present invention containing a predetermined amount of oxygen has the binding energy of Al and/or Cr (or Al, Cr and/or Si) to oxygen in 525-535 eV in X-ray photoelectron spectroscopy. The existence of AlO and/or CrO (or AlO, CrO and/or SiO) makes obscure grain boundaries functioning as oxygen diffusion paths, thereby making it difficult for oxygen to diffuse in the hard film. Also, because Cr and Al (and Si) exist in the form of nitrides, oxides and oxinitrides, the hard film is dense, thereby suppressing the oxidation of the hard film and having high hardness.

[0059] When there is the maximum oxygen concentration in the hard film in a region of depth within 500 nm from the outermost surface in a film thickness direction, the hard film has suppressed oxygen diffusion, extremely improved high-temperature oxidation resistance, and lowered friction. On the other hand, when there is the maximum oxygen concentration in a region of depth exceeding 500 nm, the hard film has low wear resistance.

[0060] (3) Elastic Recovery Ratio

[0061] In any of the hard films of the present invention, its elastic recovery ratio E determined by a nano-indentation method is preferably 28-42%. The elastic recovery ratio E in this range can be achieved by controlling film-forming conditions such as bias voltage, the partial pressure of each reaction gas, a substrate temperature, etc. When E exceeds 42%, a residual compression stress becomes too high in the hard film, resulting in poor toughness and lowered adhesion to a substrate. On the other hand, when E is less than 28%, the hard film is insufficient in strength and wear resistance, suffering from irregular wear, etc. The elastic recovery ratio E is preferably 30-40%, particularly 32-38%.

[0062] (C) Combination With Another Hard Film

[0063] With another hard film formed on the hard film of the present invention, the wear resistance can be further improved. Usable as another hard film is (a) a hard film comprising at least one metal element selected from the group consisting of Ti, Cr, Al and Si, and N, or N and at least one non-metal element selected from the group consisting of C, O and B, (b) a hard carbon film, or (c) a hard boron nitride film. These hard films may be laminated in arbitrary combination. Al, Ti and/or Cr in another hard film form oxides (TiO₂, Al₂O₃, Cr₂O₃), making layer separation difficult. Accordingly, the hard film exhibits excellent wear resistance even in a kinetic wear environment at high temperatures.

[0064] 2 Production of Hard Film

[0065] To form the hard film of the present invention containing oxygen, namely having AlO and/or CrO (or AlO, CrO and/or SiO), it is preferable to conduct an arc-discharge ion-plating method, using (a) an oxygen-containing metal target as an evaporation source, and/or (b) an oxygen-containing reaction gas. When the oxygen-containing metal target is used, the oxygen content in the metal target is preferably 2000 ppm or more, more preferably 2500 ppm or more. The upper limit of the oxygen content in the metal target is preferably 9800 ppm. When the upper limit of the oxygen content exceeds 9800 ppm, arc discharge becomes unstable, resulting in the tendency of increasing large particles and thus making the hard film surface rougher. For instance, the oxygen content in the metal target is 1800 ppm or less, there is substantially no difference in an oxygen concentration between crystal grains and boundaries. The oxygen concentration is determined from the intensity of an oxygen peak measured by electron-beam energy-loss spectroscopy, to determine a ratio P of the oxygen concentration in grain boundaries to that in crystal grains. P should be more than 1 and is preferably 4 or less.

[0066] An arc-discharge ion-plating apparatus comprises a vacuum chamber, an arc-discharge evaporation source insulated from the vacuum chamber, and a substrate holder. With electric current supplied to the arc-discharge evaporation source, arc discharge is caused on the target to ionize metal components. The substrate is heated to 500 C., for instance, by a heater disposed in the vacuum chamber. A film-forming atmosphere in the vacuum chamber contains active gases such as N₂, O₂, C₂H₂, etc. While applying a negative bias voltage to the substrate holder, a hard film comprising target metals and N or N and O and/or C is caused to grow on the substrate.

[0067] When a bias voltage is applied to the substrate, the resultant hard film can have higher adhesion to the substrate. To obtain a dense hard film having excellent adhesion, high-temperature oxidation resistance and wear resistance, the film-forming conditions are preferably a gas pressure of 1.5-15 Pa, particularly 2-5 Pa, a substrate temperature of 450 C. to 700 C., and as low bias voltage as 15 V to 300 V.

[0068] 3 Hard Film-Coated Members

[0069] The hard film of the present invention having excellent adhesion is preferably formed on substrates such as various tools such as drills, taps, reamers, end mills, gear-cutting tools, broaches and exchangeable inserts, molding dies, etc. Preferred materials for the substrate include high-speed steel, die steel, heat-resistant steel, bearing steel, austenitic stainless steel, cemented carbide, cermets, etc. The hard film of the present invention epitaxially grows on a substrate comprising, for instance, Fe, Ni and/or Co. Accordingly, it is possible to provide hard film-coated members having, excellent high-temperature oxidation resistance and wear resistance without suffering from peeling from a substrate, etc.

[0070] When the hard film of the present invention is formed on a tool, for instance, a roughing end mill, particularly made of cemented carbide or high-speed steel, it is possible to provide a hard film-coated tool having excellent adhesion, peeling resistance, hardness and wear resistance. Smoothing of a surface of the hard film-coated tool by mechanical working such as grinding, etc. effectively improves the withdrawal of chips and the suppression of the chipping of cutting edges during a cutting operation, resulting in further improvement in a cutting life.

