Pressure sensitive adhesives

[0001] (Not Applicable)

[0002] (Not Applicable)

[0003] The present invention relates to pressure sensitive adhesives based on aqueous latex emulsions and processes for the preparation of the adhesives. Pressure sensitive adhesives prepared according to the present invention have mean particle diameter sizes of less than or equal to about 100 nm and narrow particle size distributions. These pressure sensitive adhesives are particularly suitable for applications that require that the pressure sensitive adhesive maintain adhesion between the substrate and facestock when subjected to hot water spraying or immersion. In addition, the adhesives exhibit resistance to water-whitening or blush. Hot water adhesion is required in applications such as bottle labels where the bottles are subjected to hot water spraying in washing operations. In general, resistance to water-whitening is desirable anywhere a pressure sensitive adhesive with transparent facestock or substrate is subjected to water or high humidity. Examples include labels on the sides of trucks, signs and bottles.

[0004] Methods of providing water-whitening resistant latex emulsions for use in pressure sensitive adhesives are disclosed in the art. U.S. Pat. Nos. 5,286,843 and 5,536,811 disclose a process for improving the water-whitening resistance of pressure sensitive adhesives containing an aqueous latex emulsion and water soluble ions by removing the water soluble ions and adjusting the pH to at least about 6. The patents disclose that water soluble ions may be removed by a number of techniques including centrifugation, dialysis, precipitation and deionization with ion exchange resins. The preferred method of removing the water soluble ions is to contact the aqueous latex emulsion, the formulated pressure sensitive adhesive containing the aqueous emulsion or both with an ion exchange resin. International Application WO 97/11996 discloses a process for preparing hot water-whitening resistant latex emulsions useful in pressure sensitive adhesive compositions. The process involves copolymerizing a monomer mixture containing at least one alkyl acrylate ester of an alcohol containing at least 4 carbon atoms, at least one polar co-monomer and at least one partially soluble co-monomer present in an amount of at least about 7 weight %. Polymerization is carried out in the presence of at least one nonionic surfactant containing at least 8 moles of ethylene oxide and at least one anionic surfactant containing up to about 10 moles of ethylene oxide. The polymerization product is neutralized to produce an emulsion having a pH greater than 7 and containing particles having a volume average particle size diameter up to about 165 nm. An electrolyte may be added subsequent to polymerization to stabilize opacity of a film cast from the emulsion. International Application WO 98/44064 discloses inherently tacky pressure sensitive adhesives prepared by emulsion polymerization of at least one monomer mixture comprising; at least one alkyl acrylate, the alkyl group of which has from 4 to 12 carbon atoms; at least one unsaturated carboxylic acid containing from about 3 to 5 carbon atoms and one styrenic monomer; wherein the particles have a mean diameter of 300 nm or less. The publication discloses a single stage preparation of aqueous acrylic emulsions in examples 4D, 4E, 4F, 4G and 4H with average particle sizes ranging from 245 nm to 139 nm. Each of the examples discloses the use of silane crosslinkers to improve blush resistance. The reference discloses a preferred method of preparation which yields adhesives resistant to water-whitening and involves a sequential polymerization of a first and second monomer charge. None of the above references disclose a pressure sensitive adhesive that maintains adhesion in hot water environments and is resistant to water-whitening.

[0005] It has been found that pressure sensitive adhesives that maintain adhesion in hot water environments in addition to exhibiting enhanced resistance to water-whitening can be prepared using an aqueous latex emulsion prepared from a monomer mixture consisting essentially of;

[0006] a) at least one alkylacrylate having at least 4 carbon atoms in the alkyl chain,

[0007] b) at least one ethylenically unsaturated carboxylic acid or its corresponding anhydride,

[0008] c) at least one styrenic monomer.

[0009] The monomer mixtures are polymerized using single stage aqueous latex emulsion techniques. The polymerization is carried out in the presence of at least one anionic surfactant and a redox type free radical initiator system. The present invention further relates to methods of preparation of the pressure sensitive adhesives and laminates prepared using these pressure sensitive adhesives. When prepared using the disclosed monomer mixture, anionic surfactant and redox initiator system, the aqueous latex emulsion has polymer particles with an mean particle size diameter of less than or equal to about 100 nm. In addition, when prepared as described the measured particle size does not increase during the polymerization process at the expected rate, but rather maintains a relatively flat particle growth curve, while still yielding latex emulsions with relatively narrow particle size distributions. Typically, the particle size distribution exhibits a mean/median ratio of less than about 1.05.

