Ultrahigh molecular weight polyethylene articles and method of manufacture

[0001] The invention is directed to ultrahigh molecular weight polyethylene (UHMWPE) articles and their manufacture.

[0002] UHMWPE is difficult to process because the resin does not flow when melted. Berins, M. L., ed., Plastics Engineering Handbook of the Society of the Plastic Industry, Chapman & Hall, New York City, N.Y. (1991), p. 52. Consequently, UHMWPE is processed by sintering, compression molding, ram extrusion, or gel processing. Sintering is a process where resins are agglomerated by solid-state diffusion. Heat and pressure are usually essential. Compression molding is a process where resins are shaped between the faces of a mold by heat and pressure. Ram extrusion is a process where resins are shaped by forcing it through a die. The force is provided by a ram. U.S. Pat. Nos. 5,234,652 and 5,399,308 disclose a dry extrusion process for a mixture consisting of resins and lubricant. Gel processing is a process where resins are formed into gels for subsequent processing. The gel is a dilute solution or suspension of resin in a solvent, e.g., an extractable solvent (or oil or plasticizer).

[0003] UHMWPE is gel spun into fibers. In gel spinning, the primary mechanism of solidification is the gelling of the polymer solution by cooling to form a gel filament consisting of precipitated polymer and solvent. Solvent removal is accomplished following solidification by washing in a liquid bath. This process is also used to form microporous films. See U.S. Pat. Nos. 4,588,633 and 5,248,461. In U.S. Pat. No. 4,588,633, the gel solution consists of 2-4% by weight of UHMWPE. See Examples 1-12. In U.S. Pat. No. 5,248,461, the gel solution consists of up to 20% by weight of UHMWPE. See Examples 1-20. These membranes are useful as, among other things, separators for electrochemical cells. See U.S. Pat. No. 4,588,633, column 4, lines 30-36 and U.S. Pat. No. 5,248,461, column 4, lines 57-60.

[0004] Another variant of gel processing is gel processing with a filler. For example, see U.S. Pat. Nos. 3,351,495, 4,833,172, and 5,948,557. Generally, UHMWPE, a processing oil (or plasticizer), and a filler are mixed in an extruder and subsequently made into microporous sheets. In U.S. Pat. No. 3,351,495, the solution consisted of up to 20% by volume of UHMWPE. See Examples 6, 8, 18, 19, 20, and 21. The microporous membranes formed were used as separators for batteries. See column 1, lines 24-33. In U.S. Pat. Nos. 4,833,172 and 5,948,557, a calcium/zinc stearate lubricant, PETRAC CZ-81, is added to the solution. See Tables 1 and 2, respectively. The microporous membranes formed were used as labels, diffusion membranes, and separators. See U.S. Pat. No. 5,948,557, column 1, lines 27-41.

[0005] There is a need to improve the processability of UHMWPE.

[0006] An article of manufacture comprises an ultrahigh molecular weight polyethylene (UHMWPE) mixed with a processing oil and a lubricant selected from the group consisting of fatty acid esters, ethoxylated fatty acid esters, glycol esters, PEG esters, glycerol esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, mercaptan ethoxylates, modified ethoxylates, amide surfactants, phosphate esters, phosphonate esters, phosphite esters, alkyl sulfates, fatty acid ethers, alkyl ether sulfates, alkylaryl ether sulfates, sulfonates, naphthalene sulfonates, sulfosuccinates, sulfonated esters, sulfonated amides, alkyl ether carboxylates, alkylaryl ether carboxylates, quaternary amines, amino quaternary amines, ethoxylated amines, imidazoline derivatives, betaines, sultaines, aminopropionates, catechol derivatives, saturated fatty acids, unsaturated fatty acids, and combinations thereof. The method for making those articles is also disclosed.

[0007] An article of manufacture is any shaped article. For example, articles of manufacture may include, but is not limited to, films, fibers, sheets, plates, slabs, bars, rods, billets, and blocks. Preferably, these articles are made by an extrusion process. These articles also may be microporous, for example, microporous sheets and films.