[0071] The present invention will be specifically described below with reference to Examples without intention of restricting the scope of the present invention. The composition of the hard film in each Example and Comparative Example was analyzed by an electron probe microanalyzer with current for measuring the metal components set at 0.5 A, and current for measuring the non-metal components set at 0.1 A. Accordingly, a ratio of the metal components to the non-metal components was not determined. Though the metal components and the non-metal components are conveniently shown by one formula as the composition of the hard film in each Example and Comparative Example, it does not mean that a ratio of the metal components to the non-metal components is 1:1.

[0072] A substrate made of cemented carbide containing 13.5% by mass of Co, and an AlCrB alloy target containing 3100 ppm of oxygen were placed in a vacuum chamber, and a reaction gas comprising N₂ and C₂H₂ were introduced into the vacuum chamber with the total pressure in the chamber set at 3.0 Pa. With a bias voltage of 100 V and a substrate temperature of 450 C., a hard film of (Al_0.6Cr_0.4)(N_0.80CO_0.08O_0.10B_0.02) having a thickness of about 5 m was formed on the substrate. The composition of the hard film was measured by an electron probe X-ray microanalysis and an Auger electron spectroscopy.

[0073] Using an X-ray photoelectron spectroscope of a 1600S type available from PHI, the X-ray photoelectron spectroscopic analysis of the hard film was carried out. The results are shown in FIGS. 1-3. FIG. 1 shows that there was a metal-oxygen binding energy at around 530 eV, FIG. 2 shows the existence of bonds of CrN and CrO, and FIG. 3 shows the existence of bonds of AlN and AlO. The X-ray diffraction pattern shown in FIG. 4 indicates that the hard film is most oriented in a (200) face.

[0074] Hard films having compositions represented by (Al_xCr_1-x)(N_0.95O_0.05) were formed in the same manner as in Example 1. x was 0.2 in Comparative Example 1, 0.3 in Comparative Example 2, 0.5 in Example 2, 0.6 in Example 3, 0.7 in Example 4, and 0.8 in Comparative Example 3. Hard films having compositions represented by (Al_xCr_1-x)N were also formed in the same manner. x was 0.2 in Comparative Example 4, 0.5 in Comparative Example 5, and 0.7 in Comparative Example 6.

[0075] Using a micro-indentation hardness tester equipped with a triangular-pyramidal diamond indenter having a width tip angle of 1150, the indentation hardness of each hard film was measured under the conditions of the maximum load of 49 mN and a loading step of 4.9 mN/sec, with the maximum load kept for 1 second. The results are shown in FIG. 5. The indentation hardness shown in FIG. 5 is an average value of 10 measured values. FIG. 5 reveals that the hard films of Examples 2-4 having an Al content in a range of 45-75 atomic % had as high hardness as more than 40 GPa. The preferred hardness of the hard film of the present invention is 45-52 GPa. The hard films of Examples 2-4 were excellent in adhesion to a substrate and wear resistance.

[0076] Hard films having compositions shown in Table 1 were formed on substrates of cemented carbide, high-speed steel and die steel in the same manner as in Example 1. Table 1 also shows the oxide layer thickness, indentation hardness, residual compression stress and elastic recovery ratio of each hard film. The thickness of the oxide layer was measured after keeping each hard film at 1100 C. for 1 hour and 9 hours, respectively, in the air. The indentation hardness was measured in the same manner as in Example 2. The residual compression stress was calculated from the deformation of a thin plate. The elastic recovery ratio was determined by a nano-indentation method.

	TABLE 1
	Thickness (m)
	of
	Oxide Layer
		after Kept at	Indentation
	Film Composition	1100 C. for	Hardness
No.	(atomic ratio)	1 hr.	9 hrs.	(GPa)
Example 5	(Al0.6Cr0.4)(N0.95O0.05)	0.1	0.6	48.8
Example 6	(Al0.6Cr0.4)(N0.92O0.08)	0.1	0.4	49.4
Example 7	(Al0.5Cr0.4)(N0.90O0.05C0.05)	0.2	1.1	48.3
Example 8	(Al0.6Cr0.4)(N0.93O0.05B0.02)	0.1	0.3	49.8
Example 9	(Al0.6Cr0.4)(N0.87O0.10B0.03)	0.2	1.4	50.3
Comparative	(Al0.2Cr0.8)(N0.95O0.05)	2.4	3.4	34.6
Example 7
Comparative	(Al0.8Cr0.2)(N0.95O0.05)	0.1	0.7	39.2
Example 8
Comparative	(Al0.6Cr0.4)(N0.45O0.55)	1.8	3.9	38.8
Example 9
Comparative	(Al0.5Cr0.5)N	2.9	>5.0	36.9
Example 5
	Peeling of Hard Film
	Residual	Elastic		High-
	Compression	Recovery	Cemented	Speed	Die
No.	Stress (GPa)	Ratio (%)	Carbide(1)	Steel(2)	Steel(3)
Example 5	2.2	34.5	no	no	no
Example 6	2.2	34.1	no	no	no
Example 7	2.3	34.8	no	no	no
Example 8	1.9	35.2	no	no	no
Example 9	2.3	35.7	no	no	no
Comparative	2.9	27.6	no	no	no
Example 7
Comparative	3.7	30.0	yes	yes	yes
Example 8
Comparative	2.7	30.9	no	yes	yes
Example 9
Comparative	2.6	31.8	yes	yes	yes
Example 5
Note:
(1)Containing 13.5% by mass of Co.
(2)Formed from high-speed steel powder containing 8% by mass of Co.
(3)SKD61.