[0010] Pressure sensitive adhesives of the present invention are useful in clear label applications, marking films, etc. When prepared according to the invention pressure sensitive adhesives maintain adhesion in hot water environments and are resistant to water-whitening for at least 12 hours and preferably for at least 24 hours.

[0011] FIG. 1is a graph comparing the measured particle growth in the aqueous latex emulsion of both lab and plantsize batches corresponding to Example 4 compared with the predicted particle size growth calculated using the initial measured particle diameter.

[0012] FIG. 2is a graph that plots the rheology of the aqueous latex emulsion of Example 3 with a pH of 7.3 when subjected to continuous ramped shear rates as measured on a Carri-Med rheometer.

[0013] Pressure sensitive adhesives that are sufficiently versatile to wet out and coat a variety of substrate (adherend) surfaces; provide adequate adhesive characteristics such as tack, peel adhesion and shear resistance; and maintain adhesion in hot water environments in addition to exhibiting enhanced resistance to water-whitening are based on aqueous latex emulsions prepared from monomer mixtures, consisting essentially of;

[0014] A) at least one alkyl acrylate having at least 4 carbon atoms in the alkyl group,

[0015] B) at least one ethylenically unsaturated carboxylic acid or its corresponding anhydride,

[0016] C) at least one styrenic monomer.

[0017] The polymerization is carried out in the presence of an anionic surfactant or mixture of anionic surfactants. A redox type free radical initiator system is used in an amount sufficient to promote free radical polymerization of the monomers. Once the polymerization is complete it may be desirable to adjust the pH of the latex emulsion in order to enhance its stability. Other ingredients commonly used in the preparation of aqueous latex emulsions such as buffering agents, chain transfer agents, and the like may be present. General latex technology is discussed in, Kirk-Othmer, Encyclopedia of Technology 4thEd., vol.15, p.51-65; which is hereby incorporated by reference. In addition to the aqueous latex emulsion, the pressure sensitive adhesive may also contain additional components such as, biocides, wetting agents, defoamers, tackifiers, etc.

[0018] The monomers used to prepare the aqueous lattices include alkyl acrylates, ethylenically unsaturated carboxylic acids and their corresponding anhydrides and styrenic monomers.

[0019] Alkyl acrylates are alkyl esters of acrylic or methacrylic acid having at least 4 carbon atoms in the alkyl portion of the molecule. Examples include butyl acrylate, isobutyl acrylate, heptyl acrylate, octyl acrylate, isooctyl acrylate, 2-ethylhexyl acrylate, and isodecyl acrylate. A single alkyl acrylate or mixtures of more than one alkyl acrylate can be used. A preferred alkyl acrylate is 2-ethylhexyl acrylate. The alkyl acrylate monomers are present in the monomer mixture in an amount from about 50 wt % to about 90 wt % and more preferably from about 60 wt % to about 65 wt % based on the total weight of the monomer mixture.

[0020] Examples of ethylenically unsaturated carboxylic acids and their corresponding anhydrides used in the present invention include acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, beta-carboxyethyl acrylate and maleic anhydride. A single ethylenically unsaturated carboxylic acid or its corresponding anhydride or mixtures thereof can be used. A preferred carboxylic acid is beta-carboxyethyl acrylate. The ethylenically unsaturated carboxylic acids or their corresponding anhydrides are present in the monomer mixture in amounts from about 5 wt % to about 10 wt %, more preferably from about 6 wt % to about 8 wt % based on the total weight of the monomer mixture.

[0021] Examples of styrenic monomers used in the present invention include styrene, t-butyl styrene, dimethyl styrene, and vinyl toluene. A preferred monomer is styrene. The styrenic monomers are present in the monomer mixture in amounts from about 20 wt % to about 40 wt %, more preferably from about 28 wt % to about 34 wt % based on the total weight of the monomer mixture.

[0022] Surfactants suitable for use in the present invention are anionic surfactants. Examples of anionic surfactants include ammonium salts of nonylphenol ethoxylated sulfates such as ABEX EP-110 (30% active) or ABEX EP-120; lauryl ether sulfates such as Disponil FES-32 or FES-993; sulfosuccinates such as Aerosol OT-75 or OT-501 and the like. A preferred anionic surfactant is ABEX EP-110. A single anionic surfactant or mixture of anionic surfactants can be used. Typically, less than 4 wt % of the anionic surfactant based on the total weight of the latex, is used.