[0008] Ultrahigh molecular weight polyethylene (UHMWPE) is a polyethylene polymer having a weight average molecular weight greater than 510⁵. The polymer is either a homopolymer of ethylene or a copolymer of ethylene, with at most 10 mol % of one or more alpha-olefins. The polymer may be a blend with UHMWPE comprising at least 50% by weight of the blend and the balance being other polymers, such as, for example, polyolefins and synthetic and natural rubbers. The preferred weight average molecular weight is greater than 210⁶. The most preferred UHMWPE has a weight average molecular weight greater than 510⁶. UHMWPE resins are commercially available as GUR from Ticona LLC of Summit, N.J., STAMYLAN from DSM of Geleen, Netherland, UTEC from Polyailden of Camacari, Brazil, and HI-ZEX Million, LUBMER, and MIPELON, each from Mitsui Chemical of Tokyo, Japan. GUR 4130 (molecular weight about 4-5 million) and GUR 4170 (molecular weight about 8-9 million) are preferred.

[0009] Processing oil (or processing plasticizer) have little solvating effect on the UHMWPE at lower temperatures (e.g. 60 C.), but have a significant solvating effect at elevated temperatures (e.g. 200). Such oils include paraffinic oils, naphthalenic oils, and aromatic oils, as well as other materials including the phthalate ester plasticizers such as dibutyl phthalate, bis(2-ethylene)phthalate, diisodecyl phthalate, dicyclohexyl phthalate, butyl benzyl phthalate, and ditridecyl phthalate. Additional oils, plasticizers, and/or solvents are mentioned in U.S. Pat. Nos. 3,351,495; 4,588,633; 4,833,172; 5,248,461; and 5,948,557 are incorporated herein by reference.

[0010] The filler includes any particulate filler as is well known in the art. For example, see U.S. Pat. Nos. 3,351,495; 4,833,172; and 5,948,557 each is incorporated herein by reference. Preferably, the filler is a silica. Such fillers are commercially available under the tradename HiSil from PPG Industries, Inc. of Pittsburgh, Pa., SIPERANT from Degussa AG of Wesseling, Germany, ZEOSIL from Rhodia, Inc. of Cranberry, N.J. or KETJENSIL from Akzo Chemie of Compiegne, France.

[0011] Minor amounts of auxiliary components may be added. Such auxiliary components include: carbon black, stabilizers, and antioxidants. The compounds are conventional and known in the art.

[0012] Lubricants are compounds that, when added to an UHMWPE mixture, improve the processability of the UHMWPE mixture. Improved processability refers to a reduction in fusion time (the time it takes the polymeric system to melt (or dissolve) into a flowable solution). Improved processability is also seen as a reduction in energy consumption by the motor and as a reduction in mixture temperature when comparing systems with and without the lubricants. The results arising from this phenomenon include, but are not limited to, decreasing energy consumption, decreased thermal and mechanical degradation of the polymer, increased polymer strength, decrease machine wear, and increased polymer throughputs.

[0013] Such lubricants are selected from the material classes consisting of: fatty acid esters, ethoxylated fatty acid esters, glycol esters, PEG esters, glycerol esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, mercaptan ethoxylates, modified ethoxylates, amide surfactants, phosphate esters, phosphonate esters, phosphite esters, alkyl sulfates, fatty acid ethers, alkyl ether sulfates, alkylaryl ether sulfates, sulfonates, naphthalene sulfonates, sulfosuccinates, sulfonated esters, sulfonated amides, alkyl ether carboxylates, alkylaryl ether carboxylates, quaternary amines, amino quaternary amines, ethoxylated amines, imidazoline derivatives, betaines, sultaines, aminopropionate, catechol derivatives, saturated fatty acids, unsaturated fatty acids, and combinations thereof. Preferably, the lubricants are selected from the material classes consisting of: fatty acid esters, ethoxylated fatty acid esters, PEG esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, phosphate esters, phosphonate esters, phosphite esters and combinations thereof. Most preferred are sorbitol esters, ethoxylated sorbitol esters, and aromatic ethoxylates.

[0014] Such lubricants are commercially available. An exemplary list is set out in the Table below. Such lubricants specifically exclude the metallic salts of stearic acid (e.g., Zn stearate and Ca stearate) and lubricants containing same.

TABLE
Tradename or	General Class of
Abbreviation	Surfactants	Specific chemical	Company
Rhodasurf LA-12	Alcohol Ethoxylates	Mixed linear alcohol ethoxylate	Rhodia HPCII
Rhodasurf LA-3	Alcohol Ethoxylates	Mixed linear alcohol ethoxylate	Rhodia HPCII
Rhodapex CD-128	Alkyl (and Alkyllaryl) Ether	Ammonium Linear Alcohol Ether	Rhodia HPCII
	Sulfate	Sulfate
Rhodapon BOS	Alkyl Sulfates	Sodium 2-ethylhexyl Sulfate	Rhodia HPCII
Rhodapon UB	Alkyl Sulfates	Sodium Lauryl Sulfate	Rhodia HPCII
Alkamide STEDA/B	Amide surfactant	Ethylene Bisstearamide	Rhodia HPCII
Igepal CO-210	Aromatic Ethoxylates	Nonylphenol ethoxylates	Rhodia HPCII
Igepal CO-630	Aromatic Ethoxylates	Nonylphenol ethoxylates	Rhodia HPCII
Igepal RC-630	Aromatic Ethoxylates	Dodecyl Phenol Ethoxylates	Rhodia HPCII
Mirataine CBS	Betaines, Sultaines, and	Coco/Oleamidopropyl Betaine	Rhodia HPCII
	Aminopropionates
Mirataine COB	Betaines, Sultaines, and	Cocamidopropyl Hydroxy Sultaine	Rhodia HPCII
	Aminopropionates
Miranate LEC-80	Ether Carboxylate	Sodium Laureth 13 Carboxylate	Rhodia HPCII
Rhodameen PN-430	Ethoxylated Fatty Amines	Ethoxylated (5 moles) tallow amine	Rhodia HPCII
Rhodameen T-50	Ethoxylated Fatty Amines	Ethoxylated (50 moles) tallow	Rhodia HPCII
		amine
Calcium Stearate	Fatty acids, saturated	Calcium stearate
Linseed Oil	Fatty acids, unsaturated	Linoleic and linolenic acids	Hardware Store
Tung Oil	Fatty acids, unsaturated	Eleostearic acid	Hardware Store
Alkamuls GMS	Glycerol ester	Glycerol stearate	Rhodia HPCII
Kemester 1000	Glycerol trioleate	Glycerol trioleate	Crompton Corp.
Alkamuls EGDS	Glycol ester	Glycol distearate	Rhodia HPCII
Alkamuls JK	Guerbet ester	Guerbet diester	Rhodia HPCII
Neustrene 059	Hydrogenated tallow glycerol	(30% Palmitic, 60% Stearic)	Crompton Corp.
Neustrene 064	Hydrogenated tallow glycerol	(88% Stearic, 10% Palmitic)	Crompton Corp.
Miranol C2M-SF	Imidazoline derivative	Disodium Cocoampho	Rhodia HPCII
		Dipropionate
Miranol JEM	Imidazoline derivative	Sodium Mixed C8	Rhodia HPCII
		Amphocarboxylate
Antarox 724/P	Ethoxylate		Rhodia HPCII
Rhodacal N	Naphthalene Formaldehyde	Sodium Naphthalene	Rhodia HPCII
	Sulfonates	Formaldehyde Sulfonate
Supragil WP	Naphthalene Sulfonates	Sodium Diisopropyl Naphthalene	Rhodia HPCII
		Sulfonate
Alkamuls EL-620	PEG Ester	PEG-30 Castor Oil (ricinoleic	Rhodia HPCII
		oleic palmitic . . . )
Duraphos 2EHA PO4	Phosphate Ester	Phosphoric Acid, Mono & Di(2-	Rhodia HPCII
		ethylhexyl) ester
DEHPA extractant	Phosphate Ester	Phosphoric Acid, Bis(2-ethylhexyl)	Rhodia HPCII
		ester
Rhodafac LO-11A LA	Phosphate Ester	Phosphoric Acid, Blend of linear	Rhodia HPCII
octyl/decyl alcohol esters
Amgard TOF	Phosphate Ester	Phosphoric Acid, Tris(2-ethylhexyl)	Rhodia HPCII
		ester
Albrite B(2EH) 2EHP	Phosphonate Ester	Phosphonic Acid, (2-ethylhexyl)-	Rhodia HPCII
		bis 2-ethylhexyl) ester
Octylphosphonic Acid	Phosphonate Ester	Octyl Phosphonic Acid Ester	Rhodia HPCII
Rhodaquat DAET-90	Quaternary Amine	Complex ditallow sulfate	Rhodia HPCII
		quaternary amine
Alkamuls SML	Sorbitan ester	Sorbitan Monolaurate	Rhodia HPCII
Alkamuls SMO	Sorbitan ester	Sorbitan Monooleate	Rhodia HPCII
Alkamuls STO	Sorbitan ester, ethoxylated	Sorbitan Trioleate	Rhodia HPCII
OT-75, OT-100	Sulfosuccinates	Dioctyl sodium sulfosuccinate	Cytec