[0077] It was confirmed from the data of the thickness of the oxide layer that the hard films of Examples 5-9 were substantially not oxidized, excellent in a high-temperature oxidation resistance. On the contrary, the hard film of Comparative Example 5 was extremely oxidized, and the diffusion of oxygen reached the substrate. The hard films of Examples 5-9 were higher in indentation hardness and lower in residual stress than those of Comparative Examples 5, 7-9.

[0078] It is clear from a load-displacement curve shown in FIG. 6 that the hard film of Example 5 was large in the maximum displacement and small in plastic deformation at the maximum load, meaning that there is large elastic recovery when the same stress is applied to the hard film. An elastic recovery ratio E was determined from this load-displacement curve. It is clear from Table 1 that the hard films of Examples 5-9 are excellent in elastic recovery characteristics. The hard films of Examples 5-9 having excellent elastic recovery characteristics had decreased peeling and cracking and thus excellent adhesion to the substrate.

[0079] Using a Rockwell hardness meter, each hard film was given a dent at a load of 150 N, to observe the peeling of the film by an optical microscope. The results are shown in Table 1. The hard films of Examples 5-9 were free from peeling, proving excellent adhesion. This is due to the fact that the hard films of Examples had proper elastic recovery ratios E. On the other hand, each hard film of Comparative Examples 5 and 7-9 having a low elastic recovery ratio E failed to follow the deformation of the substrate, resulting in peeling in a portion near the dent.

[0080] Using an AlCrSi alloy target having an oxygen content of 3300 ppm produced by a powder metallurgy method to have a targeted composition, and introducing an active gas comprising a nitrogen gas, an oxygen gas and, if necessary, an acetylene gas into a vacuum chamber with the total gas pressure set at 3.0 Pa, a hard film of Example 10 of (Al_0.60Cr_0.36Si_0.04)(N_0.8C_0.1O_0.1) having a thickness of about 5 m was formed on a mirror-polished substrate formed by fine cemented carbide particles containing 13.5% by mass of Co, at a bias voltage of 100 V and at a film-forming temperature of 450 C. by an arc-discharge ion-plating method. Also, using the same target as in Example 10 except that its oxygen content was 1800 ppm, a hard film of Comparative Example 10 was formed under the same film-forming conditions as in Example 10.

[0081] After the surface of each hard film was etched by an Ar ion gun for 5 minutes to remove contaminations from each hard film surface, X-ray photoelectron spectroscopic analysis was conducted to obtain a wide spectrum for each hard film. And after etching for 30 seconds, X-ray photoelectron spectroscopic analysis was conducted to obtain a narrow spectrum for each hard film. X-ray photoelectron spectroscopic analysis was carried out in a circular region having a diameter of 0.4 mm in each hard film at 400 W by an X-ray photoelectron spectroscope of a 1600S type available from PHI using MgK as an X-ray source. An etching rate by the Ar ion gun was 1.9 nm/minute as converted to SiO₂. The composition of the resultant hard film was determined by an electron probe X-ray microanalysis and an Auger electron spectroscopy.

[0082] The wide spectrum of the hard film of Example 10 is shown in FIG. 7. FIG. 7 indicates the existence of Si and O and the binding energy of SiO in the hard film of Example 10. It is also clear from an X-ray diffraction pattern shown in FIG. 8 that the hard film of Example 10 has crystal structure oriented most in a (200) face. On the other hand, there was no peak indicating the bonding of oxygen at around 530 eV in the hard film of Comparative Example 10.

[0083] Using targets (oxygen content: 3300 ppm) having metal compositions for the targeted film composition, and mirror-polished substrates formed from fine cemented carbide particles containing 13.5% by mass of Co, hard films having compositions shown in Table 2 were formed by an arc-discharge ion-plating method under the film-forming conditions shown in Table 2. The intensity of SiN, SiO and Si in each hard film was determined by X-ray photoelectron spectroscopy. The results are shown in Table 2.

	TABLE 2
	Film-Forming Conditions
		Bias	Gas	Substrate
	Film Composition	Voltage	Pressure	Temperature
No.	(atomic ratio)	(V)	(Pa)	( C.)
Example 11	(Al0.6Cr0.35Si0.05)	100	2.0	500
	(N0.85O0.09C0.06)
Example 12	(Al0.6Cr0.35Si0.05)	100	5.0	500
	(N0.85O0.09C0.06)
Example 13	(Al0.6Cr0.36Si0.04)	200	5.0	500
	(N0.85O0.09C0.06)
Example 14	(Al0.6Cr0.36Si0.04)	300	5.0	500
	(N0.85O0.09C0.06)
Example 15	(Al0.6Cr0.35Si0.05)	200	5.0	350
	(N0.85O0.09C0.06)
Example 16	(Al0.5Cr0.35Si0.15)	100	5.0	500
	(N0.85O0.11C0.04)
Comparative	(Al0.6Cr0.36Si0.04)	200	5.0	800
Example 11	(N0.85O0.09C0.06)
Comparative	(Al0.6Cr0.35Si0.05)	100	0.5	500
Example 12	(N0.85O0.09C0.06)
	Intensity (%)
	No.	I(SiN)	I(SiO)	I(Si)
	Example 11	52.3	12.7	35.0
	Example 12	58.3	9.1	32.6
	Example 13	61.2	13.5	25.3
	Example 14	68.5	10.6	20.9
	Example 15	63.5	11.1	25.4
	Example 16	70.9	10.3	18.8
	Comparative	44.2	17.6	38.2
	Example 11
	Comparative	48.3	15.2	36.5
	Example 12

[0084] Each relative intensity was calculated by peak separation in the Si_2pspectrum of each hard film shown in Table 2, and the peak separation was carried out by a peak-fitting method, with the peak position of SiN set at 101.20.2 eV, the peak position of SiO set at 103.30.2 eV, and the peak position of Si (metal) set at 99.30.2 eV. FIG. 9 shows a narrow spectrum of S_2p in Example 12, and FIG. 10 shows a narrow spectrum of Si_2p in Example 16.

