US 2003/0173330 A1Application
Micromechanical component and method for producing the same
Publication Date:2003-09-18
•21 Claims
•3 Drawing Sheets
Abstract
A method of manufacturing a micromechanical component having the following steps is described: providing a substrate (1); providing a first micromechanical functional layer (5) on the sacrificial layer (4); structuring the first micromechanical functional layer (5) in such a manner that it is provided with a mobilizable sensor structure (6); providing and structuring a first sealing layer (8) on the structured first micromechanical functional layer (5); providing and structuring a second micromechanical functional layer (10) on the first sealing layer (8) which has at least a covering function and is at least partially anchored in the first micromechanical functional layer (5); making the sensor structure (6) movable and providing a second sealing layer (8) on the second micromechanical functional layer (10). A corresponding micromechanical component is also described.
Metadata
Inventor
- Markus Lutz
Application Information
Application Number:US 10/240,339
Filing Date:2003-05-09
Priority Date:2000-04-07
Patent Drawings (3 sheets)
Description
Background Information
[0001] The present invention relates to a micromechanical component having a substrate an a movable sensor structure in a first micromechanical functional layer on the sacrificial layer. The present invention also relates to a corresponding manufacturing method.
[0002] Although it is applicable to any micromechanical components and structures, in particular to sensors and actuators, the present invention and the underlying problem are elucidated with reference to a micromechanical component, e.g., an acceleration sensor, that is manufacturable using silicon surface micromechanical technology.
[0003] Monolithically integrated inertial sensors manufactured by surface micromechanical technology in which the sensitive movable structures are situated on the chip without protection (analog devices) are generally known. This results in increased expenses for handling and packaging.
[0004] This problem may be circumvented by a sensor, the structures manufactured by surface micromechanics being covered by a second cap wafer. This type of packaging is responsible for a large share (approximately 75%) of the cost of manufacturing an acceleration sensor by surface micromechanical. These costs arise as a result of the high surface area requirements of the sealing surface between the cap wafer and the sensor wafer and due to the complex structuring (2-3 masks, bulk micromechanics) of the cap wafer.
[0005] The structure of a functional layer system and a method for hermetic capping of sensors using surface micromechanics is described in German Patent Application 195 37 814 A1. The manufacture of the sensor structure using known technological methods is explained. The cited hermetic capping is performed using a separate cap wafer made of silicon, which is structured using expensive structuring processes such as KOH etching. The cap wafer is applied to the substrate with the sensor (sensor wafer) using a seal glass. This requires a wide bonding frame around each sensor chip to ensure an adequate adhesion and sealing ability of the cap. This limits the number of sensor chips per sensor wafer considerably. Due to the large amount of space required and the expensive manufacture of the cap wafer, sensor capping incurs considerable costs.
Advantages of the Invention
[0006] The manufacturing method of the present invention having the features of claim 1 and the micromechanical component as recited in claim 12 have the following advantages.
[0007] It builds on a known surface micromechanical method which creates epitaxial polysilicon of a thickness of at least 10 m to form a micromechanical functional layer. No novel permeable layer is required but rather known processes are used. The only novel feature is the step to produce the sealing layers which have a sealing and leveling function.
[0008] The result is that the surface micromechanical method is simplified since the cap wafer is not needed due to the second micromechanical functional layer which performs at least one cover function and the structures may be contacted from above.
[0009] In addition, the functionality of the process is enhanced, i.e., additional mechanical and/or electrical components to implement the component are available to the designer. The following functional elements in particular may be created:
[0010] a pressure sensor diaphragm in the second micromechanical functional layer;
[0011] a printed conductor structure in the second micromechanical functional layer which is capable of crossover with an additional printed conductor structure provided above the second sealing layer;
[0012] very low-resistance aluminum leads in the additional printed conductor structure provided above the second sealing layer;
[0013] a vertical differential capacitor;
[0014] additional anchor points of the structures of the first micromechanical functional layer in the second micromechanical functional layer.
[0015] Customary IC packaging methods such as hybrid, plastic, flip-chip, etc. may also be used.
[0016] The dependent claims contain advantageous refinements of and improvements on the object of the present invention.
[0017] According to a preferred refinement, a sacrificial layer is provided on the substrate and the sacrificial layer is etched to mobilize the sensor structure. In a simplified version, the substrate may be provided with a sacrificial layer and the first micromechanical functional layer may be provided as a silicon-on-insulator (SOI) structure.