[0023] A redox type free radical initiator system is used to promote polymerization of the monomers. The initiator is peroxide or hydroperoxide such as t-butyl hydroperoxide. The reducing agent used in the redox system is zinc formaldehyde sulfoxylate, sodium formaldehyde sulfoxylate, ascorbic acid, isoascorbic acid, sodium metabisulfite and the like. A preferred redox type system consists of t-butyl hydroperoxide and zinc formaldehyde sulfoxylate.

[0024] The aqueous latex emulsions which form the basis of the pressure sensitive adhesives of the present invention are prepared in a single stage synthesis with or without a seed in the reaction vessel prior to beginning the monomer feed. Reaction temperatures during the monomer feed can range from about 50 C. to about 90 C. In a preferred method of preparing the aqueous latex a pre-emulsion, an aqueous solution of the initiator, and an aqueous solution of a reducing agent are prepared in separate vessels. A reaction vessel is charged with deionized water, an anionic surfactant and a predetermined amount of initiator. The mixture in the reaction vessel is heated with stirring and up to 20 wt % of the pre-emulsion, more preferably up to 8 wt % and most preferably 4 wt % is added to the reaction vessel along with a predetermined amount of the reducing agent to form the seed. In small batches such as laboratory size synthesis the predetermined amount of reducing agent, the initial Zn hit, can be added before the initial pre-emulsion charge. In larger scale synthesis it is preferred that the predetermined amount of reducing agent is added after the initial pre-emulsion charge is added to the reaction vessel. After forming the seed, the contents of the reaction vessel are heated to a desired temperature and the pre-emulsion, initiator and the reducing agent are simultaneously metered into the reaction vessel with stirring. It has been found to be advantageous to mix the pre-emulsion and initiator. This can be accomplished by merging the preemulsion and initiator feed streams and passing the merged stream through a static mixer or by simply allowing the two feed streams to converge in a common feed line. On completion of the pre-emulsion feed, the contents of the reaction vessel are cooled and alternating predetermined amounts of the initiator and reducing agent are added to the reaction vessel with stirring. This alternating initiator/reducing agent addition is preferably performed at least once. Once the reaction is complete the pH may be adjusted. The pH of the aqueous latex emulsion is preferably adjusted to a pH of about 6 to about 9 and more preferably about 6 to about 7.5. For efficiency and economy an aqueous solution of ammonium hydroxide can be used to adjust the pH. Other bases that may be used include amines, imines, alkali metal and alkaline metal hydroxides, carbonates, etc.

[0025] In addition to the aqueous latex emulsion, the pressure sensitive adhesive composition advantageously contains biocides, wetting agents, defoamers, etc. Examples of suitable biocides include Kathon LX, commercially available as a 1.5% solution from Rohm & Haas and Metatin 910, commercially available from ACIMA. An example of a suitable wetting agent is Surfynol SE commercially available from Air Products, PLURONIC type polyols commercially available from BASF Corp, and the like. Examples of defoamers include Drewplus T-1201 and Drewplus 1-191 commercially available from Ashland Speciality Chemical Company and Rhodoline 6681, commercially available from Rhodia.

[0026] The pressure sensitive adhesives described above can be used to prepare articles such as tapes, labels, signs, marking films and the like. In a typical construction the pressure sensitive adhesive is coated or otherwise applied to a release liner such as a siliconized paper, dried and laminated to a facestock. Alternatively, the pressure sensitive adhesive is coated directly on a facestock. Examples of face stock include cellulosics, metal foils, polycarbonates, polyethylene, polypropylene, polyethylene terephthalate and vinyl films.

[0027] The pressure sensitive adhesives typically have a viscosity after adjusting the pH to between about 6 and about 8 of from about 1,000 to about 20,000 centipoise. The pressure sensitive adhesives exhibit a shear-thinning rheology such that it allows coating even on difficult to coat films. Conventional coating techniques can be used to apply the pressure sensitive adhesives. Such techniques include dipping, slot die, air knife, brush curtain, extrusion blade, reverse roll, squeeze roll coating and the like.

[0028] The following examples illustrate the invention and should not be construed as limiting in nature. In the examples particle sizes were determined using a COULTER LS particle size analyzer. Test procedures were as follows: