REMOVAL OF H2S AND/OR MERCAPTANS FROM SUPERCRITICAL AND/OR LIQUID CO2

[0001] The invention relates to removing or scavenging hydrogen sulfide (H₂S) and/or mercaptans from carbon dioxide (CO₂), and most particularly relates, in one non-limiting embodiment, to removing or scavenging H₂S from liquid and/or super-critical CO₂.

[0002] Carbon dioxide is widely used in secondary and tertiary recovery of oil and natural gas in oil field applications. Prior to injection, CO₂ is processed and purified in processing plants and compressed to about 1800 to 2000 psig (about 12,000 to 14,000 kPa) for distribution and injection. To comply with some governmental regulations, the H₂S concentration of CO₂ to field injection points is required to be less than 100 ppm.

[0003] Some of the plants processing and purifying CO₂ are operating at their maximum capacity for handling CO₂ and effectively removing H₂S to maintain H₂S concentrations at less than 100 ppm. The primary limitation of some plants is their capacity to remove H₂S to an outlet concentration of less than 100 ppm. Operators of such facilities may experience a peak in gas production resulting in an increased requirement in capacity to handle the volume of CO₂ produced. The cost for making mechanical changes to these existing plants may require several million dollars and take a year or more. A chemical treatment would be a desirable alternative to making such a capital investment. Under these conditions, such plants cannot handle the increased production. Hence, the additional volume of CO₂ cannot be processed and H₂S cannot be removed from the CO₂ thus preventing the use of the additional CO₂ for further recovery of hydrocarbons.

[0004] It is known to use triazines to selectively remove H₂S from natural gas in the presence of CO₂. Tauseef Salma in Effect of Carbon Dioxide on Hydrogen Sulfide Scavenging, SPE 59765, 2000 SPE Permian Basin oil and Gas Recovery Conference, Midland, Tex. Mar. 21-23, 2000, studied the effect of CO₂ on the H₂S scavenging capacity of triazine-based scavengers for removing H₂S from natural gas. She concluded that CO₂ has very little effect on the H₂S scavenging performance of a triazine based H₂S scavenger.

[0005] U.S. Pat. No. 4,978,512 describes methods for selectively reducing the levels of hydrogen sulfide and organic sulfides from gaseous and/or liquid hydrocarbon streams, particularly natural gas streams, comprising contacting the streams with a composition comprising the reaction product of (i) a lower alkanolamine with (ii) a lower aldehyde. The reaction product of formaldehyde with monoethanolamine is 1,3,5-tri-(2-hydroxyethyl)-hexahydro-S-triazine.

[0006] Thus, it would be desirable if a method for removing or scavenging H₂S from carbon dioxide in liquid and/or supercritical form could be discovered which involved simply adding a chemical scavenger to the carbon dioxide.

[0007] An object of the invention is to provide a method for scavenging or removing H₂S from liquid and/or supercritical CO₂.

[0008] An additional object of the invention includes providing a method for scavenging or removing H₂S from liquid and/or supercritical CO₂ that may be accomplished by adding an effective amount of a chemical scavenging agent to the carbon dioxide.

[0009] Another object of the invention is to provide a scavenging agent for removing H₂S from liquid and/or supercritical carbon dioxide where the scavenging agent is easily made.

[0010] In carrying out these and other objects of the invention, there is provided, in one form, a method for scavenging a sulfur compound such as H₂S and/or a mercaptan from carbon dioxide which can either be liquid CO₂, supercritical CO₂, and mixtures thereof. The method involves adding to the CO₂ an effective amount of a triazine to scavenge at least a portion of the H₂S.

[0011] It has been discovered that triazines and particularly hexahydrotriazines can effectively scavenge H₂S from liquid and/or supercritical CO₂ itself. The invention was discovered while resolving the problem of handing the additional volume of CO₂ in a plant by removing the H₂S corresponding to the increased production.

[0012] While triazines are widely used in the natural gas industry for removal of H₂S, and also used in removing H₂S in tail gas processing where the tail gas comprises gaseous CO₂, the application of non-regenerable chemical liquid scavengers such as triazines has not been known or documented for the removal of H₂S from supercritical and liquid carbon dioxide prior to this invention. This is a very specialized application due to the fact that under supercritical conditions, CO₂ exists as a single fluid phase.

[0013] The work done on the inventive method investigated the actual removal of H₂S from supercritical CO₂ at high partial pressures of CO₂.

[0014] While many triazines are expected to be useful in the method of this invention, suitable hexahydrotriazines may have the formula:

[0015] where R¹, R² and R³ are independently selected from the group consisting of straight or branched alkyl groups, substituted or unsubstituted with hydroxyl groups, where the alkyl groups average from about 1 to about 20 carbon atoms, preferably from about 1 to about 5 carbon atoms. Triazines, such as the preferred hexahydrotriazines of the invention, are readily made by reacting formaldehyde with a primary amine or an alkanolamine where the amine is primary. Suitable reactants with formaldehyde include amines of the formula H₂NR^x where R^x can be defined as R¹, R², and R³ above. In one non-limiting embodiment, the preferred hexahydrotriazines include, but are not necessarily limited to, 1,3,5-tri-(2-hydroxyethyl)-hexahydro-S-triazine; 1,3,5-trimethylhexahydro-1,3,5-triazine; or mixtures thereof.

[0016] It is not always possible to predict with precision what the effective proportions of triazine are in removing or scavenging at least a portion of the H₂S from supercritical or liquid CO₂ since such dosage is typically dependent upon a number of complex, interrelated factors including, but not necessarily limited to, the partial pressure of the CO₂, the temperature of the CO₂, the particular nature of the triazine or blend of triazines if a blend is used, and the like. Nevertheless, in an effort to illustrate what an effective amount range may be, an effective amount of triazine ranges from about 1 to about 100 parts per part sulfur compound in the carbon dioxide on a weight basis. Preferably, the effective amount of triazine ranges from about 3 to about 20 parts per part sulfur compound, most preferably from about 3 to about 15 parts per part sulfur compound. These triazine scavengers have been shown to remove 1-2 pounds of H₂S per gallon of triazine (120-240 kg/m³) from supercritical/liquid CO₂, in one non-limiting embodiment of the invention.

[0017] In another non-limiting embodiment of the invention, the amount of H₂S in the liquid or supercritical CO₂ is reduced to less than 100 ppm, preferably less than about 80 ppm.

[0018] In application, the invention is a process for removing H₂S from supercritical CO₂ in a flow line using a triazine-based H₂S scavenger. A method such as the following may be used, in one non-limiting embodiment.

[0019] A suitable injection point is selected for the scavenger injection preferably as far upstream of the monitoring point as possible.

[0020] The scavenger is then pumped into the target flow line via a high-pressure, positive displacement pump, using an injection quill and a pulsation dampener.

[0021] In turbulent flow regime, the scavenger will be homogeneously distributed into the main body of the fluid, and such regime provides efficient mixing.

[0022] In the presence of efficient mixing and optimized injection set-up, triazine-based scavenger will react irreversibly with H₂S and form liquid reaction products.

[0023] The H₂S concentration in the CO₂ upstream from the injection point could be measured to establish the injection rate. The continuous scavenger injection rate could be continuously adjusted using a conventional feedback loop control system either from the upstream monitoring point, or a downstream monitoring point, or both.

[0024] In general, the triazine scavengers are water-soluble and are delivered in water as a solvent. Any other suitable solvent may also be used. The inventive process is applicable for removal of H₂S from liquid and/or supercritical CO₂ under conditions of temperature and pressure where injection of the treatment chemical does not increase the water content above its water saturation limit. For example, at 1200 psig (8300 kPa) and 70 F. (21 C.), the saturation limit is 130 pounds of water per MMSCF of CO₂ (2.110³ kg/m³), in one non-limiting embodiment of the invention. The volume of scavenger that can be injected should not introduce water exceeding the saturation point. The presence of any free water can cause very high corrosion rates in mild steel pipelines.

[0025] The triazine scavengers of this invention can remove H₂S from liquid and/or supercritical CO₂ at a wide range of temperatures and pressures, however; in general, the efficiency of the triazine scavengers increases with increasing temperatures and pressures.

[0026] As noted, carbon dioxide injection is widely used for secondary and tertiary recovery of hydrocarbons. Removal of H₂S from liquid and/or supercritical CO₂ will provide a cost effective treatment method to increase the volume of CO₂ processed and used for injection into the formation that will yield improved recovery of the hydrocarbons.

[0027] The invention will be further illustrated with respect to the following Examples, which are not intended to limit the invention in any way but rather are included to give a better sense of the invention.

[0028] A mixture of liquid CO₂ containing 500 ppm H₂S was blended in a 1000 cc bomb at 825 psig (5,690 kPa). The CO₂ was transferred from the pressure bomb to test pressure cells each having a volume of about 30 ml (30 cc). A first cell was maintained as a control and no scavenger was added to it.

[0029] To a second test cell was added 3 ml of a 1% 1,3,5-tri-(2-hydroxyethyl)-hexahydro-S-triazine scavenger, abbreviated herein as 1,3,5-triazine. The effective concentration of the 1,3,5-triazine was about 1000 ppm. The liquid CO₂ mixed with 500 ppm H₂S from the pressure bomb was used to fill the second test cell to the point where pressure equilibrated between the cell and the bomb. After the test cell was disconnected from the pressure bomb, the cell was shaken 50 times before placing it in a hood. The H₂S concentration in the gas phase was measured using Sensidyne stain tubes. A third test cell was employed in a similar manner using a higher concentration of 1,3,5-triazine scavenger. The results are presented in Table I:

TABLE I
Removal of H2S From Liquid CO2 at 825 psig
(5,690 kPa), 70 F. (21 C.) Using 1,3,5-Triazine Scavenger
Ex. No.	1,3,5-Triazine, ppm	Time, hours	H2S content, 10 ppm
1 (control)	0	0	500
		5	500
		10	500
2	1,000	0	520
		5	300
		10	240
3	3,000	0	500
		5	0
		10	0

[0030] From Example 2, it was calculated that the ratio of 1,3,5-triazine to H₂S removed was about 3.57:1, on a weight basis. From Example 3, the ratio of 1,3,5-triazine to H₂S removed was about 6:1.

[0031] The experimental set-up used for these Examples was in essence a static system. However, in an actual system, CO₂ would be flowing in turbulent flow (Reynolds number>106, velocity approximately 6.8 ft/s (2.1 mls), in a non-limiting embodiment), which would facilitate the mixing of the CO₂ with the scavenger. High velocities and efficient mixing should provide a significantly faster rate of H₂S removal. In natural gas applications, significant reductions in H₂S concentrations have been observed at contact times on the order of a few seconds to a few minutes, depending upon the operating conditions of the system. For example, if the distance between the injection point and the header where sweet CO₂ blends with the treated plant CO₂ is approximately 2000 ft (610 m), then CO₂ moving at a velocity of 6.8 ft/sec (2.1 m/s) will be in contact with the triazine scavenger for approximately 260 seconds.

[0032] These results clearly demonstrate that with sufficient contact time and at sufficient dosage, 1,3,5-triazine can remove H₂S from liquid CO₂. It is expected that the triazines of this invention can remove other sulfur compounds from liquid or supercritical CO₂ besides H₂S, such as mercaptans.

[0033] A field trial with the 1,3,5-triazine of Examples 1-3 was conducted on a line carrying supercritical CO₂. This line had characteristics similar to those expected at a plant injection point. Test results confirmed that given sufficient mixing by velocity and contact time 1,3,5-triazine successfully selectively scavenged H₂S in supercritical CO₂. However, variations in the incoming H₂S levels (ranging from 80 to 117 ppm H₂S) and limitations of selected experimental setup prevented determination of the efficiency of the reaction.

[0034] Many modifications may be made in the composition and implementation of this invention without departing from the spirit and scope thereof that are defined only in the appended claims. For example, the exact triazine used may be different from those used here. Blends of triazines are also expected to be useful. Further, sulfur compounds other than H₂S are expected to be removed from liquid or super-critical CO₂ using the triazines of this invention. Additionally, application conditions other than those specifically exemplified herein are anticipated to be environments in which the inventive method will find success.