[0085] It is clear from Table 2 that the preferred film-forming conditions for making I(SiN)/I(SiN)I(SiO)I(Si) of 52% or more are a gas pressure of about 2.0-5.0 Pa, a bias voltage of 100 V to 300 V, and a film-forming temperature of 350 C. to 500 C. I(SiN) changes not only by the film-forming conditions but also by the film composition.

[0086] Hard films having compositions shown in Table 3 were formed on a mirror-polished substrate of SNMN432 formed by cemented carbide containing 13.5% by mass of Co under the same film-forming conditions as in Example 10. Each hard film was kept at 1100 C. for 1 hour and 9 hours, respectively, in the air, to measure the thickness of an oxide layer on each hard film. The results are shown in Table 3 together with those of Comparative Example 5. It is clear from Table 3 that the hard films of Examples 17-21 were not drastically oxidized, proving that they were excellent in a high-temperature oxidation resistance. On the other hand, the hard film of Comparative Example 13 containing 20 atomic % of Al was much more oxidized than those of Examples 17-21, proving that the former was poorer in a high-temperature oxidation resistance.

[0087] The cross section of each of the same hard films was mirror-polished by 0.1-m grinding diamond particles with inclination of 5. The indentation hardness of the hard film was measured at a depth of 3.5 m from the film surface under the following conditions. Namely, using a micro-indentation hardness tester equipped with a Berkovich-type triangular-pyramidal diamond indenter having a width tip angle of 1150, the indentation hardness of each hard film was measured under the conditions of the maximum load of 49 mN and a loading step of 4.9 mN/sec, with the maximum load kept for 1 second. Because a ratio (T/L) of the thickness T of the hard film to the maximum indentation depth L relative to a load is 10 or more, the hardness of the hard film per se can be measured without influence of the substrate. Table 3 shows an average value of 10 measured values. Table 3 also shows the residual compression stress of the hard film calculated from the deformation of a thin plate.

[0088] It is clear from Table 3 that the hard films of Examples 17-21 were lower in residual stress and higher in hardness than the Al_0.5Cr_0.5N film of Comparative Example 5. On the other hand, the hard film of Comparative Example 13 containing 20 atomic % of Al was lower in hardness and poorer in a high-temperature oxidation resistance than those of Examples 17-21. Though the hard film of Comparative Example 14 containing 30 atomic % of Si had an improved high-temperature oxidation resistance, it was lower in hardness and poorer in wear resistance than those of Examples 17-21. The hard film of Comparative Example 15 containing 85 atomic % of Al had low hardness and insufficient wear resistance.

[0089] Hard films having compositions shown in Table 3 were formed on ground substrates of SNMN432 formed by cemented carbide containing 13.5% by mass of Co, high-speed steel containing 8% by mass of Co, and SKD die steel, respectively, under the same film-forming conditions as in Example 10. An indenter of a Rockwell hardness meter was pressed onto each hard film under a load of 1470 N, to observe by an optical microscope whether or not there was peeling near the dent. Table 3 shows the presence and absence of peeling. It is clear from Table 3 that the hard films of Examples 17-21 do not peel from any substrates, exhibiting excellent adhesion. On the other hand, the hard film of Comparative Example 5 could not follow the deformation of the substrate, resulting in peeling in a portion near the dent.

[0090] Coated cutting tools, etc. are microscopically plastically deformed in cutting edges and their vicinities in a cutting stress direction during a cutting operation. When the cutting edges are plastically deformed, peeling and cracking occur in the hard film, likely to cause irregular wear and damage to the cutting edges. Thus, the plastic deformation resistance of the hard film is important in a kinetic environment accompanied with plastic deformation. Therefore, with respect to the hard films of Examples 17-21 and Comparative Examples 13-15 produced under the same film-forming conditions as in Example 10, load-displacement curves were obtained by the same nano-indentation method as above. The elastic recovery ratio E of each hard film was determined from each load-displacement curve. The results are shown in Table 3 together with those of Comparative Example 5. It is clear from Table 3 that the hard films of Examples 17-21 had better elastic recovery characteristics than the hard films of Comparative Examples 5 and 13-15. With a high elastic recovery ratio, the peeling and cracking of the hard film are suppressed in a kinetic environment causing wear, etc., proving that the hard film has good adhesion to the substrate. Examples 17-21 reveal that the elastic recovery ratio E is more preferably 30-40%, particularly 32-40%.

[0091] FIG. 11 shows the load-displacement curves of Example 17 and Comparative Example 5. It is clear from FIG. 11 that the hard film of Example 17 is large in the maximum displacement at the maximum load, small in a plastic deformation representing a permanent strain, and large in an elastic recovery ratio when the same stress was applied.

[0092] To examine high-temperature stability, hard films having compositions shown in Table 3 were formed on the above cemented carbide substrate in the same manner as in Example 10. Each hard film was kept at room temperature, 1101 C. and 1200 C., respectively, for 4 hours in vacuum, to measure its micro-indentation hardness in the same manner as above. The results are shown in Table 3. The hard films of Examples 17-21 did not suffer from remarkable decrease in hardness in a high-temperature environment. On the other hand, the hard film of Comparative Example 5 after kept at 1100 C. for 4 hours had indentation hardness of 35.5 GPa, indicating that its hardness decreased to substantially the same level as that of a TiN film. C and Co were diffused from the substrate into the hard film after keeping at 1200 C. for 4 hours in Comparative Example 5.

	TABLE 3
		Thickness
		(m) of
		Oxide Layer
		after Kept at	Indentation	Residual
	Film Composition	1100 C. for	Hardness	Compression
No.	(atomic ratio)	1 hr.	9 hrs.	(GPa)	Stress (GPa)
Example 17	(Al0.6Cr0.35Si0.05)(N0.95O0.05)	0.1	0.6	50.7	2.3
Example 18	(Al0.5Cr0.35Si0.15)(N0.92O0.08)	0.1	0.4	52.2	2.4
Example 19	(Al0.55Cr0.44Si0.01)(N0.95O0.05)	0.1	0.8	49.2	2.4
Example 20	(Al0.6Cr0.35Si0.05)(N0.93O0.05B0.02)	0.1	0.3	50.0	2.6
Example 21	(Al0.6Cr0.35Si0.05)(N0.80O0.05C0.15)	0.1	1.4	51.6	2.4
Comparative	(Al0.20Cr0.75Si0.05)(N0.95O0.05)	0.5	3.9	37.2	2.9
Example 13
Comparative	(Al0.20Cr0.50Si0.30)(N0.95O0.05)	0.1	1.2	43.2	3.8
Example 14
Comparative	(Al0.85Cr0.10Si0.05)(N0.95O0.05)	0.2	0.7	37.1	2.6
Example 15
Comparative	(Al0.5Cr0.5)N	2.9	>5.0	36.9	2.6
Example 5
	Peeling	Elastic	Indentation
	Cemented	High-Speed		Recovery	Hardness (GPa)(4)
No.	Carbide(1)	Steel(2)	Die Steel(3)	Ratio (%)	1100 C.	1200 C.
Example 17	no	no	no	34.2	50.2	47.2
Example 18	no	no	no	35.1	51.3	51.6
Example 19	no	no	no	34.6	48.3	47.0
Example 20	no	no	no	35.1	49.3	48.2
Example 21	no	no	no	35.3	50.7	50.1
Comparative	no	no	yes	28.6	36.1	34.5
Example 13
Comparative	yes	yes	yes	30.1	35.2	35.1
Example 14
Comparative	yes	yes	yes	30.4	36.2	35.1
Example 15
Comparative	yes	yes	yes	31.8	35.5	34.5
Example 5
Note:
(1)Containing 13.5% by mass of Co.
(2)Produced from high-speed steel powder containing 8% by mass of Co.
(3)SKD61.
(4)After heat-treated at 1100 C. and 1200 C., respectively, for 4 hours in vacuum.

[0093] Hard films having composition represented by (Al_xCr_0.95-xSi_0.05)(NO) and (Al_xCr_l-x)N, respectively, were formed under the same film-forming conditions as in Example 10. In the hard film of (Al_xCr_0.95-xSi_0.05)(NO), x was 0.2 in Comparative Example 16, 0.3 in Comparative Example 17, 0.5 in Example 22, 0.6 in Example 23, 0.7 in Example 24, and 0.8 in Comparative Example 18. In the hard film of (Al_xCr_1-x)N, x was 0.2 in Comparative Example 19, 0.5 in Comparative Example 20, and 0.7 in Comparative Example 21. The indentation hardness of each hard film was measured in the same manner as in Examples 17-21. The results are shown in FIG. 12.

[0094] The hard films of Examples 22-24 having an Al content in a range of 45-75 atomic % had as high hardness as more than 40 GPa because of the inclusion of Si and oxygen. The more preferred hardness is 45-55 GPa. With such high hardness, the hard films have excellent wear resistance and adhesion to the substrate.

[0095] A degreased and washed substrate was placed in a vacuum chamber of an arc-discharge ion-plating apparatus, kept at 500 C. for 30 minutes and then irradiated with Ar ions for cleaning.

[0096] With each of an Al_0.7Cr_0.3 alloy target (Examples 25, 26, 29-36, Comparative Examples 22-24) and an Al_0.68Cr_0.27Si_0.5 alloy target (Examples 27,28) both with an oxygen content of 3200 ppm placed in the vacuum chamber, an N₂ gas and reaction gases selected from a CH₄ gas, a C₂H₂ gas, an Ar gas, an O₂ gas, a CO gas and a B₃N₃H₆ gas depending on the object were introduced into the vacuum chamber, with the total pressure set at 7.5 Pa. With a pulse bias voltage (negative bias voltage: 120 V, positive bias voltage: 10 V, frequency: 20 kHz, and pulse width: negative pulse to positive pulse 80%: 20%), arc discharge was applied to each target to form a hard film having a thickness of about 3.5 m on a mirror-polished substrate of SNMN432 formed by ultrafine cemented carbide particles containing 7% by mass of Co at a film-forming temperature of 450 C. The film-forming conditions of Comparative Examples were the same as in Examples unless otherwise mentioned, except that a constant negative bias voltage was applied to the substrate.

[0097] Each of the resultant hard films was analyzed by an electron probe microanalyzer with respect to composition in a region of 50 m in diameter. The analysis results are shown in Table 4.

[0098] To confirm the presence of oxygen in the hard film, the cross section structure of the hard film was observed by a field emission transmission electron microscope (TEM) of a JEM-2010F type available from JEOL. Ltd. at an acceleration voltage of 200 kV. FIG. 13 is a TEM photograph showing the cross section structure of the hard film of Example 25. In the TEM photograph of FIG. 13, crystal grains 1, 2 and boundaries were clearly observed.

[0099] The oxygen contents in crystal grains and grain boundaries were analyzed by an electron-beam energy-loss spectroscope of Model 766 available from Gatan. In the electron-beam energy-loss spectroscopy, an analysis region was 1 nm in diameter. FIG. 14 shows the analysis results of the crystal grain 2 in FIG. 13 in a region of 1 nm in diameter by the electron-beam energy-loss spectroscopy. FIG. 15 shows the analysis results of the boundary (shown by the arrow) in FIG. 13 in a region of 1 nm in diameter by the electron-beam energy-loss spectroscopy.

[0100] It was confirmed from FIG. 15 that there was oxygen in the grain boundaries. FIGS. 14 and 15 indicate that oxygen exists more in grain boundaries than in crystal grains in the hard film. To control such that oxygen exists more in grain boundaries than in crystal grains, the proper film-forming conditions should be selected. In addition, the use of an oxygen-containing metal target is effective.

[0101] To detect the bonding state of oxygen in the hard film of Example 25, X-ray photoelectron spectroscopic analysis was carried out at 400 W in a circular region of 0.4 mm in diameter in the film, using an X-ray photoelectron spectroscope of 1600S type available from PHI, which comprised MgK as an X-ray source. Each test piece for analysis was sufficiently degreased and washed. With an Ar ion gun placed with inclination of 50 to a test piece surface, an X-ray generator was disposed at such a position that X-ray impinges the test piece surface at 900, and a photoelectron detector was disposed with inclination of 35 relative to the test piece surface. A 10-mm²-region of each test piece was etched with Ar ions for 120 minutes, and spectrum was measured every 24 minutes. A rate of etching with Ar ions was 1.5 nm/min on the basis of SiO₂.

[0102] FIG. 16 shows the spectrum after etching with Ar ions for 120 minutes. It is clear from FIG. 16 that the hard film of Example 25 contained oxygen. FIG. 17 shows the results of element analysis conducted by X-ray photoelectron spectroscopy in a film thickness direction. It was confirmed from FIG. 17 that there was about 6 atomic % of oxygen per the total amount (100 atomic %) of non-metal elements in the hard film of Example 25. FIG. 18 shows the spectra corresponding to O_ls measured every 24 minutes. In FIG. 18, the outermost surface of the test piece is shown on a rear end, and the deepest portion of the test piece is shown on a front end. It is clear from FIG. 18 that the hard film of Example 25 has the binding energy of metals (Al and Cr) and oxygen in a range of 525-535 eV. The bonding was mainly between carbon and oxygen on the test piece surface, while the bonding of metals and oxygen increased as going inside the film. Table 4 shows the binding energy and bonding state of oxygen to metals in a range of 525-535 eV in each hard film.

[0103] Further, the following characteristics of each hard film were evaluated.

[0104] (1) Crystallinity of hard film

[0105] To evaluate the crystallinity of each hard film, X-ray diffraction measurement was conducted with the incidence angle of X-ray to the test piece surface set at 5. It was found from the resultant X-ray diffraction profile that the face index of the hard film at the maximum intensity was a (111) face or a (200) face of an NaCl-type crystal structure. Expressing the X-ray diffraction intensity of the (111) face as I(111), and the X-ray diffraction intensity of the (200) face as I(200), the half width of 2 of the face index of each film at the maximum intensity and I(200)/I(111) are shown in Table 4.

[0106] (2) Indentation hardness and elastic recovery ratio

[0107] With each mirror-polished hard film inclined by 5, the indentation hardness of each hard film was measured at a depth of 2-3 m from the surface at 10 points by the same nano-indentation method as in Examples 17-21. The elastic recovery ratio E was calculated from a load-displacement curve obtained by the measurement of the indentation hardness. Table 4 shows an average value of the hardness of each film and the elastic recovery ratio E.

[0108] (3) Thickness of oxide layer

[0109] To evaluate the high-temperature oxidation resistance of each hard film, a test piece having each hard film was kept at 1100 C. for 9 hours in the air, and the thickness of the resultant oxide layer was measured. The results are shown in Table 4.

[0110] (4) Adhesion of hard film

[0111] To evaluate the adhesion of each hard film, the hardness of a test piece having each hard film was measured at 1470 N by a Rockwell hardness meter, and observation was conducted on whether or not there was peeling in a portion near the dent. The results are shown in Table 4.

[0112] (5) Wear resistance

[0113] Each hard film was formed on a four-edge roughing end mill made of high-speed steel having an outer diameter of 12 mm, to measure cutting length until the average wear width of a flank reached 0.25 mm, or when the tool was broken, thereby evaluating the wear resistance of the hard film. The results are shown in Table 4. The cutting conditions were as follows:

[0114] Cutting method: Rough working on side surface,

[0115] Work: SCM440 (HRC 31),

[0116] Depth of cutting: 6 mm in a radial direction and 12 mm in an axial direction,

[0117] Cutting speed: 70 ml/min,

[0118] Feed: 0.07 mm/edge, and

[0119] Cutting oil: None (dry type using air blow).

TABLE 4
		Face
		Index	Half Width
		at	of 2 in
		Maxi-	Face
	Film	mum	Index at	Oxygen
	Composition	Inten-	Maximum	Concen-
No.	(atomic ratio)	sity	Intensity()	tration
Example	(Al0.65Cr0.35)	(111)	0.7	Boundaries >
25	(N0.96O0.03C0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	0.9	Boundaries >
26	(N0.96O0.03C0.01)			Crystal Grains
Example	(Al0.65Cr0.31Si0.04)	(200)	0.8	Boundaries >
27	(N0.95O0.05)			Crystal Grains
Example	(Al0.65Cr0.31Si0.04)	(200)	1.2	Boundaries >
28	(N0.95O0.05)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	1.1	Boundaries >
29	(N0.97O0.03)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	1.2	Boundaries >
30	(N0.99O0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(200)	0.9	Boundaries >
31	(N0.92O0.03B0.05)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	0.7	Boundaries >
32	(N0.99O0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	0.8	Boundaries >
33	(N0.99O0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	0.8	Boundaries >
34	(N0.99O0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	0.7	Boundaries >
35	(N0.99O0.01)			Crystal Grains
Example	(Al0.65Cr0.35)	(111)	1.3	Boundaries >
36	(N0.99O0.01)			Crystal Grains
Comp-	(Al0.65Cr0.35)	(111)	0.9	Boundaries
arative	(N0.97O0.02C0.01)			Crystal Grains
Example
22
Comp-	(Al0.65Cr0.35)	(111)	0.3	Boundaries
arative	(N0.98O0.01C0.01)			Crystal Grains
Example
23
Comp-	(Al0.65Cr0.35)	(111)	2.1	Boundaries
arative	(N0.98O0.01C0.01)			Crystal Grains
Example
24
Comp-	(Al0.50Ti0.50)N	(200)	0.4	Boundaries
arative				Crystal Grains
Example
25
Comp-	(Al0.50Cr0.50)N	(111)	0.7	Boundaries
arative				Crystal Grains
Example
26
+TL,1	Oxygen	Peak of Oxygen
No.	Bonding(1)	Concentration(2)	I(200)/I(111)
Example 25	AlO, CrO	yes	0.8
Example 26	AlO, CrO	yes	0.8
Example 27	AlO, CrO, SiO	yes	1.8
Example 28	AlO, CrO, SiO	yes	2.2
Example 29	AlO, CrO	yes	0.8
Example 30	AlO, CrO	yes	0.9
Example 31	AlO, CrO	yes	1.4
Example 32		no	0.7
Example 33	AlO, CrO	yes	15
Example 34	AlO, CrO	yes	0.9
Example 35	AlO, CrO	yes	0.8
Example 36	AlO, CrO	yes	0.4
Comparative	AlO, CrO	yes	0.6
Example 22
Comparative	AlO, CrO	yes	0.4
Example 23
Comparative	AlO, CrO	yes	0.9
Example 24
Comparative		no	12
Example 25
Comparative		no	0.9
Example 26
Note:
(1)Oxygen bonding in a range of 525-535 eV.
(2)The peak of the oxygen concentration in a region 500 nm deep
from a surface.
			Thickness of
		Hardness	Oxide Layer		Cutting
No.	E(%)	(GPa)	(m)	Peeling	Length (m)
Example 25	31	48	0.6	no	63
Example 26	32	49	0.6	no	62
Example 27	33	52	0.3	no	74
Example 28	34	53	0.3	no	78
Example 29	31	49	0.5	no	61
Example 30	32	47	0.6	no	61
Example 31	33	51	0.2	no	72
Example 32	30	44	0.7	no	36
Example 33	30	43	0.9	no	43
Example 34	27	42	0.9	no	45
Example 35(1)	31	48	0.2	no	79
Example 36(2)	28	42	0.7	no	45
Comparative	29	36	1.5	yes	23
Example 22(3)
Comparative	28	35	1.2	yes	25
Example 23
Comparative	28	35	1.2	yes	14
Example 24
Comparative	27	38	5 or more	yes	20
Example 25
Comparative	27	36	5 or more	yes	21
Example 26
Note:
(1)The oxygen concentration was the maximum on the outermost surface.
(2)Hcp phase detected.
(3)At a reaction gas pressure of 0.3 Pa.

[0120] It was confirmed from Table 4 that the oxygen concentration was higher in grain boundaries than in crystal grains in any of Examples 25-36. Examples 25-36 provided higher hardness and better adhesion than Comparative Examples 22-26. The half width of 2 at a face index at the maximum intensity in X-ray diffraction was in a range of 0.5-2 in Examples 25-36, while it was 0.30 in Comparative Example 23 and 2.1 in Comparative Example 24. Accordingly, the hard films of Comparative Examples 23 and 24 had low hardness and thus poor adhesion. With respect to the high-temperature oxidation resistance, oxidation proceeded slowly in Examples 25-36.

[0121] As is clear from Table 4, the hard films of Examples 25-36 had longer cutting life and better wear resistance than those of Comparative Examples 22-26. Particularly, the hard films of AlCrSiNO of Examples 27 and 28 had a long cutting life and thus excellent wear resistance.

[0122] The hard film of AlCrNOB of Example 31 had excellent wear resistance because of the inclusion of B.

[0123] Rather than Example 32, in which the bonding of oxygen was not clearly observed in a range of 525-535 eV, other Examples, in which the bonding of oxygen was clearly observed, had higher hardness, longer cutting length and better wear resistance.

[0124] Rather than Example 33, in which a ratio of I(200)/I(111) was 15, other Examples meeting the conditions of 0.3<I(200)/I(11)<12 had higher hardness, longer cutting life and better wear resistance.

[0125] Rather than Example 34, in which the elastic recovery ratio E determined by a nano-indentation method was 27, other Examples meeting the conditions of 28E42, had higher hardness, higher adhesion, longer cutting length and better wear resistance.

[0126] Example 35 having the peak of the oxygen concentration at a depth within 500 nm from the surface had an excellent high-temperature oxidation resistance and the longest cutting life.

[0127] Rather than the hard film of Example 36 having a hexagonal crystal (considered to be AlN) in addition to an NaCl-type crystal structure in X-ray diffraction, the hard films of other Examples having only an NaCl structure had higher hardness, longer cutting life and better wear resistance.

[0128] In Comparative Example 22, in which a hard film was formed at a reaction gas pressure of 0.3 Pa, there was no difference in the oxygen concentration observed between crystal grains and grain boundaries, resulting in insufficient hardness and adhesion. Accordingly, the wear resistance was not improved, and the life was short.

[0129] In Comparative Examples 23 and 24, in which the halfwidth of 2 was 0.30 and 2.1, respectively, the hardness and the adhesion were not sufficiently improved, failing to improve the wear resistance and resulting in short life.

[0130] The same tools as in Examples 25-36 were coated with hard films shown in Table 5 and then with additional films shown in Table 5 in a thickness of about 1 m, to conduct a cutting test under the same conditions as in Examples 25-36. The film composition of each tool and the maximum life are shown in Table 5.

	TABLE 5
	Composition (atomic ratio)	Cutting
No.	Hard Film	Additional Film	Length (m)
Example 37	(Al0.65Cr0.35)(N0.97O0.03)	(Al0.75Si0.25)(N0.97O0.03)	72
Example 38	(Al0.65Cr0.35)(N0.97O0.03)	(Cr0.97Si0.03)(N0.97B0.03)	75
Example 39	(Al0.65Cr0.35)(N0.97O0.03)	(Ti0.78Si0.22)N	89
Example 40	(Al0.65Cr0.35)(N0.97O0.03)	Hard Carbon	82
Example 41	(Al0.65Cr0.35)(N0.97O0.03)	Boron Nitride	91
Example 42	(Al0.65Cr0.35)(N0.97O0.03)	Ti(N0.97B0.03)	93
Example 43	(Al0.65Cr0.35)(N0.92O0.03B0.05)	Ti(N0.88B0.12)	95
Example 44	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	(Al0.75Si0.25)(N0.97O0.03)	82
Example 45	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	(Cr0.97Si0.03)(N0.97B0.03)	86
Example 46	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	(Ti0.78Si0.22)N	98
Example 47	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	Hard Carbon	102
Example 48	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	Boron Nitride	111
Example 49	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	Ti(N0.97B0.03)	104
Example 50	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	Ti(N0.88B0.12)	107
Example 51(1)	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	(Cr0.97Si0.03)(N0.97B0.03)	92
Example 52(1)	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	(Ti0.78Si0.22)N	118
Example 53(1)	(Al0.65Cr0.31Si0.04)(N0.95O0.05)	Ti(N0.88B0.12)	121
Comparative	(Al0.65Cr0.35)(N0.97O0.03)	(Ti0.78Zr0.22)N	75
Example 27
Comparative	(Al0.65Cr0.35)(N0.97O0.03)	(V0.75Zr0.25)N	67
Example 28
Note:
(1)Surface smoothed.

[0131] Examples 37-42 each having an additional film shown in Table 5 immediately on the hard film of Example 29 were longer in cutting length and better in wear resistance than the hard film of Example 29. Example 43 having an additional film shown in Table 5 immediately on the hard film of Example 31 was longer in cutting life and better in wear resistance than Example 31. Examples 44-50 each having an additional film shown in Table 5 immediately on the hard film of Example 27 were longer in cutting length and better in wear resistance than Example 27. The tools of Examples 51-53 obtained by smoothing the film surfaces of Examples 45, 46 and 50 by mechanical working had as long life as 1.2 times at maximum. The films of TiZrN and VZrN in Comparative Examples 27 and 28 had poor adhesion to the hard film of the present invention, failing to further improve the wear resistance. It is thus clear that the formation of at least one of a hard film comprising at least one metal selected from the group consisting of Ti, Cr, Al and Si, and N and at least one non-metal element of C, O and/or B, a hard carbon film, and a boron nitride film immediately on the hard film of the present invention is preferable for increasing the tool life.

[0132] Though the present invention has been explained in detail referring to Examples above, the present invention is not restricted thereto, and various modifications may be made within the scope of the concept of the present invention. For instance, part of the metal components (less than 4 atomic %) may be replaced by one or more metals in 4a, 5a and 6a groups in the hard film.

[0133] As described above in detail, with oxygen or oxygen and Si added to the hard film of AlCrN, the hard film can be provided with improved hardness, adhesion, wear resistance and high-temperature oxidation resistance. When such hard films are formed on cutting tools and wear-resistant tools such as end mills, drills, etc., the cutting life can be extremely improved. With these improvements, the production cost of members requiring the above characteristics is drastically reduced.