US 12,674,047 B2Grant

Upgraded polyethylene for jacketing

Issue Date:2026-07-07

•13 Claims

Abstract

Mixed-plastic-polyethylene composition having a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min; and a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³.

Metadata

Assignee

BOREALIS AG

Inventors

Yi Liu
Susanne Kahlen
Hermann Braun
Elisabeth Ribarits
Christian Goetzloff

Application Information

Application Number:US 17/997,962

Filing Date:2021-05-17

Priority Date:2020-05-20

Art Unit:1763

Classifications

IPC:

C08L23/0807C08F210/16C08J3/00

Field of Search:

C08L 23/0815C08L 2203/202C08L 2205/025C08L 2205/03C08L 2207/062C08L 2207/20C08F 210/16C08F 2/001C08F 2/14C08F 2/34C08F 4/6492C08J 3/005C08J 2323/08C08J 2423/08Y02W 30/62

Patent Drawings

This patent does not have any drawings.

Description

Field of the Invention

[0001] The present invention relates to upgrading of PE recycling streams using virgin high-density polyethylenes (HDPE) to give jacketing materials that have acceptable ESCR (Environmental Stress Crack Resistance) performance.

Background

[0002] Polyolefins, in particular polyethylene and polypropylene are increasingly consumed in large amounts in a wide range of applications, including packaging for food and other goods, fibres, automotive components, and a great variety of manufactured articles.

[0003] Polyethylene based materials are a particular problem as these materials are extensively used in packaging. Taking into account the huge amount of waste collected compared to the amount of waste recycled back into the stream, there is still a great potential for intelligent reuse of plastic waste streams and for mechanical recycling of plastic wastes.

[0004] Generally, recycled quantities of polypropylene on the market are mixtures of both polypropylene (PP) and polyethylene (PE), this is especially true for post-consumer waste streams. Moreover, commercial recyclates from post-consumer waste sources are conventionally cross contaminated with non-polyolefin materials, such as polyethylene terephthalate, polyamide, polystyrene or non-polymeric substances like wood, paper, glass or aluminium. These cross-contaminations drastically limit final applications or recycling streams such that no profitable final uses remain.

[0005] In addition, recycled polyolefin materials normally have properties, which are much worse than those of the virgin materials, unless the amount of recycled polyolefin added to the final compound is extremely low. For example, such materials often have limited impact strength and poor mechanical properties (such as e.g. brittleness) and thus, they do not fulfil customer requirements. For several applications, e.g. jacketing materials (for cables), containers, automotive components or household articles. This normally excludes the application of recycled materials for high quality parts, and means that they are only used in low-cost, non-demanding applications, such as e.g. in construction or in furniture. In order to improve the mechanical properties of these recycled materials, generally relatively large amounts of virgin materials (produced from oil) are added.

[0006] U.S. Pat. No. 8,981,007 B2 relates to non-crosslinked polyethylene compositions for use in the jacketing of power cables. Generally crosslinked polyethylene is used for power cables, due to its excellent heat resistance, chemical resistance and electrical properties. However, since crosslinked polyethylene resin is a thermoset resin, it is not recyclable. There is, therefore, a demand for an eco-friendly non-crosslinked type thermoplastic polyethylene resin, which is also heat resistant and hence suitable for use in power cables.

[0007] EP 2417194 B1 also relates to uncrosslinked polyethylene compositions for use in power cables. The compositions disclosed herein are polymer blends comprising MDPE and HDPE and one or more additive(s) selected from a flame retardant, an oxidation stabilizer, a UV stabilizer, a heat stabilizer and a process aid.

[0008] DE-102011108823-A1 relates to a composite for the electrical isolation of electrical cables. The composite comprises a plastic, a material having a heat conductivity of less than 1 W/(mk) and a displacement material (C). In certain embodiments, the displacement material can be a recycled material.

[0009] EP 1676283 B1 relates to medium/high voltage electrical energy transport or distribution cables comprising at least one transmissive element and at least one coating layer, said coating layer being made from a coating material comprising at least one recycled polyethylene (obtained from a waste material) with a density not higher than 0.940 g/cm³and at least a second polyethylene material having a density higher than 0.940 g/cm³. The coating material in some of the examples of EP 1676283 B1 showed improved values with respect to stress cracking resistance with respect to those obtained from recycled polyethylene alone. However, these values were considerably lower than those obtained with the virgin material.

[0010] A particular problem in recycled polyethylene materials is that variations in ESCR (Environmental Stress Crack Resistance) properties are unacceptable depending on the waste origin. ESCR can be evaluated with a number of parameters including the failure time of Bell test and strain hardening modulus, i.e., the slope of the strain hardening part of a stress—strain curve (Kurelec, L.; Teeuwen, M.; Schoffeleers, H.; Deblieck, R., Strain hardening modulus as a measure of environmental stress crack resistance of high density polyethylene. Polymer 2005, 46 (17), 6369-6379). Thus, there is need for addressing these limitations in a flexible way. For jacketing applications an ESCR Bell test failure time of >1000 hours is desirable.

[0011] In addition to that there is usually a problem with tensile strain at break (in %). Materials made from recycling streams usually suffer from very low tensile strain at break values, whereby the end-use applications are severely limited.

[0012] Thus, there remains a need in the art to provide recycled polyethylene solutions for jacketing materials that have acceptable and constant ESCR (Environmental Stress Crack Resistance) performance, with Bell test failure time >1000 hours, preferably >2000 hours with other properties, particularly tensile properties, especially tensile strain at break, as well as acceptable or even good strain hardening modulus which are similar to blends of virgin polyethylene and carbon black marketed for the purpose of cable jacketing.

Summary of the Invention

[0013] The present invention is based on the surprising finding that a good ESCR and strain hardening performance is obtained when various units in specific amounts are present.

[0014] The present invention provides a compositions with acceptable ESCR performance (Bell test failure time >1000 hours, preferably >2000 hours) and good strain hardening range, while maintaining other properties similar to blends of virgin polyethylene and carbon black marketed for the purpose of cable jacketing. The present invention is also concerned with the use of a specific virgin high-density polyethylene to improve ESCR, SH modulus and Charpy notched impact strength of blends of a mixed-plastic-polyethylene blend and a secondary blend of high-density polyethylene and carbon black.

[0015] The present invention provides a

- [0016] mixed-plastic-polyethylene composition comprising a mixed-plastic-polyethylene primary recycling blend (A), the mixed-plastic-polyethylene composition
  - [0017] having
    - [0018] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min;
    - [0019] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;
  - [0020] the mixed-plastic-polyethylene composition comprising
    - [0021] a total amount of ethylene units (C2 units) of from 92.0 to 97.0 wt.-%, and
    - [0022] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.5 to 6.65 wt.-%,
    - [0023] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
  - [0024] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0025] wherein the mixed-plastic-polyethylene composition comprises
  - [0026] one or more in any combination of, more preferably all of:
    - [0027] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
    - [0028] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
    - [0029] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
    - [0030] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0031] Further provided is a mixed-plastic-polyethylene composition

- [0032] obtainable by blending and extruding
- [0033] a. 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A) wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm; and wherein the mixed-plastic-polyethylene primary blend (A) has
  - [0034] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0035] a density of from 945 to 990 kg/m³,
  - [0036] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0037] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0038] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0039] b. 35.0 to 68.0 wt.-% of a secondary component (B) being a first virgin high-density polyethylene (HDPE1) optionally blended with carbon black, the secondary component (B) having
  - [0040] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0041] a density of from 940 to 970 kg/m³, preferably from 955 to 970 kg/m³,
  - [0042] a shear thinning index SHI_2.7/210of 15 to 30
  - [0043] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0044] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B), and
  - [0045] preferably a limonene content below 0.10 ppm,
- [0046] c. 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0047] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0048] a density from 945 to 965 kg/m³,
  - [0049] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0050] preferably a limonene content below 0.10 ppm.

[0051] The invention is further directed to an article, comprising the mixed-plastic-polyethylene composition of the present invention, preferably wherein the article is a cable jacket.

[0052] Also provided is a process for preparing the mixed-plastic-polyethylene composition of the invention, comprising the steps of:

- [0053] a. providing a mixed-plastic-polyethylene primary recycling blend (A) in an amount of 30.0 to 60.0 wt.-% based on the overall weight of the composition,
  - [0054] wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm and wherein the mixed-plastic-polyethylene primary blend has
  - [0055] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0056] a density of from 945 to 990 kg/m³,
  - [0057] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0058] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0059] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0060] b. providing a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, in an amount of 35.0 to 68.0 wt.-% based on the overall weight of the composition, the secondary component (B) having
  - [0061] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0062] a density of from 940 to 970 kg/m³, preferably from 955 to 970 kg/m³,
  - [0063] a shear thinning index SHI_2.7/210of 15 to 30
  - [0064] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0065] optionally a optional carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B); and
  - [0066] preferably a limonene content below 0.10 ppm,
- [0067] c. 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0068] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0069] a density from 945 to 965 kg/m³,
  - [0070] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR, Preferably a limonene content below 0.10 ppm.
- [0071] d. melting and mixing the blend of mixed-plastic-polyethylene primary blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) in an extruder, optionally a twin screw extruder, and
- [0072] e. optionally pelletizing the obtained mixed-plastic-polyethylene composition.

[0073] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention pertains. Although, any methods and materials similar or equivalent to those described herein can be used in practice for testing of the present invention, the preferred materials and methods are described herein. In describing and claiming the present invention, the following terminology will be used in accordance with the definitions set out below.

[0074] Unless clearly indicated otherwise, use of the terms “a,” “an,” and the like refers to one or more.

[0075] For the purposes of the present description and of the subsequent claims, the term “recycled waste” is used to indicate a material recovered from both post-consumer waste, as opposed to virgin polymers and/or materials. Post-consumer waste refers to objects having completed at least a first use cycle (or life cycle), i.e. having already served their first purpose.

[0076] The term “virgin” denotes the newly produced materials and/or objects prior to their first use, which have not already been recycled. The term “recycled material” such as used herein denotes materials reprocessed from “recycled waste”.

[0077] The term “natural” in the context of the present invention means that the components are of natural colour. This means that no pigments (including carbon black) are included in the components of the mixed-plastic-polyethylene composition of the present invention.

[0078] A blend denotes a mixture of two or more components, wherein one of the components is polymeric. In general, the blend can be prepared by mixing the two or more components. Suitable mixing procedures are known in the art. The secondary component (B) may be a blend comprising at least 90 wt.-% of a reactor made high-density polyethylene material, as well as carbon black. This high-density polyethylene material is a virgin material which has not already been recycled.

[0079] For the purposes of the present description and of the subsequent claims, the term “mixed-plastic-polyethylene” indicates a polymer material including predominantly units derived from ethylene apart from other polymeric ingredients of arbitrary nature. Such polymeric ingredients may for example originate from monomer units derived from alpha olefins such as propylene, butylene, octene, and the like, styrene derivatives such as vinylstyrene, substituted and unsubstituted acrylates, substituted and unsubstituted methacrylates.

[0080] Said polymeric materials can be identified in the mixed-plastic polyethylene composition by means of quantitative ¹³C{¹H} NMR measurements as described herein. In the quantitative ¹³C{¹H} NMR measurement used herein and described below in the measurement methods different units in the polymeric chain can be distinguished and quantified. These units are ethylene units (C2 units), units having 3, 4 and 6 carbons and units having 7 carbon atoms.

[0081] Thereby, the units having 3 carbon atoms (C3 units) can be distinguished in the NMR spectrum as isolated C3 units (isolated C3 units) and as continuous C3 units (continuous C3 units) which indicate that the polymeric material contains a propylene based polymer. These continuous C3 units can also be identified as iPP units. The continuous C3 units thereby can be distinctively attributed to the mixed-plastic-polyethylene primary recycling blend (A) as the secondary component (B) and the second virgin high-density polyethylene (C) in the mixed-plastic-polyethylene composition according to the present invention usually does not include any propylene based polymeric components.

[0082] The units having 3, 4, 6 and 7 carbon atoms describe units in the NMR spectrum which are derived from two carbon atoms in the main chain of the polymer and a short side chain or branch of 1 carbon atom (isolated C3 unit), 2 carbon atoms (C4 units), 4 carbon atoms (C6 units) or 5 carbon atoms (C7 units).

[0083] The units having 3, 4 and 6 carbon atoms (isolated C3, C4 and C6 units) can derive either from incorporated comonomers (propylene, 1-butene and 1-hexene comonomers) or from short chain branches formed by radical polymerization.

[0084] The units having 7 carbon atoms (C7 units) can be distinctively attributed LDPE contamination in recycling polyethylene streams. In LDPE resins the amount of C7 units is always in a distinct range. Thus, the amount of C7 units measured by quantitative ¹³C{¹H} NMR measurements can be used to calculate the amount of LDPE in a polyethylene composition.

[0085] Thus, the amounts of continuous C3 units, isolated C3 units, C4 units, C6 units and C7 units are measured by quantitative ¹³C{¹H} NMR measurements as described below, whereas the amount of LDPE is calculated from the amount of C7 units as described below.

[0086] The total amount of ethylene units (C2 units) is attributed to units in the polymer chain, which do not have short side chains of 1-5 carbon atoms, in addition to the units attributed to the LDPE (i.e. units which have longer side chains branches of 6 or more carbon atoms).

[0087] A mixed-plastic-polyethylene primary recycling blend (A) denotes the starting primary blend containing the mixed plastic-polyethylene as described above. Conventionally further components such as filers, including organic and inorganic fillers for example talc, chalk, carbon black, and further pigments such as TiO₂as well as paper and cellulose may be present. According to the present invention, the waste stream is a consumer waste stream, such a waste stream may originate from conventional collecting systems such as those implemented in the European Union. Post-consumer waste material is characterized by a limonene content of from 0.10 to 500 ppm (as determined using solid phase microextraction (HS-SPME-GC-MS) by standard addition).

[0088] Mixed-plastic-polyethylene primary blend(s) (A) as used herein are commercially available. Suitable blends include a number of recyclates available from Mtm plastics under the brand name Purpolen.

[0089] Within the meaning of this invention the term “jacketing materials” refers to materials used in cable jacketing/cable coating applications for electrical/telephone/telecommunications cables. These materials are required to show good ESCR properties, such as a Bell test failure time of >1000 hours.

[0090] If not indicated otherwise “%” refers to weight-%.

Detailed Description

Natural Mixed-Plastic-Polyethylene Primary Recycling Blend (A)

[0091] The mixed-plastic-polyethylene composition according to the present invention comprises a mixed-plastic-polyethylene primary recycling blend (A). It is the essence of the present invention that this primary recycling blend is obtained from a post-consumer waste stream.

[0092] According to the present invention the mixed-plastic-polyethylene primary recycling blend (A) is generally a blend, wherein at least 90.0 wt.-%, preferably at least 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend originates from post-consumer waste, such as from conventional collecting systems (curb-side collection), such as those implemented in the European Union.

[0093] Said post-consumer waste can be identified by its limonene content. It is preferred that the post-consumer waste has a limonene content of from 0.10 to 500 ppm.

[0094] The mixed-plastic-polyethylene primary recycling blend (A) preferably comprises a total amount of ethylene units (C2 units) of from 70.0 wt.-% to 95.0 wt.-%, more preferably of from 71.5 wt.-% to 92.0 wt.-%, still more preferably of from 73.0 wt.-% to 90.0 wt.-% and most preferably of from 74.0 wt.-% to 88.0 wt.-%.

[0095] The total amounts of C2 units are based on the total weight amount of monomer units in the mixed-plastic-polyethylene primary recycling blend (A) and are measured according to quantitative ¹³C{¹H} NMR measurement.

[0096] The mixed-plastic-polyethylene primary recycling blend (A) preferably further comprises a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 4.0 to 30.0 wt.-%, more preferably from 7.0 wt.-% to 28.0 wt.-%, still more preferably from 9.0 wt.-% to 26.5.0 wt.-% and most preferably from 11.0 wt.-% to 25.5 wt.-%.

[0097] In addition to C2 units and continuous C3 units the mixed-plastic-polyethylene primary recycling blend (A) can further comprise units having 3, 4, 6 or 7 or more carbon atoms so that the mixed-plastic-polyethylene primary recycling blend (A) overall can comprise ethylene units and a mix of units having 3, 4, 6 and 7 or more carbon atoms.

[0098] The mixed-plastic-polyethylene primary recycling blend (A) preferably comprises one or more in any combination, preferably all of:

- [0099] a total amount of units having 3 carbon atoms as isolated C3 units (isolated C3 units) of from 0.01 wt.-% to 0.50 wt.-%, more preferably from 0.05 wt.-% to 0.45 wt.-%, still more preferably from 0.10 wt.-% to 0.40 wt.-% and most preferably from 0.15 wt.-% to 0.35 wt.-%;
- [0100] a total amount of units having 4 carbon atoms (C4 units) of from 0.01 to 0.60 wt.-%, more preferably from 0.05 wt.-% to 0.50 wt.-%, still more preferably from 0.10 wt.-% to 0.45 wt.-% and most preferably from 0.20 wt.-% to 0.40 wt.-%;
- [0101] a total amount of units having 6 carbon atoms (C6 units) of from 0.01 to 1.00 wt.-%, more preferably from 0.05 wt.-% to 0.80 wt.-%, still more preferably from 0.10 wt.-% to 0.60 wt.-% and most preferably from 0.15 wt.-% to 0.50 wt.-%; and
- [0102] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.50 wt.-%, of from 0.00 wt.-% to 0.20 wt.-%, still more preferably of from 0.00 to 0.10 wt.-% yet more preferably of from 0.00 wt.-% to 0.05 wt.-%, most preferably there are is no measureable content of units having 7 carbon atoms (C7 units).

[0103] The total amounts of C2 units, continuous C3 units, isolated C3 units, C4 units, C6 units and C7 units thereby are based on the total weight amount of monomer units in the mixed-plastic-polyethylene primary recycling blend (A) and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0104] Preferably, the total amount of units, which can be attributed to comonomers (i.e. isolated C3 units, C4 units, C6 units and C7 units), in the mixed-plastic-polyethylene primary recycling blend (A) is from 0.10 wt.-% to 2.00 wt.-%, more preferably from 0.20 wt.-% to 1.70 wt.-%, still more preferably from 0.25 wt.-% to 1.40 wt.-% and most preferably from 0.30 wt.-% to 1.20 wt.-%, and is measured according to quantitative ¹³C{¹H} NMR measurement.

[0105] It is preferred that the mixed-plastic-polyethylene primary recycling blend (A) has

- [0106] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, more preferably from 0.5 to 1.0 g/10 min; and/or
- [0107] a density of from 945 to 990 kg/m³, more preferably from 948 to 987 kg/m³, most preferably from 950 to 985 kg/m³.

[0108] The mixed-plastic-polyethylene primary recycling blend (A) may also include:

- [0109] a) 0 to 10.0 wt.-% units derived from olefin(s) comprising functional groups,
- [0110] b) 0 to 3.0 wt.-% stabilizers,
- [0111] c) 0 to 3.0 wt.-% talc,
- [0112] d) 0 to 3.0 wt.-% chalk,
- [0113] e) 0 to 3.0 wt.-% TiO₂, and
- [0114] f) 0 to 6.0 wt.-% further components
  all percentages with respect to the mixed-plastic-polyethylene primary recycling blend (A).

[0115] The mixed-plastic-polyethylene primary recycling blend (A) preferably has one or more, more preferably all, of the following properties in any combination:

- [0116] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 2.0 to 6.0 g/10 min, more preferably from 3.0 to 5.0 g/10 min;
- [0117] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 50.0 to 120.0 g/10 min, more preferably from 70.0 to 100.0 g/10 min;
- [0118] a polydispersity index PI of from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹, yet more preferably from 1.7 to 2.1 s⁻¹;
- [0119] a shear thinning index SHI_2.7/210of from 30 to 60, more preferably 35 to 50, yet more preferably from 38 to 47;
- [0120] a complex viscosity at the frequency of 300 rad/s, eta₃₀₀, of from 450 to 700 Pa·s, more preferably from 500 to 650 Pa·s;
- [0121] a complex viscosity at the frequency of 0.05 rad/s, eta_0.05, of from 20000 to 40000 Pa·s, more preferably from 25000 to 35000 Pa·s;
- [0122] a xylene hot insoluble content, XHU, of from 0.01 to 1.0 wt.-%, more preferably from 0.1 to 0.5 wt.-%, and/or
- [0123] a limonene content of from 0.10 to 500 ppm.

[0124] Generally, recycled materials perform less well in functional tests such as the ESCR (Bell test failure time), SH modulus and Shore D tests than virgin materials or blends comprising virgin materials. Usually the ESCR (bell test failure time) of recycled polyethylenes is utterly devastating.

[0125] The mixed-plastic-polyethylene primary recycling blend (A) is preferably present in the composition of the present invention in an amount of from 30.0 to 60.0 wt.-%, more preferably 34.0 to 55.0 wt.-%, still more preferably from 37.0 to 52.0 wt.-%, and most preferably from 40.0 to 50.0 wt.-%, based on the overall weight of the composition.

Secondary Component (B)

[0126] The mixed-plastic-polyethylene composition of the invention comprises a secondary component (B) being a virgin high-density polyethylene (HDPE1) and optionally blended with carbon black (CB).

[0127] The secondary component (B) preferably has:

- [0128] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min; and/or
- [0129] a density of from 940 to 970 kg/m3, more preferably 955 to 970 kg/m³, yet more preferably from 959 to 967 kg/m³; and/or
- [0130] a polydispersity index from 1.6 to 2.2 s⁻¹, more preferably from 1.8 to 2.1 s⁻¹,
- [0131] a shear thinning index SHI_2.7/210of 15 to 30, more preferably 20 to 27,
- [0132] optionally a carbon black content of 1.5 to 3.0 wt.-%, with respect to the secondary component (B), more preferably of 1.8 to 2.8 wt.-%, and
- [0133] a limonene content below 0.10 ppm.

[0134] The secondary component (B) includes as polymeric component a copolymer of ethylene and one or more comonomer units selected from alpha-olefins having from 3 to 6 carbon atoms. It is preferred that the polymeric component is a copolymer of ethylene and 1-butene or a copolymer of ethylene and 1-hexene.

[0135] Apart from the polymeric component the secondary component (B) can further comprise additives in an amount of 10 wt.-% or below, more preferably 9 wt.-% or below, more preferably 7 wt.-% or below of the secondary component (B). Suitable additives are usual additives for utilization with polyolefins, such as stabilizers (e.g. antioxidant agents), metal scavengers and/or UV-stabilizers, antistatic agents and utilization agents (such as processing aid agents).

[0136] The secondary component (B) preferably has one or more, more preferably all of the following properties in any combination:

- [0137] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 1.0 to 5.0 g/10 min, more preferably from 1.3 to 3.0 g/10 min;
- [0138] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 20.0 to 50.0 g/10 min, more preferably from 25.0 to 40.0 g/10 min;
- [0139] a complex viscosity at the frequency of 300 rad/s, eta₃₀₀, of from 500 to 900 Pa·s, more preferably from 600 to 850 Pa·s;
- [0140] a complex viscosity at the frequency of 0.05 rad/s, eta_0.05, of from 15000 to 30000 Pa·s, more preferably from 17500 to 27500 Pa·s;
- [0141] a Shore D hardness, measured after 15 s according to ISO 868, Shore D 15 s, of from 50.0 to 70.0, more preferably of from 55.0 to 65.0,
- [0142] a Shore D hardness, measured after 1 s according to ISO 868, Shore D 1 s, of from 55.0 to 75.0, more preferably of from 58.0 to 70.0,
- [0143] a Shore D hardness, measured after 3 s according to ISO 868, Shore D 3 s, of from 55.0 to 75.0, more preferably of from 58.0 to 70.0,
- [0144] a strain hardening modulus, SH modulus, of from 20.0 to 35.0 MPa, more preferably from 22.5 to 32.5 MPa,
- [0145] a Charpy notched impact strength at 23° C., Charpy NIS 23° C., of from 8.0 to 20.0 kJ/m², more preferably from 10.0 to 17.5 kJ/m²,
- [0146] a Charpy notched impact strength at 0° C., Charpy NIS 0° C., of from 4.0 to 15.0 kJ/m², more preferably from 6.0 to 12.5 kJ/m²,
- [0147] a tensile stress at break of from 25 to 50 MPa, more preferably from 28 to 40 MPa,
- [0148] a tensile strain at break of from 700 to 1000%, more preferably from 800 to 950%,
- [0149] an environmental stress crack resistance, ESCR, of at least 2500 hours, more preferably at least 3000 hours.

[0150] Generally, recycled materials perform less well in functional tests such as the ESCR (Bell test failure time), SH modulus and Shore D tests than virgin materials or blends comprising virgin materials.

[0151] The secondary component (B) is preferably present in the composition of the present invention in an amount of from 35.0 to 68.0 wt.-%, more preferably 40.0 to 63.0 wt.-%, still more preferably from 42.0 to 59.0 wt.-%, and most preferably from 45.0 to 55.0 wt.-%, based on the overall weight of the composition.

[0152] The secondary component (B) preferably contains carbon black in and amount of 1.5 to 3.0 wt.-%, with respect to the secondary component (B), more preferably of 1.8 to 2.8 wt.-% and most preferably 2.0 to 2.8 wt.-%.

Second Virgin High-Density Polyethylene (C)

[0153] The mixed-plastic-polyethylene composition of the invention comprises a second virgin high-density polyethylene (C).

[0154] The second virgin high-density polyethylene (C) preferably has one or more, more preferably all of the following properties in any combination

- [0155] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
- [0156] a density from 945 to 965 kg/m³;
- [0157] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR;
- [0158] a limonene content below 0.10 ppm.

[0159] It is further preferred that the second virgin high-density polyethylene (C) has one or both of the following properties

- [0160] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 1.0 to 10.0 g/10 min, preferably from 3.0 to 8.0 g/10 min; and/or
- [0161] a polydispersity index (PI) of from 2.5 to 3.5 s⁻¹; and/or
- [0162] W_COPof from 0.5 to 5.0, more preferably from 0.5 to 2.0

[0163] The second virgin high-density polyethylene (C) preferably includes as polymeric component a copolymer of ethylene and one or more comonomer units selected from alpha-olefins having from 3 to 8 carbon atoms. It is preferred that the polymeric component is a copolymer of ethylene and 1-butene or a copolymer of ethylene and 1-hexene, most preferably a copolymer of ethylene and 1-hexene.

[0164] The second virgin high-density polyethylene (C) is preferably present in the composition of the present invention in an amount of from 2.0 to 20.0 wt.-%, more preferably 3.0 to 18.0 wt.-%, still more preferably 4.0 to 16.0 wt.-%, and most preferably from 5.0 to 15.0 wt.-%, based on the overall weight of the composition.

Mixed-Plastic-Polyethylene Composition

[0165] The present invention seeks to provide a mixed-plastic-polyethylene composition comprising a mixed-plastic-polyethylene primary recycling blend (A) with improved ESCR, impact strength and SH modulus compared to the mixed-plastic-polyethylene primary recycling blend (A), to levels which are suitable for jacketing applications.

[0166] The mixed-plastic-polyethylene composition as described herein is especially suitable for wire and cable applications, such as jacketing applications.

[0167] In a first aspect the present invention relates to a mixed-plastic-polyethylene composition comprising a mixed-plastic-polyethylene primary recycling blend (A), the mixed-plastic-polyethylene composition

- [0168] having
  - [0169] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min;
  - [0170] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;
- [0171] the mixed-plastic-polyethylene composition comprising
  - [0172] a total amount of ethylene units (C2 units) of from 92.0 to 97.0 wt.-%, and
  - [0173] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.5 to 6.65 wt.-%,
  - [0174] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
- [0175] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0176] wherein the mixed-plastic-polyethylene composition comprises
- [0177] one or more in any combination of, more preferably all of:
  - [0178] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0179] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0180] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
- [0181] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0182] In said aspect the mixed-plastic-polyethylene composition preferably comprises carbon black in an amount of 1.0 to 3.0 wt.-% with respect to the total of the mixed-plastic-polyethylene composition, more preferably of 1.3 to 2.5 wt.-%, most preferably 1.5 to 2.0 wt.-%.

[0183] In said aspect the mixed-plastic-polyethylene composition is preferably obtainable by blending and extruding

- [0184] a) 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A) wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm; and wherein the mixed-plastic-polyethylene primary blend (A) has
  - [0185] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0186] a density of from 945 to 990 kg/m³,
  - [0187] optionally a shear thinning index SHI_2.7/210of 30 to 60, more preferably 35 to 50
  - [0188] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0189] and a content of units derived from ethylene of 70 to 95 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0190] b) 35.0 to 68.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, the secondary component (B) having
  - [0191] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0192] a density of from 940 to 970 kg/m³, preferably 955 to 970 kg/m³,
  - [0193] a shear thinning index SHI_2.7/210of 15 to 30
  - [0194] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0195] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B), and
  - [0196] preferably a limonene content below 0.10 ppm,
- [0197] c) 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0198] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0199] a density from 945 to 965 kg/m³,
  - [0200] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0201] preferably a limonene content below 0.10 ppm.

[0202] The mixed-plastic-polyethylene composition preferably comprises

- [0203] a total amount of ethylene units (C2 units) of from 92.0 to 95.0 wt.-%, preferably from 92.0 to 93.0 wt.-%,
- [0204] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.50 to 6.65 wt.-%, more preferably from 4.0 wt.-% to 6.65 wt.-%, still more preferably from 5.0 wt.-% to 6.65 wt.-%,
- [0205] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
  - [0206] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0207] wherein the mixed-plastic-polyethylene composition comprises
- [0208] one or more in any combination of, more preferably all of:
  - [0209] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0210] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0211] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
- [0212] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0213] In a further preferred embodiment, the mixed-plastic-polyethylene composition comprises

- [0214] a total amount of ethylene units (C2 units) of from 91.0 to 94.0 wt.-%,
- [0215] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 5.0 to 6.65 wt.-%, and
- [0216] a total amount of units having 4 carbon atoms (C4 units) of from 1.10 wt.-% to 1.50 wt.-%.
- [0217] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0218] wherein the mixed-plastic-polyethylene composition comprises
- [0219] one or more in any combination of, more preferably all of:
  - [0220] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0221] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0222] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
  - [0223] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0224] Preferably, the total amounts of units, which can be attributed to comonomers other than C4 (i.e. isolated C3 units, C6 units and C7 units), in the mixed-plastic-polyethylene composition is from 0.00 wt.-% to 1.00 wt.-%, more preferably from 0.00 wt.-% to 0.70 wt.-%, still more preferably from 0.00 wt.-% to 0.50 wt.-%, and is measured according to quantitative ¹³C{¹H} NMR measurement.

[0225] The mixed-plastic polyethylene composition according to the present invention has a

- [0226] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min, preferably from 0.3 to 0.5 g/10 min;
- [0227] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;

[0228] The composition can have further components apart from the mixed-plastic-polyethylene primary recycling blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) such as further polymeric components or additives in amounts of not more than 15 wt.-%, based on the total weight of the composition.

[0229] Suitable additives are usual additives for utilization with polyolefins, such as stabilizers, (e.g. antioxidant agents), metal scavengers and/or UV stabilizers, antistatic agents, and utilization agents. The additives can be present in the composition in an amount of 10 wt.-% or below, more preferably 9 wt.-% or below, more preferably 7 wt.-% or below.

[0230] It is, however, preferred that the composition consists of the mixed-plastic-polyethylene primary recycling blend (A), the secondary component (B) and the second virgin high-density polyethylene (C).

[0231] The mixed-plastic-polyethylene composition according to the present invention is preferably obtainable by blending and extruding

- [0232] a) 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0233] b) 35.0 to 68.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0234] c) 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C).

[0235] In a preferable embodiment, the composition is obtainable by blending and extruding

- [0236] a) 34.0 to 55.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0237] b) 40.0 to 63.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0238] c) 3.0 to 18.0 wt.-% of a second virgin high-density polyethylene (C).

[0239] In a further preferable embodiment, the composition is obtainable by blending and extruding

- [0240] a) 37.0 to 52.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0241] b) 42.0 to 59.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0242] c) 4.0 to 16.0 wt.-% of a second virgin high-density polyethylene (C).

[0243] In a yet further preferable embodiment, the composition is obtainable by blending and extruding

- [0244] a) 40.0 to 50.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0245] b) 45.0 to 55.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0246] c) 5.0 to 15.0 wt.-% of a second virgin high-density polyethylene (C).

[0247] The mixed-plastic-polyethylene primary recycling blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) are generally defined as described above or below.

[0248] The mixed plastic polyethylene composition preferably has an impact strength at 23° C. (ISO 179-1 eA) of from 6.0 to 15.0 kJ/m², preferably from 6.0 to 10.0 kJ/m².

[0249] Further, the mixed plastic polyethylene composition preferably has an impact strength at 0° C. (according to ISO 179-1 eA) of from 4.0 to 10.0 kJ/m², more preferably from 4.0 to 8.0 kJ/m².

[0250] The mixed-plastic-polyethylene composition preferably has a strain hardening modulus (SH modulus) of from 15.0 to 25.0 MPa, more preferably from 17.0 to 23.0 MPa and most preferably from 18.0 to 22.0 MPa.

[0251] It is preferred that that the mixed-plastic-polyethylene composition preferably has

- [0252] a Shore D hardness, measured according to ISO 868 with a measuring time of 1 s, Shore D 1 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0, and/or
- [0253] a Shore D hardness, measured according to ISO 868 with a measuring time of 3 s, Shore D 3 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0, and/or
- [0254] a Shore D hardness, measured according to ISO 868 with a measuring time of 15 s, Shore D 15 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0.

[0255] The mixed-plastic-polyethylene composition preferably has one or more, preferably all of the following rheological properties, in any combination:

- [0256] a shear thinning index SHI_2.7/210of from 35.0 to 50.0, more preferably from 37 to 45 and/or
- [0257] a complex viscosity at 0.05 rad/s, eta_0.05, of from 29000 to 45000 Pa·s, more preferably from 33000 to 42000 Pa·s, and/or
- [0258] a complex viscosity at 300 rad/s, eta₃₀₀, of from 650 to 850 Pa·s, more preferably from 700 to 800 Pa·s, and/or
- [0259] a polydispersity index PI of from 2.2 to 3.0 s⁻¹, more preferably from 2.4 to 2.8 s⁻¹.

[0260] Further, the mixed-plastic-polyethylene composition preferably has one or more, preferably all of the following melt flow rate properties, in any combination:

- [0261] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.3 to 0.5 g/10 min, and/or
- [0262] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 1.2 to 2.0 g/10 min, and/or
- [0263] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 30.0 to 50.0 g/10 min.

[0264] Still further, the mixed-plastic-polyethylene composition preferably has a tensile modulus in the range from 1050 to 1400 MPa, more preferably in the range from 1060 to 1300 MPa, most preferably in the range from 1070 to 1200 MPa.

[0265] Further, the mixed-plastic-polyethylene composition preferably has a tear resistance of from 15.0 to 30.0 N/mm, more preferably of from 17.5 to 27.5 N/mm and most preferably of from 20.0 to 25.0 N/mm. The tear resistance of the mixed-plastic-polyethylene composition is measured on a compression moulded plaque made from the composition having a thickness of 1 mm thickness.

[0266] It is further preferred that the mixed-plastic-polyethylene composition has a pressure deformation of not more than 15%, more preferably not more than 10%. The lower limit is usually at least 3%, preferably at least 4%.

[0267] Still further, the mixed-plastic-polyethylene composition has a water content of preferably not more than 500 ppm more preferably not more than 400 ppm. The lower limit is usually at least 100 ppm.

[0268] The mixed-plastic-polyethylene composition preferably also has an ESCR (Bell test failure time of at least 2000 hours, preferably at least 2500 hours, most preferably at least 3000 hours.

Article

[0269] The present application is further directed to an article comprising the mixed-plastic-polyethylene composition as described above.

[0270] In a preferred embodiment, the article is used in jacketing applications i.e. for a cable jacket. Preferably, the article is a cable comprising at least one layer which comprises the mixed-plastic-polyethylene composition as described above.

[0271] Preferably, the cable comprising a layer such as a jacketing layer, which comprises the the mixed-plastic-polyethylene composition as described above, has a cable shrinkage of not more than 2.0%, more preferably not more than 1.5%. The lower limit is usually at least 0.3%, preferably at least 0.5%.

[0272] All preferred aspects and embodiments as described above shall also hold for the article.

Process

[0273] The present invention also relates to a process for preparing the mixed-plastic-polyethylene composition as defined above or below. The process according to the present invention results in an improvement in the mechanical properties of the mixed-plastic-polyethylene primary recycling blend (A).

[0274] The process according to the present invention comprises the steps of:

- [0275] a. providing a mixed-plastic-polyethylene primary recycling blend (A) in an amount of 30.0 to 60.0 wt.-% based on the overall weight of the composition,
  - [0276] wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm and wherein the mixed-plastic-polyethylene primary blend has
  - [0277] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0278] a density of from 945 to 990 kg/m³,
  - [0279] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0280] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0281] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0282] b. providing a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, in an amount of 35.0 to 68.0 wt.-% based on the overall weight of the composition, the secondary component (B) having
  - [0283] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min,
  - [0284] a density of from 940 to 970 kg/m³, preferably 955 to 970 kg/m³,
  - [0285] a shear thinning index SHI_2.7/210of 15 to 30,
  - [0286] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0287] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B); and
  - [0288] preferably, a limonene content below 0.10 ppm.
- [0289] c. providing a second virgin high-density polyethylene (C) in an amount of 2.0 to 20.0 wt.-%, based on the overall weight of the composition, the second virgin high-density polyethylene having
  - [0290] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0291] a density from 945 to 965 kg/m³,
  - [0292] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0293] preferably a limonene content below 0.10 ppm
- [0294] d. melting and mixing the blend of mixed-plastic-polyethylene primary blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) in an extruder, optionally a twin screw extruder, and
- [0295] e. optionally pelletizing the obtained mixed-plastic-polyethylene composition.

[0296] All preferred aspects, definitions and embodiments as described above shall also hold for the process.

Experimental Part

1. Test Methods

[0297] a) Melt Flow Rate

[0298] Melt flow rates were measured with a load of 2.16 kg (MFR₂), 5.0 kg (MFR_S) or 21.6 kg (MFR₂₁) at 190° C. as indicated. The melt flow rate is that quantity of polymer in grams which the test apparatus standardized to ISO 1133 extrudes within 10 minutes at a temperature of or 190° C. under a load of 2.16 kg, 5.0 kg or 21.6 kg.

[0299] b) Density

[0300] Density is measured according to ISO 1183-187. Sample preparation is done by compression moulding in accordance with ISO 17855-2.

[0301] c) Comonomer Content

[0302] Quantification of C6 in the Reactor-Made Virgin High-Density Polyethylene (PE3)

[0303] Quantitative nuclear-magnetic resonance (NMR) spectroscopy was used to quantify the comonomer content of the polymer.

[0304] Quantitative ¹³C{¹H} NMR spectra recorded in the molten-state using a Bruker Avance III 500 NMR spectrometer operating at 500.13 and 125.76 MHz for ¹H and ¹³C respectively. All spectra were recorded using a ¹³C optimised 7 mm magic-angle spinning (MAS) probehead at 150° C. using nitrogen gas for all pneumatics. Approximately 200 mg of material was packed into a 7 mm outer diameter zirconia MAS rotor and spun at 4 kHz. This setup was chosen primarily for the high sensitivity needed for rapid identification and accurate quantification {klimke06, parkinson07, castignolles09}. Standard single-pulse excitation was employed utilising the NOE at short recycle delays of 3 s {pollard04, klimke06} and the RS-HEPT decoupling scheme {fillip05, griffin07}. A total of 1024 (1 k) transients were acquired per spectra.

[0305] Quantitative ¹³C{¹H} NMR spectra were processed, integrated and relevant quantitative properties determined from the integrals. All chemical shifts are internally referenced to the bulk methylene signal (δ) at 30.00 ppm {randall89}.

[0306] Characteristic signals corresponding to the incorporation of 1-hexene were observed {randall89}. The amount of isolated 1-hexene incorporated in EEHEE sequences was quantified using the integral of the *B4 sites (I_*B4) at 38.3 ppm accounting for the number of reporting sites per comonomer:
H=I_*B4.

[0307] Characteristic signals resulting from saturated end-groups were observed. The content of such saturated end-groups was quantified using the average of the integral of the signals at 22.8 ppm and 32.2 ppm assigned to the 2 s (I_2S) and 3 s (I_3S) sites respectively:
S=(½)*(I_2S+I_3S)

[0308] The amount of ethylene was quantified using the integral of the bulk methylene (I_δ) sites at 30.00 ppm. This integral included the γ site as well as the 3B4 sites from 1-hexene.

[0309] The total ethylene content was calculated based on the bulk integral and compensating for the observed 1-hexene sequence and end-group:
E=(I_□/2)+(3*H/2)−(H/2)+(3*S/2)
The total mole fraction of 1-hexene in the polymer was then calculated as:
fH=H/(E+H)

[0310] The mole percent comonomer incorporation was calculated from the mole fraction:
H[mol %]=100*fH
The weight percent comonomer incorporation was calculated from the mole fraction:
H[wt %]=100*(fH*84.16)/((fH*84.16)+((1−fH)*28.05))
randall89

[0311] J. Randall, Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, C29, 201.
klimke06
[0312] Klimke, K., Parkinson, M., Piel, C., Kaminsky, W., Spiess, H. W., Wilhelm, M., Macromol. Chem. Phys. 2006; 207:382.
parkinson07
[0313] Parkinson, M., Klimke, K., Spiess, H. W., Wilhelm, M., Macromol. Chem. Phys. 2007; 208:2128.
pollard04
[0314] Pollard, M., Klimke, K., Graf, R., Spiess, H. W., Wilhelm, M., Sperber, O., Piel, C., Kaminsky, W., Macromolecules 2004; 37:813.
filip05
[0315] Filip, X., Tripon, C., Filip, C., J. Mag. Resn. 2005, 176, 239
griffin07
[0316] Griffin, J. M., Tripon, C., Samoson, A., Filip, C., and Brown, S. P., Mag. Res. in Chem. 2007 45, S1, S198
castignolles09
[0317] Castignolles, P., Graf, R., Parkinson, M., Wilhelm, M., Gaborieau, M., Polymer 50 (2009) 2373
Quantification of C2, iPP (Continuous C3), LDPE and Polyethylene Short Chain Branches in the Commercially Prepared Polethylenes

[0318] Quantitative ¹³C{¹H} NMR spectra were recorded in the solution-state using a Bruker Avancelll 400 MHz NMR spectrometer operating at 400.15 and 100.62 MHz for ¹H and ¹³C respectively. All spectra were recorded using a ¹³C optimised 10 mm extended temperature probehead at 125° C. using nitrogen gas for all pneumatics. Approximately 200 mg of material was dissolved in 3 ml of 1,2-tetrachloroethane-d₂(TCE-d₂) along with chromium-(111)-acetylacetonate (Cr(acac)₃) resulting in a 65 mM solution of relaxation agent in solvent {singh09}. To ensure a homogenous solution, after initial sample preparation in a heat block, the NMR tube was further heated in a rotatory oven for at least 1 hour. Upon insertion into the magnet the tube was spun at 10 Hz. This setup was chosen primarily for the high resolution and quantitatively needed for accurate ethylene content quantification. Standard single-pulse excitation was employed without NOE, using an optimised tip angle, 1 s recycle delay and a bi-level WALTZ16 decoupling scheme {zhou07, busico07}. A total of 6144 (6 k) transients were acquired per spectra.

[0319] Quantitative ¹³C{¹H} NMR spectra were processed, integrated and relevant quantitative properties determined from the integrals using proprietary computer programs. All chemical shifts were indirectly referenced to the central methylene group of the ethylene block (EEE) at 30.00 ppm using the chemical shift of the solvent. Characteristic signals corresponding to polyethylene with different short chain branches (B1, B2, B4, B5, B6plus) and polypropylene were observed {randall89, brandolini00}.

[0320] Characteristic signals corresponding to the presence of polyethylene containing isolated B1 branches (starB1 33.3 ppm), isolated B2 branches (starB2 39.8 ppm), isolated B4 branches (twoB4 23.4 ppm), isolated B5 branches (threeB5 32.8 ppm), all branches longer than 4 carbons (starB4plus 38.3 ppm) and the third carbon from a saturated aliphatic chain end (3 s 32.2 ppm) were observed. The intensity of the combined ethylene backbone methine carbons (ddg) containing the polyethylene backbone carbons (dd 30.0 ppm), γ-carbons (g 29.6 ppm) the 4 s and the threeB4 carbon (to be compensated for later on) is taken between 30.9 ppm and 29.3 ppm excluding the Tββ from polypropylene. The amount of C2 related carbons was quantified using all mentioned signals according to the following equation:
fC_C2total=(Iddg−ItwoB4)+(IstarB1*6)+(IstarB2*7)+(ItwoB4*9)+I(threeB5*10)+((IstarB4plus−ItwoB4−IthreeB5)*7)+(I3s*3)

[0321] Characteristic signals corresponding to the presence of polypropylene (iPP, continuous C3)) were observed at 46.7 ppm, 29.0 ppm and 22.0 ppm. The amount of PP related carbons was quantified using the integral of Sαα at 46.6 ppm:
fC_PP=Isαα*3

[0322] The weight percent of the C2 fraction and the polypropylene can be quantified according following equations:
wt_C2fraction=fC_C2total*100/(fC_C2total+fC_PP)
wt_PP=fC_PP*100/(fC_C2total+fC_PP)

[0323] Characteristic signals corresponding to various short chain branches were observed and their weight percentages quantified as the related branch would be an alpha-olefin, starting by quantifying the weight fraction of each:
fwtC2=fC_C2total−((IstarB1*3)−(IstarB2*4)−(ItwoB4*6)−(IthreeB5*7)
fwtC3(isolated C3)=IstarB1*3
fwtC4=IstarB2*4
fwtC6=ItwoB4*6
fwtC7=IthreeB5*7

[0324] Normalisation of all weight fractions leads to the amount of weight percent for all related branches:
fsum_{wt.-% total}=fwtC2+fwtC3+fwtC4+fwtC6+fwtC7+fC_PP
wtC2total=fwtC2*100/fsum_{wt.-% total}
wtC3total=fwtC3*100/fsum_{wt.-% total}
wtC4total=fwtC4*100/fsum_{wt.-% total}
wtC6total=fwtC6*100/fsum_{wt.-% total}
wtC7total=fwtC7*100/fsum_{wt.-% total}

[0325] The content of LDPE can be estimated assuming the B5 branch, which only arises from ethylene being polymerised under high pressure process, being almost constant in LDPE. We found the average amount of B5 if quantified as C7 at 1.46 wt.-%. With this assumption it is possible to estimate the LDPE content within certain ranges (approximately between 20 wt.-% and 80 wt.-%), which are depending on the SNR ratio of the threeB5 signal:
wt.-% LDPE=wtC7total*100/1.46

References

[0326] zhou07 Zhou, Z., Kuemmerle, R., Qiu, X., Redwine, D., Cong, R., Taha, A., Baugh, D. Winniford, B., J. Mag. Reson. 187 (2007) 225
[0327] busico07 Busico, V., Carbonniere, P., Cipullo, R., Pellecchia, R., Severn, J., Talarico, G., Macromol. Rapid Commun. 2007, 28, 1128
[0328] singh09 Singh, G., Kothari, A., Gupta, V., Polymer Testing 28 5 (2009), 475
[0329] randall89 J. Randall, Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, C29, 201.
[0330] brandolini00 A. J. Brandolini, D. D. Hills, NMR Spectra of Polymers and Polymer Additives, Marcel Dekker Inc., 2000

[0331] d) Impact Strength

[0332] The impact strength is determined as Charpy Notched Impact Strength according to ISO 179-1 eA at +23° C. and at 0° C. on compression moulded specimens of 80×10×4 mm prepared according to ISO 17855-2.

[0333] e) Tensile Testing of 5A Specimen

[0334] For tensile testing, dog bone specimens of 5A are prepared according to ISO 527-2/5A by die cutting from compression moulded plaques of 2 mm′ thickness. If ageing is needed, the 5A specimens are kept at 110° C. in a cell oven for 14 days (336 hours). All specimens are conditioned for at least 16 hours at 23° C. and 50% relative humidity before testing. Tensile properties are measured according to ISO 527-1/2 at 23° C. and 50% relative humidity with Alwetron R24, 1 kN load cell. Tensile testing speed is 50 mm/min, grip distance is 50 mm and gauge length is 20 mm.

[0335] f) Rheological Measurements

[0336] Dynamic Shear Measurements (Frequency Sweep Measurements)

[0337] The characterisation of melt of polymer composition or polymer as given above or below in the context by dynamic shear measurements complies with ISO standards 6721-1 and 6721-10. The measurements were performed on an Anton Paar MCR501 stress controlled rotational rheometer, equipped with a 25 mm parallel plate geometry. Measurements were undertaken on compression moulded plates, using nitrogen atmosphere and setting a strain within the linear viscoelastic regime. The oscillatory shear tests were done at 190° C. applying a frequency range between 0.01 and 600 rad/s and setting a gap of 1.3 mm.

[0338] In a dynamic shear experiment the probe is subjected to a homogeneous deformation at a sinusoidal varying shear strain or shear stress (strain and stress controlled mode, respectively). On a controlled strain experiment, the probe is subjected to a sinusoidal strain that can be expressed by
γ(t)=γ₀sin(cot) (1)

[0339] If the applied strain is within the linear viscoelastic regime, the resulting sinusoidal stress response can be given by
σ(t)=σ₀sin(ωt+δ) (2)

[0340] where

[0341] σ₀and γ₀are the stress and strain amplitudes, respectively

[0342] ω is the angular frequency

[0343] δ is the phase shift (loss angle between applied strain and stress response)

[0344] t is the time

[0345] Dynamic test results are typically expressed by means of several different rheological functions, namely the shear storage modulus G′, the shear loss modulus, G″, the complex shear modulus, G*, the complex shear viscosity, η*, the dynamic shear viscosity, η′, the out-of-phase component of the complex shear viscosity η″ and the loss tangent, tan δ which can be expressed as follows:

[0346]

\begin{matrix} G^{'} = \frac{σ_{0}}{γ_{0}} \cos δ [Pa] & (3) \end{matrix}

\begin{matrix} G^{″} = \frac{σ_{0}}{γ_{0}} \sin δ [Pa] & (4) \end{matrix}

\begin{matrix} G^{*} = G^{'} + {iG}^{″} [Pa] & (5) \end{matrix}

\begin{matrix} η^{*} = η^{'} - i η^{″} [Pa . s] & (6) \end{matrix}

\begin{matrix} η^{'} = \frac{G^{″}}{ω} [Pa . s] & (7) \end{matrix}

\begin{matrix} η^{″} = \frac{G^{'}}{ω} [Pa . s] & (8) \end{matrix}

[0347] The determination of so-called Shear Thinning Index, which correlates with MWD and is independent of Mw, is done as described in equation 9.

[0348]

\begin{matrix} {SHI}_{(x / y)} = \frac{{Eta}^{*} for (G^{*} = x kPa)}{{Eta}^{*} for (G^{*} = y kPa)} & (9) \end{matrix}

[0349] For example, the SHI_2.7/210is defined by the value of the complex viscosity, in Pa s, determined for a value of G* equal to 2.7 kPa, divided by the value of the complex viscosity, in Pa s, determined for a value of G* equal to 210 kPa.

[0350] The values of storage modulus (G′), loss modulus (G″), complex modulus (G*) and complex viscosity (η*) were obtained as a function of frequency (ω).

[0351] Thereby, e.g. η*_300rad/s(eta*_300rad/s) is used as abbreviation for the complex viscosity at the frequency of 300 rad/s and η*_0.05rad/s(eta*_0.05rad/s) is used as abbreviation for the complex viscosity at the frequency of 0.05 rad/s.

[0352] The loss tangent tan (delta) is defined as the ratio of the loss modulus (G″) and the storage modulus (G′) at a given frequency. Thereby, e.g. tan_0.05is used as abbreviation for the ratio of the loss modulus (G″) and the storage modulus (G′) at 0.05 rad/s and tan₃₀₀used as abbreviation for the ratio of the loss modulus (G″) and the storage modulus (G′) at 300 rad/s.

[0353] The elasticity balance tan_0.05/tan₃₀₀is defined as the ratio of the loss tangent tan_0.05and the loss tangent tan₃₀₀.

[0354] Besides the above mentioned rheological functions one can also determine other rheological parameters such as the so-called elasticity index EI(x). The elasticity index EI(x) is the value of the storage modulus (G′) determined for a value of the loss modulus (G″) of x kPa and can be described by equation 10.
EI(x)=G′ for (G″=x kPa) [Pa] (10)
For example, the EI(5 kPa) is the defined by the value of the storage modulus (G′), determined for a value of G″ equal to 5 kPa.

[0355] The polydispersity index, PI, is defined by equation 11.

[0356]

\begin{matrix} PI = \frac{10^{5}}{G^{'} (ω_{COP})}, ω_{COP} = ω for (G^{'} = G^{″}) & (11) \end{matrix}

where ω_COPis the cross-over angular frequency, determined as the angular frequency for which the storage modulus, G′, equals the loss modulus, G″.

[0357] The values are determined by means of a single point interpolation procedure, as defined by Rheoplus software. In situations for which a given G* value is not experimentally reached, the value is determined by means of an extrapolation, using the same procedure as before. In both cases (interpolation or extrapolation), the option from Rheoplus “Interpolate y-values to x-values from parameter” and the “logarithmic interpolation type” were applied.

References

[0358] [1] Rheological characterization of polyethylene fractions” Heino, E. L., Lehtinen, A., Tanner J., Seppälä, J., Neste Oy, Porvoo, Finland, Theor. Appl. Rheol., Proc. Int. Congr. Rheol, 11th (1992), 1, 360-362
[0359] [2] The influence of molecular structure on some rheological properties of polyethylene”, Heino, E. L., Borealis Polymers Oy, Porvoo, Finland, Annual Transactions of the Nordic Rheology Society, 1995).
[0360] [3] Definition of terms relating to the non-ultimate mechanical properties of polymers, Pure & Appl. Chem., Vol. 70, No. 3, pp. 701-754, 1998.

[0361] g) ESCR (Bell Test, h)

[0362] By the term ESCR (environmental stress cracking resistance) is meant the resistance of the polymer to crack formation under the action of mechanical stress and a reagent in the form of a surfactant. The ESCR is determined in accordance with IEC 60811-406, method B. The reagent employed is 10 weight % Igepal CO 630 in water. The materials were prepared according to instructions for HDPE as follows: The materials were pressed at 165° C. to a thickness of 1.75-2.00 mm. The notch was 0.30-0.40 mm deep.