[0015] The components, UHMWPE, filler (optional), processing oil, and lubricant, are mixed. In formulations with filler, the weight ratio of polymer to filler may range from 1:1 to 1:5, 1:3 being preferred. The ratio of UHMWPE and filler to oil may range from 1:1 to 1:2, 1:1.5 being preferred. The lubricant may comprise up to 15 weight % of the formulation, with 0.2 to 8% being preferred. In formulation without filler, the polymer may comprise up to 80% by weight of the mixture, preferably in the range of 20-65% by weight. The ratio of oil to lubricant may range from 3:1 to 1:3, with the range of 2:1 to 1:2 being preferred. The components are preferably mixed in a continuous fashion, for example, in a twin screw extruder or a Brabender extruder or a screw extruder with a blown film die.

[0016] After mixing, the mixture is shaped. Shaping will depend upon the particular article desired, as is known in the art. For example, if a film or sheet is desired, then the appropriate die may be added to the extruder. After shaping, the articles are most often subjected to a step to remove the processing oil or solvent from the article (gel), (e.g., an extraction (or washing or leaching) step to remove processing oil and lubricant). This step is conventional. For example, see U.S. Pat. Nos. 3,351,495; 4,588,633; 4,833,172; 5,248,461; and 5,948,557 each is incorporated herein by reference. In formulations with filler, the extruded sheets are preferably subjected to an extraction step to remove processing oil. After extraction, these sheets may have about 0.5% (nominally 0%) to 30% by weight oil remaining, preferably 5-25%, and most preferably 10-20%. It is understood that it is impossible to remove all of the processing oil and lubricant from any of the mixtures, so at least a trace amount will remain in the final articles. In formulations without fillers, the extruded sheets are preferably subjected to an extraction step. After extraction, these sheets may have only residual amounts of oil and lubricant. Articles may be subjected to stretching or tentering before, during, or after extraction.

[0017] Preferably, these articles are formed into microporous sheets or films. Such microporous sheets and films may be used as labels, diffusion membranes, and separators in electrochemical devices (e.g., batteries, capacitors, and fuel cells). A battery is an electrochemical device having an anode, a cathode, an electrolyte, and a separator sandwiched between the anode and the cathode and impregnated with the electrolyte. Formulation with filler are used preferably in lead acid batteries. Formulations without filler are used preferably in lithium batteries.

[0018] In the following examples, set out in Tables 1-8, ultrahigh molecular weight polyethylene (GUR 4130 and GUR 4170 from Ticona LLC of Summit, N.J.), filler (specifically silica, HiSil from PPG of Pittsburgh, Pa.), processing oil (naphthalenic oil from Calumet Co. of Princeton, La.), and lubricant (as identified in the tables) were blended together and extruded from a twin screw extruder. The extruded product, a sheet, was subjected to an extraction step for the removal of processing oil. During extrusion, torque (% KW) and melt temperature were measured for comparison to control (examples without additive) and indicates the amount of energy needed to mix the components. After extraction, the amount of oil remaining in the article of manufacture (final oil %) was determined by a extraction technique in which: a dried, 1.33 inch (3.38 cm)6 inch (15.24 cm) piece of sheet was weighed (W1) and then immersed in 200 ml of fresh, room temperature hexane in a ultrasonic bath for at least 15 minutes; then the sample is dried and reweighed (W2). The % oil is (W1W2)/W1*100. Two samples are averaged. Additionally, basis weight was measured in conventional fashion, and thickness (web) by ASTM D 374, MD tensile by ASTM D 638, porosity by Battery Council International (BCI) TM-3.207, and ER by BCI TM-3.218 using a conventional tester from Palico Instrument Limited of Circle Pines, Minn. Puncture strength generally follows ASTM D3763 except as noted below: The instrument used was a Chatillon digital force guage DFIS 10 on a motorized test stand TCM 201. Chatillon/Ametek is located in Largo, Fla. The puncture tip is slightly rounded and 1.930 mm in diameter, and the platform hole is 6.5 mm in diameter. The travel speed is set at 300 mm/min, and at least 10 measurements are averaged across a representative area of the sample. This method is generally independent of sample size, and representative area of the sample refers to across the width and length of a reasonably sized sample. The peak force needed to puncture the sample is recorded in units of N or lbs.

[0019] In Tables 1-5, ingredients were mixed at the throat of the extruder, and in Tables 6-8, the lubricant was injected through the extruder's barrel.

TABLE 1
Examples	1	2	3	4	5	6	7	8
Additive name			A	B	C	D	E	F	G
Polymer type		4170	4170	4170	4170	4170	4170	4170	4170
Polymer	kg	4.14	4.14	4.14	4.14	4.14	4.14	4.14	4.14
Filler	kg	10.76	10.76	10.76	10.76	10.76	10.76	10.76	10.76
Additive	kg	0.00	1.09	1.09	1.09	1.09	1.09	1.09	1.09
Oil	kg	27.50	26.41	26.41	26.41	26.41	26.41	26.41	26.41
Torque	% KW	26	24	25	27	24	25	26	24
Melt Temp.	C.	210	214	214	216	208	268	208	212
Web Thickness	microns	189.2	217.2	220.0	209.8	208.0	206.2	205.5	203.2
Basis Weight	g/m2	106.9	140.0	140.9	127.1	134.1	129.4	134.0	127.0
Puncture	N	11.9	24.3	23.6	24.2	17.8	20.0	19.2	16.8
MD Tensile	N/mm2	17.5	28.9	29.1	29.3	27.3	21.9	26.4	21.6
Porosity	%	63.1	60.2	60.1	61.9	65.6	63.2	59.0	61.1
ER w/o Coating	mohm-cm2	582.6	285.2	279.4	285.2	385.2	505.8	705.8	541.3
Final Oil	%	18.2	13.9	14.1	15.2	14.9	16.7	14.5	19.7

[0020]

TABLE 2
Examples	9	10	11	12	13	14	15	16
Additive name			A	B	C	D	E	F	G
Polymer type		4130	4130	4130	4130	4130	4130	4130	4130
Polymer	kg	4.14	4.14	4.14	4.14	4.14	4.14	4.14	4.14
Filler	kg	10.76	10.76	10.76	10.76	10.76	10.76	10.76	10.76
Additive	kg	0.00	1.09	1.09	1.09	1.09	1.09	1.09	1.09
Oil	kg	27.50	26.41	26.41	26.41	26.41	26.41	26.41	26.41
Torque	% KW	28	24	26	27	25	28	25	26
Melt Temp.	C.	207	211	214	214	203	216	214	221
Web Thickness	microns	179.1	232.2	227.3	211.3	172.0	209.6	202.4	229.4
Basis Weight	g/m2	106.6	147.8	139.9	131.8	112.9	135.3	132.1	144.7
Puncture	N	11.8	20.4	21.0	17.0	14.2	16.6	15.9	14.8
MD Tensile	N/mm2	18.3	24.8	21.9	23.1	21.9	19.1	22.6	16.9
Porosity	%	67.2	60.7	63.7	63.0	61.6	63.6	60.6	62.2
ER w/o Coating	mohm-cm2	461.3	240.0	263.2	283.2	163.2	361.3	362.6	471.6
Final Oil	%	23.8	13.4	15.6	13.7	22.8	14.7	14.3	13.7

[0021]

TABLE 3
Examples	17	18	19	20	21	22
Additive name			A	B	C	F	H
Polymer type		4170	4170	4170	4170	4170	4170
Polymer	kg	3.10	3.10	3.10	3.10	3.10	3.10
Filler	kg	8.41	8.41	8.41	8.41	8.41	8.41
Additive	kg	0.00	0.82	0.82	0.82	0.82	0.82
Oil	kg	20.35	19.52	19.52	19.52	19.52	19.52
Torque	% KW	27	24	24	24	26	22
Melt Temp.	C.	208	211	210	211	210	208
Web Thickness	microns	173.0	161.5	177.8	180.1	177.8	191.3
Basis Weight	g/m2	111.7	119.6	107.3	123.5	126.3	140.3
Puncture	N	11.4	16.2	13.6	16.0	13.2	20.3
MD Tensile	N/mm2	20.3	34.5	18.4	24.2	20.6	26.5
Porosity	%	59.2	58.1	59.7	60.7	59.7	59.1
ER w/o Coating	mohm-cm2	434.8	127.7	145.8	248.4	435.5	76.1
Final Oil	%	14.0	13.7	13.9	13.7	12.9	12.8

[0022]

TABLE 4
Examples	17	23	24	25	40
Additive				A	H	A
name
Polymer		4170	4130	4170	4170	4170
type
Polymer	kg	3.10	3.10	2.87	2.87	4.39
Filler	kg	8.41	8.41	9.20	9.20	11.86
Additive	kg	0.00	0.82	1.63	1.63	1.12
Oil	kg	20.35	20.35	18.78	18.78	26.99
Torque	% KW	27	24	23	23	23
Melt	C.	208	209	211	208	216
Temp.
Web	microns	173.0	177.8	180.3	172.7	114.3
Thickness
Basis	g/m2	111.7	113.3	135.4	137.4	83.8
Weight
Puncture	N	11.4	10.1	13.5	17.5	11.4
MD	N/mm2	20.3	16.9	21.6	32.8	27.1
Tensile
Porosity	%	59.2	62.3	59.0	58.5	65.5
ER w/o	mohm-cm2	434.8	464.5	78.1	64.5	36.1
Coating
Final Oil	%	14.0	14.6	12.5	11.6	14.7

[0023]

TABLE 5
Examples	26	31	27	28	29	30
Additive name				I	J	K	K
Polymer type		4130	4170	4170	4170	4170	4170
Polymer	kg	3.10	4.39	3.10	3.10	4.34	3.25
Filler	kg	8.41	11.86	8.41	8.41	11.75	8.81
Additive	kg	0.00	0.00	0.82	0.82	0.53	0.82
Oil	kg	20.35	28.66	19.52	19.52	27.86	20.48
Torque	% KW		28	23	23	24	25
Melt Temp.	C.		217	217		222	227
Web Thickness	microns	188.5	183.4	192.8	179.6	198.9	191.5
Basis Weight	g/m2	100.1	102.4	117.9	127.2	114.6	116.7
Puncture	N	9.6	13.1	16.8	22.0	11.5	12.8
MD Tensile	N/mm2	15.6	20.4	28.4	33.2	12.8	12.5
Porosity	%	63.0	66.3	62.5	61.1	66.2	65.9
ER w/o Coating	mohm-cm2	320.3	221.9	109.8	397.4	292.3	220.0
Final Oil	%	13.7	10.9	11.2	11.5	11.9	12.5

[0024]

TABLE 6
Examples	31	32	33	34	35	41
Additive name			J	J	J	J	J
Polymer type		4170	4170	4170	4170	4170	4170
Polymer	kg	4.39	4.39	4.39	4.39	4.39	3.35
Filler	kg	11.86	11.86	11.86	11.86	11.86	9.04
Additive	kg	0.00	0.55	1.12	2.32	3.59	1.63
Oil	kg	28.66	27.83	26.99	25.25	23.42	23.59
Torque	% KW	28	28	26	24	25	24
Melt Temp.	C.	217	210	207	205	204	204
Web Thickness	microns	183.4	175.3	182.9	162.6	170.2	182.9
Basis Weight	g/m2	102.4	119.2	122.2	126.0	141.2	118.5
Puncture	N	13.1	15.2	20.8	22.5	24.5	17.1
MD Tensile	N/mm2	20.4	24.3	38.2	48.8	48.5	22.1
Porosity	%	66.3	65.3	61.4	58.1	57.0	61.1
ER w/o Coating	mohm-cm2	221.9	198.7	282.6	1052.9	751.6	543.9
Final Oil	%	10.9	12.8	12.5	13.9	13.3	13.8

[0025]

TABLE 7
Examples	31	36	37	38	39
Additive			H	H	H	H
name
Polymer		4170	4170	4170	4170	4170
type
Polymer	kg	4.39	4.39	4.39	4.39	4.39
Filler	kg	11.86	11.86	11.86	11.86	11.86
Additive	kg	0.00	0.55	1.12	2.32	3.59
Oil	kg	28.66	27.83	26.99	25.25	23.42
Torque	% KW	28	25	24	26	27
Melt	C.	217	213	201	200	204
Temp.
Web	microns	183.4	170.2	182.9	183.6	167.6
Thickness
Basis	g/m2	102.4	108.2	152.2	145.4	156.4
Weight
Puncture	N	13.1	12.9	22.5	16.4	14.8
MD	N/mm2	20.4	21.3	46.7	38.3	33.4
Tensile
Porosity	%	66.3	64.4	61.2	61.1	57.0
ER w/o	mohm-cm2	221.9	46.5	223.9	593.5	150.3
Coating
Final Oil	%	10.9	14.1	12.9	13.8	12.5

[0026]

TABLE 8
Examples	49	42	43	44	45	46	47	48
Additive name			L	M	N	O	P	Q	R
Polymer type		4170	4170	4170	4170	4170	4170	4170	4170
Polymer	Kg	3.25	3.25	3.25	3.25	3.25	3.25	3.25	3.25
Filler	Kg	8.79	8.79	8.79	8.79	8.79	8.79	8.79	8.79
Additive	Kg	0.00	0.82	0.82	0.82	0.82	0.82	0.82	0.82
Oil	Kg	21.27	20.34	20.34	20.34	20.34	20.34	20.34	20.34
Torque	% KW	24	24	24	24	23	24	23	24
Melt Temp.	C.	227	234	233	236	235	234	234	237
Web Thickness	microns	157.5	177.8	167.6	175.3	185.4	162.6	180.3	175.3
Basis Weight	g/m2	110.6	126.3	120.0	125.0	129.4	119.4	119.4	125.6
Puncture	N	10.6	18.5	15.9	18.5	16.4	17.5	13.8	17.4
MD Tensile	N/mm2	16.3	34.8	31.9	45.7	31.6	35.8	33.1	35.8
Porosity	%	64.5	61.6	62.5	63.0	63.4	61.7	63.0	63.7
ER w/o Coating	Mohm-cm2	470.3	872.9	1707.1	201.3	376.1	225.2	294.8	19.4
Final Oil	%	13.6	12.5	12.7	14.3	14.0	14.8	15.5	14.3

[0027] In the following examples, set out in Table 9, ultrahigh molecular weight polyethylene (GUR 4130 from Ticona LLC of Summit, N.J.), processing oil (naphthalenic oil from Calumet Co. of Princeton, La.), and lubricant (as identified in the table) were blended together and extruded from a twin screw extruder. The extruded product was observed as it exited the extruder die and categorized by appearance scale 1-10. A rating of 10 meant a smooth product that appeared well mixed, and a rating of 1 meant a very grainy and rough appearance.