[0018] According to another preferred refinement, the first micromechanical functional layer is structured in such a way that it has passages extending to the sacrificial layer. Furthermore, the second micromechanical functional layer is structured in such a way that it has second passages extending to the first sealing layer, the second passages being connected to the first sealing layer by connection areas. The first sealing layer is then etched to remove the connection areas using the second passages as etch channels. Finally, the sacrificial layer is etched using the first and second passages connected together by the removal of the connection areas. This minimizes the cost of the etching processes since it is possible to etch the sacrificial layer and the first sealing layer in one step.
[0019] Thus, etch channels running through the first and second micromechanical functional layer and the intermediate first sealing layer are produced to remove the optionally provided sacrificial layer. This makes it possible to increase the thickness of the second micromechanical functional layer and improve its strength or stiffness. As a consequence, it is possible to span large areas and expose the components to greater stress. When removing the sacrificial layer, it not necessary to be concerned with the aluminum of the printed conductors or the like since it is not applied until a later point in time.
[0020] According to another preferred refinement, a buried polysilicon layer is provided below the first or second micromechanical functional layer. It is also possible to dispense with the buried polysilicon and an insulation layer lying below it since additional wiring levels above the sensor structure are available.
[0021] According to another preferred refinement, the first and second sealing layer are designed substantially thinner than the first and second micromechanical functional layer.
[0022] According to another preferred refinement, the first and/or second sealing layers are provided by a nonconforming deposition in such a manner that only the upper areas of the first and second passages, respectively, are obstructed. This reduces the etching time for removal of the sacrificial layer since only a portion of the passages is obstructed.
[0023] According to another preferred refinement, the first and/or second passages are designed as trenches or holes which narrow toward the top.
[0024] According to another preferred refinement, the first and/or second micromechanical functional layers are made of a conductive material, preferably polysilicon.
[0025] According to another preferred refinement, the first and/or second sealing layers are made of a dielectric material, preferably silica.
[0026] According to another preferred refinement, one or more printed conductor layers, preferably made of aluminum, are provided on the second sealing layer.
[0027] According to another preferred refinement, a printed conductor structure is integrated into the second micromechanical functional layer.
Drawing
[0028] Exemplary embodiments of the present invention are illustrated in the drawing and described in detail in the description below.
[0029] FIG. 1 shows a schematic cross-sectional view of a micromechanical component according to a first embodiment of the present invention in a first process stage;
[0030] FIG. 2 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a second process stage;
[0031] FIG. 3 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a third process stage;
[0032] FIG. 4 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a fourth process stage and
[0033] FIG. 5 shows an enlarged detail of the schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention as shown in FIG. 4 .
Detailed Description of the Exemplary Embodiments
[0034] In the figures, identical reference symbols denote identical or functionally equivalent components.
[0035] FIG. 1 shows a schematic cross-sectional view of a micromechanical component according to a first embodiment of the present invention in a first process stage.
[0036] In FIG. 1, 1 denotes a silicon substrate wafer, 2 a lower oxide, 3 a buried polysilicon layer, 4 a sacrificial oxide, 20 a contact hole in lower oxide 2 and 21 denotes contact holes in sacrificial oxide 4.
[0037] In order to manufacture the structure shown in FIG. 1 , lower oxide 2 is first deposited on the entire surface of silicon substrate wafer 1. In a subsequent step, polysilicon is deposited and structured to produce printed conductors in buried polysilicon layer 3.
[0038] Subsequently, sacrificial oxide 4 is applied to the entire surface of the overall structure using, for example, a low-temperature oxide (LTO) method or a tetraethyl orthosilicate (TEOS) method. Then contact holes 20 and 21 are created at the intended locations using conventional photomethods and etching methods.
[0039] FIG. 2 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a second process stage.
[0040] In addition to the reference symbols already introduced in FIG. 2, 5 denotes a first micromechanical functional layer in the form of an epitaxial polysilicon layer, 6 a sensor structure (comb structure) to be mobilized later, 7 trenches in first micromechanical functional layer 5, 8 a first sealing oxide (LTO, TEOS or the like), 9 plugs in trenches 7 made of sealing oxide 8, 16 oxide connection areas for the later sacrificial oxide etching and 22 contact holes in sealing oxide 8.
[0041] To manufacture the structure shown in FIG. 2 , epitaxial polysilicon is first deposited in a known manner to form first micromechanical functional layer 5 and micromechanical functional layer 5 is structured to form sensor structure 6 to be mobilized and trenches 7.
[0042] This is followed by a refill process to seal trenches 7 using sealing oxide 8 and subsequent optional planarization. Although it is not mentioned explicitly below, such planarization may in principle be performed after each layer deposition on the entire surface.
[0043] In the example shown, the refill is not complete but rather covers 100% of the underlying structure upward only and also provides a seal. This is shown in greater detail in FIG. 5 .
[0044] A process follows to form contact holes 22 by conventional photomethods and etching methods. These contact holes 22 are used to anchor second micromechanical functional layer 10 to be applied later (see FIG. 3 ) and to limit oxide connection areas 16 for later sacrificial oxide etching.
[0045] FIG. 3 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a third process stage.
[0046] In addition to the reference symbols already introduced in FIG. 3, 10 denotes a second micromechanical functional layer in the form of an epitaxial polysilicon layer and 11 denotes trenches in second micromechanical functional layer 10.
[0047] To form the structure shown in FIG. 3 , second micromechanical functional layer 10 is deposited in a manner similar to first micromechanical functional layer 5 as a stable sealing layer for underlying sensor structure 6. In addition to this sealing function, second micromechanical functional layer 10 may of course also be used for contacting, as a feed, as an upper electrode, etc. for the component. This layer 10 is then structured to produce trenches 11 which are later required together with trenches 9 for the sacrificial oxide etching.
[0048] FIG. 4 shows a schematic cross-sectional view of the micromechanical component according to the first embodiment of the present invention in a fourth process stage.
[0049] In addition to the reference symbols already introduced in FIG. 4, 13 denotes a second sealing oxide (LTO, TEOS or the like), 14 a contact hole in sealing oxide 13, 15 a printed conductor level made of aluminum which is connected to second micromechanical functional layer 10 via contact holes 14.
[0050] Starting from the process stage shown in FIG. 3 , the following steps are carried out to achieve the process stage according to FIG. 4 . First, sealing oxide 8 is etched to remove oxide connection areas 16 using second trenches 11 as etch channels. Sacrificial layer 4 is then etched using first and second trenches 7, 11 connected together by removing connection areas 16 as etch channels. A long sacrificial oxide etching is possible since no aluminum is present on the surface at this time.
[0051] In a subsequent process step, a second refill process forms second sealing oxide 13, this deposition also not being a conforming deposition but rather only the surfaces of trenches 11 are occluded. This is illustrated in greater detail in FIG. 5 . The internal pressure or internal atmosphere contained in sensor structure 6 is a function of the process conditions of the refill process. These parameters determine, e.g., the damping of the sensor structure.
[0052] Second sealing oxide 13 is then structured to form contact holes 14 and printed conductor level 15 made of aluminum is deposited and structured.
[0053] Although the present invention has been described above on the basis of a preferred exemplary embodiment, it is not limited to it but instead is modifiable in a variety of ways.
[0054] In particular, any micromechanical base materials such as, e.g., germanium may be used and not only the silicon substrate cited as an example.
[0055] Also, any sensor structures may be formed and not only the acceleration sensor illustrated.
[0056] Although not shown in the figures, trenches 7 and 11 may be designed to narrow toward the top in order to promote the non-conforming deposition of first and second sealing layers 8, 13.
[0057] The layer thicknesses of first and second micromechanical functional layer 5, 10 may be varied by the epitaxial and planarization process in a simple manner since the sacrificial layer etching is not a function of the permeability of the second micromechanical functional layer.
[0058] Of course, the micromechanical functional layer/sealing layer sequence may be repeated and it is also possible to provide a buried printed conductor under each micromechanical functional layer above the underlying micromechanical functional layer.
[0059] Finally, it is also possible to apply additional wiring levels made of aluminum or other suitable metals with dielectric lying between them.
[0060] It is also possible to planarize the individual levels using chemical-mechanical polishing, for example, in a single polishing step, preferably only for the second sealing level.
Claims
1. A method of manufacturing a micromechanical component including the steps:
providing a substrate (1);
providing a first micromechanical functional layer (5) on a sacrificial layer (4);
structuring the first micromechanical functional layer (5) in such a way that it has a mobilizable sensor structure (6);
providing and structuring a first sealing layer (8) on the structured first micromechanical functional layer (5);
providing and structuring a second micromechanical functional layer (10) on the first sealing layer (8) which has at least a covering function and is at least partially anchored in the first micromechanical functional layer (5);
making the sensor structure (6) movable; and providing a second sealing layer (13) on the second micromechanical functional layer (10), the first and second sealing layers (8, 13) being designed substantially thinner than the first and second micromechanical functional layer (5, 10).
2. The method as recited in claim 1, characterized by the steps:
providing a sacrificial layer (4) on the substrate (1), and
etching the sacrificial layer (4) to make the sensor structure (6) movable.
3. The method as recited in claim 1 or 2, characterized by the steps:
structuring the first micromechanical functional layer (5) in such a way that it has first passages (7) extending to the sacrificial layer (4);
structuring the second micromechanical functional layer (10) n such a way that it has second passages (11) extending to the first sealing layer (8), the second passages being connected to the first passages (7) by connection areas (16) of the first sealing layer (8); etching the first sealing layer (8) to remove the connection areas (16) using the second passages (11) as etch channels; and
etching the sacrificial layer (4) using the first and second passages (7, 11), connected to each other by removing the connection areas (16), as etch channels.
4. The method as recited in claim 1, 2 or 3,
wherein a buried polysilicon layer (3) is provided below the first and second micromechanical functional layer (5, 10).
5. The method as recited in one of the preceding claims,
wherein the first and/or second sealing layers (8, 13) are provided by a non-conforming deposition in such a way that only the upper areas of the first and second passages (7, 11) are occluded.
6. The method as recited in claims 3 through 5,
wherein the first and/or second passages (7, 11) are designed as trenches or holes which narrow toward the top.
7. The method as recited in one of the preceding claims,
wherein the first and/or second micromechanical functional layers (5, 10) are manufactured from a conductive material, preferably polysilicon.
8. The method as recited in one of the preceding claims,
wherein the first and/or second sealing layers (8, 13) are manufactured from a dielectric material, preferably silica.
9. The method as recited in one of the preceding claims,
wherein one or more printed conductor layers (15), preferably made of aluminum, are provided on the second sealing layer (13).
10. The method as recited in one of the preceding claims,
wherein a printed conductor structure is integrated into the second micromechanical functional layer (10).
11. A micromechanical component comprising:
a substrate (1);
a movable sensor structure (6) in a first micromechanical functional layer (5) situated above the substrate; a first sealing layer (8) on the first micromechanical functional layer (5) which is at least partially structured;
a second micromechanical functional layer (10) on the first sealing layer (8) which has at least a covering function and is at least partially anchored in the first micromechanical functional layer (5); and
a second sealing layer (8) on the second micromechanical functional layer (10),
wherein the first and second sealing layer (8, 13) are substantially thinner than the first and second micromechanical functional layer (5, 10).
12. The micromechanical component as recited in claim 11,
wherein the movable sensor structure (6) is situated above a sacrificial layer (4) located on the substrate (1) and is mobilized by at least partial removal of the sacrificial layer (4).
13. The micromechanical component as recited in claim 12,
wherein the first micromechanical functional layer (5) has first passages (7) extending to the depth of the sacrificial layer (4);
the second micromechanical functional layer (10) has second passages (11) extending to the depth of the first sealing layer (8); and
the first and second passages (7, 11) are connected to each other by removed connection areas (16) of the first sealing layer (8).
14. The micromechanical component as recited in claim 11, 12 or 13,
wherein a buried polysilicon layer (3) is provided below the movable sensor structure (10) between the sacrificial layer (4) and the substrate (1).
15. The micromechanical component as recited in one of claims 11 through 14,
wherein the first and/or second sealing layer (8, 13) has plugs (9, 9) for sealing corresponding first and second passages (7, 11).
16. The micromechanical component as recited in one of claims 13 through 15,
wherein the first and/or second passages (7, 11) are trenches or holes which narrow toward the top.
17. The micromechanical component as recited in one of claims 11 through 16,
wherein the first and/or second micromechanical functional layer (5, 10) is manufactured from a conductive material, preferably polysilicon.
18. The micromechanical component as recited in one of claims 11 through 17,
wherein the first and/or second sealing layers (8, 13) are manufactured from a dielectric material, preferably silica.
19. The micromechanical component as recited in one of claims 11 through 18,
wherein one or more printed conductor layers (15), preferably made of aluminum, are provided on the second sealing layer (13).
20. The micromechanical component as recited in one of claims 11 through 19,
wherein the second micromechanical functional layer (10) has a printed conductor structure.
21. The micromechanical component as recited in one of claims 11 through 20,
wherein the second micromechanical functional layer (10) has a diaphragm structure.