TABLE 9
Examples:	46	47	48	49	50	51	52	53	54	55
polymer wt %	33.0	38.5	52.9	38.5	52.2	50.0	45.0	61.0	25.0	65.0
oil wt %	33.0	46.1	17.7	38.5	23.9	35.0	20.0	14.0	50.0	12.7
additive wt %	33.0	15.4	29.4	23.0	23.9	15.0	35.0	25.0	25.0	22.3
name additive	J	J	J	J	J	J	J	J	J	J
VISUAL RATING	5	6	8	8	9	4	1	10	10	4
A Phosphate Ester; fatty alcohol blend phosphate esters; Rhodafac LO-11A LA from Rhodia HPCII of Cranberry, NJ.
B Phosphate Ester; Bis(2-ethylhexyl) phosphate ester from Rhodia HPCII of Cranberry, NJ.
C Phosphate Ester; Bis(2-ethylhexyl) mono(2-ethylhexyl) phosphate esters from Rhodia HPCII of Cranberry, NJ.
D Phosphonate Ester; 2-ethylhexyl bis(2-ethylhexyl) phosphonate ester from Rhodia HPCII of Cranberry, NJ.
E Phosphate Ester; Tris(2-ethylhexyl) phosphate ester from Rhodia HPCII of Cranberry, NJ.
F Fatty acids, unsaturated; linoleic and linolenic acids; Linseed Oil.
G Fatty acids, unsaturated; eleostearic acid; Tung Oil.
H Phosphonate Ester; octyl phosphonic acid ester from Rhodia HPCII of Cranberry, NJ.
I PEG Esters; PEG-30 castor oil (ricinoleic oleic palmitic . . . ); Alkamuls EL-620 from Rhodia HPCII of Cranberry, NJ.
J Sorbitan Esters; sorbitan monooleate; Alkamuls SMO from Rhodia HPCII of Cranberry, NJ.
K Sulfosuccinate Ester; dioctyl sodium sulfosuccinate; OT-100 from Cytec Industries of Charlotte, NC.
L Sorbitan Ester; sorbitan monolaurate; Alkamuls SML from Rhodia HPCII of Cranberry, NJ.
M Sorbitan Ester Ethoxylated; sorbitan trioleate; Alkamuls STO From Rhodia HPCII of Cranberry, NJ.
N Aromatic Ethoxylate; dodecyl phenol ethoxylates; lgepal RC-630 From Rhodia HPCII of Cranberry. NJ.
O Aromatic Ethoxylate; nonylphenol ethoxylates; lgepal CO-210 From Rhodia HPCII of Cranberry, NJ.
P Aromatic Ethoxylate; nonylphenol ethoxylates; lgepal CO-630 From Rhodia HPCII of Cranberry, NJ.
Q Alcohol Ethoxylate; mixed linear alcohol ethoxylates; Rhodasurf LA-3 from Rhodia HPCII of Cranberry, NJ.
R Alcohol Ethoxylate; mixed linear alcohol ethoxylates; Rhodasurf LA-12 from Rhodia HPCII of Cranberry, NJ.

[0028] In the following examples, set out in Table 10, ultrahigh molecular weight polyethylene (GUR 4170 from Ticona LLC, Summit, N.J.), filler (silica, HiSil from PPG of Pittsburgh, Pa.), processing oil (naphthelenic oil from Calumet Co. of Pamaton, La.), and lubricant (as identified in the table) were mixed together and extruded from a Brabender extruder (B W Brabender Co. of South Hackensack, N.J.). In the control, 5.42 grams of UHMWPE was mixed with 14.65 g filler and 30.56 g oil. In the other examples, 5.42 grams of UHMWPE was mixed with 14.65 filler, 29.06 g oil and 1.50 g lubricant. This procedure is used to predict the lubricant's efficacy by observing fusion time and terminal torque. The fusion time is a measure of when the polymer dissolves in the oil (phase inversion of the polymer). The fusion time is typically the second go peak on a plot of torque as a function of time. The fusion time typically occurs after a first peak which indicates wetting of the polymer by the oil. The terminal torque is measured after 10 minutes of mixing.

	TABLE 10
		Fusion Time	Terminal
	Additive	(sec)	Torque (mg)
	Control - 59% Oil	182	660
	Octyl PO4	42	501
	Antarox 724/P	48	685
	Alkamide STEDA/B	55	845
	Rhodasurf LA-12	61	633
	T(2EH)PO4	64	640
	Alkamuls SMO	65	566
	Igepal CO-630	66	627
	Alkamuls STO	66	553
	Alkamuls SML	71	607
	Rhodasurf LA-3	74	545
	Alkamuls EL-620	83	583
	Igepal CO-210	88	528
	Igepal RC-630	92	601
	Linseed Oil	92	650
	B(2EH)2EHP1	92	610
	2EHAPO4	95	465
	DEHPA	100	410
	Rhodafac LO-11A	109	516
	Rhodapon BOS	110	623
	Tung Oil	114	647
	OT-75	115	820
	Rhodapex CD-128	122	570
	Miranol C2M-SF	125	678
	Mirataine COB	135	730
	Mirataine CBS	135	752
	Miranate LEC-80	140	672
	Miranol JEM	149	727
	Rhodapon UB	152	892
	Supragil WP	153	776
	Ca Stearate	196	766
	Rhodacal N	230	816
	Neustrene 059
	Neustrene 064
	Kemester 1000
	Rhodaquat DAET-90
	Rhodameen PN-430
	Rhodameen T-50
	Alkamuls GMS
	Alkamuls EGDS
	Alkamuls JK

[0029] The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicated the scope of the invention.