[0363] h) Shore D Hardness

[0364] Two different Shore D hardness measurements were conducted:

[0365] Firstly, Shore D hardness is determined according to ISO 868 on moulded specimen with a thickness of 4 mm. The shore hardness is determined after 1 sec, 3 sec or 15 sec after the pressure foot is in firm contact with the test specimen. The sample is compression moulded according to ISO 17855-2 and milled into specimens of 80×10×4 mm.

[0366] Secondly, Shore D hardness is determined according to ASTM D2240-03. The same samples as for the Shore D hardness according to ISO 868 were used.

[0367] i) Strain Hardening (SH) Modulus

[0368] The strain hardening test is a modified tensile test performed at 80° C. on a specially prepared thin sample. The Strain Hardening Modulus (MPa), <Gp>, is calculated from True Strain-True Stress curves; by using the slope of the curve in the region of True Strain, λ, is between 8 and 12.

[0369] The true strain, λ, is calculated from the length, I (mm), and the gauge length, I0 (mm), as shown by Equation 1.

[0370]

\begin{matrix} λ = \frac{l}{l_{0}} = 1 + \frac{Δ l}{l_{0}} & (1) \end{matrix}

where ΔI is the increase in the specimen length between the gauge marks, (mm). The true stress, σtrue (MPa), is calculated according to formula 2, assuming conservation of volume between the gauge marks:
σ_true=σ_nλ (2)
where σn is the engineering stress.

[0371] The Neo-Hookean constitutive model (Equation 3) is used to fit the true strain-true stress data from which <Gp> (MPa) for 8<λ<12 is calculated.

[0372]

\begin{matrix} σ_{true} = \frac{〈 Gp 〉}{20} (λ^{2} - \frac{1}{λ}) + C & (3) \end{matrix}

where C is a mathematical parameter of the constitutive model describing the yield stress extrapolated to λ=0.

[0373] Initially five specimens are measured. If the variation coefficient of <Gp> is greater than 2.5%, then two extra specimens are measured. In case straining of the test bar takes place in the clamps the test result is discarded.

[0374] The PE granules of materials were compression molded in sheets of 0.30 mm thickness according to the press parameters as provided in ISO 17855-2.

[0375] After compression molding of the sheets, the sheets were annealed to remove any orientation or thermal history and maintain isotropic sheets. Annealing of the sheets was performed for 1 h in an oven at a temperature of (120±2) ° C. followed by slowly cooling down to room temperature by switching off the temperature chamber. During this operation free movement of the sheets was allowed.

[0376] Next, the test pieces were punched from the pressed sheets. The specimen geometry of the modified ISO 37:1994 Type 3 (FIG. 3) was used.

[0377] The sample has a large clamping area to prevent grip slip, dimensions given in Table 1.

[0378]

TABLE 1

Dimensions of Modified ISO 37:1994 Type 3
Dimension		Size (mm)

L	start length between clamps	30.0 +/− 0.5
I0	Gauge length	12.5 +/− 0.1
I1	Prismatic length	16.0 +/− 1.0
I3	Total length	70
R1	Radius	10.0 +/− 0.03
R2	Radius	8.06 +/− 0.03
b1	Prismatic width	4.0 +/− 0.01
b2	Clamp width	20.0 +/− 1.0
h	Thickness	0.30 + 0.05/0.30 − 0.03

[0379] The punching procedure is carried out in such a way that no deformation, crazes or other irregularities are present in the test pieces.

[0380] The thickness of the samples was measured at three points of the parallel area of the specimen; the lowest measured value of the thickness of these measurements was used for data treatment.

- [0381] 1. The following procedure is performed on a universal tensile testing machine having controlled temperature chamber and non-contact extensometer:
- [0382] 2. Condition the test specimens for at least 30 min in the temperature chamber at a temperature of (80±1) ° C. prior to starting the test.
- [0383] 3. Clamp the test piece on the upper side.
- [0384] 4. Close the temperature chamber.
- [0385] 5. Close the lower clamp after reaching the temperature of (80±1) ° C.
- [0386] 6. Equilibrate the sample for 1 min between the clamps, before the load is applied and measurement starts.
- [0387] 7. Add a pre-load of 0.5 N at a speed of 5 mm/min.
- [0388] 8. Extend the test specimen along its major axis at a constant traverse speed (20 mm/min) until the sample breaks.
- [0389] During the test, the load sustained by the specimen is measured with a load cell of 200 N. The elongation is measured with a non-contact extensometer.

[0390] j) Water Content

[0391] The water content was determined as described in IS015512:2019 Method A—Extraction with anhydrous methanol. There the test portion is extracted with anhydrous methanol and the extracted water is determined by a coulometric Karl Fischer Titrator.

[0392] k) Cable Extrusion

[0393] The cable extrusion is done on a Nokia-Maillefer cable line. The extruder has five temperature zones with temperatures of 170/175/180/190/190° C. and the extruder head has three zones with temperatures of 210/210/210° C. The extruder screw is a barrier screw of the design Elise. The die is a semi-tube on type with 5.9 mm diameter and the outer diameter of the cable is 5 mm. The compound is extruded on a 3 mm in diameter, solid aluminum conductor to investigate the extrusion properties. Line speed is 75 m/min. The pressure at the screen and the current consumption of the extruder is recorded for each material.

[0394] I) Pressure Deformation

[0395] Pressure test is conducted according to EN 60811-508. An extruded cable sample is placed in an air oven at a 115° C. and subjected to a constant load applied by means of a special indentation device (with a rectangular indentation 0.7 mm wide knife) for 6 hours. The percentage of indentation is measured afterwards using a digital gauge.

[0396] m) Cable Shrinkage

[0397] The shrinkage of the composition is determined with the cable samples obtained from the cable extrusion. The cables are conditioned in the constant room at least 24 hours before the cutting of the samples. The conditions in the constant room are 23±2° C. and 50±5% humidity. Samples are cut to 400 mm at least 2 m away from the cable ends. They are further conditioned in the constant room for 24 hours after which they are place in an oven on a talcum bed at 100° C. for 24 hours. After removal of the sample from the oven they are allowed to cool down to room temperature and then measured. The shrinkage is calculated according to formula below:
[(L_Before−L_After)/L_Before]×100%, wherein L is length.

[0398] n) Tear Resistance

[0399] Tear resistance is measured on compression moulded plaques of 1 mm thickness according to BS 6469 section 99.1. A test piece with a cut is used to measure the tear force by means of a tensile testing machine. The tear resistance is calculated by dividing the maximum force needed to tear the specimen by its thickness.

[0400] o) Amount of Limonene

[0401] This method allows nature of a raw mixed-plastic-polyethylene primary recycling blend to be determined.

[0402] Limonene quantification was carried out using solid phase microextraction (HS-SPME-GC-MS) by standard addition.

[0403] 20 mg cryomilled samples were weighed into 20 mL headspace vials and after the addition of limonene in different concentrations and a glass-coated magnetic stir bar, the vial was closed with a magnetic cap lined with silicone/PTFE. Micro capillaries (10 pL) were used to add diluted limonene standards of known concentrations to the sample. Limonene was added to the samples to obtain concentration levels of 1 ppm, 2 ppm, 3 ppm and 4 ppm limonene. For quantification, ion-93 acquired in SIM mode was used. Enrichment of the volatile fraction was carried out by headspace solid phase microextraction with a 2 cm stable flex 50/30 pm DVB/Carboxen/PDMS fibre at 60° C. for 20 minutes. Desorption was carried out directly in the heated injection port of a GCMS system at 270° C.

[0404] GCMS Parameters:

[0405] Column: 30 m HP 5 MS 0.25*0.25

[0406] Injector: Splitless with 0.75 mm SPME Liner, 270° C.

[0407] Temperature program: −10° C. (1 min)

[0408] MS: Single quadrupole, direct interface, 280° C. interface temperature

[0409] Acquisition: SIM scan mode

[0410] Scan parameter: 20-300 amu

[0411] SIM Parameter: m/Z 93, 100 ms dwell time

[0412] 2. Materials

[0413] PE1 is HE6062, a black bimodal high-density polyethylene jacketing compound for energy and communication cables (available from Borealis AG).

[0414] PE2 is BorSafe™ HE3490-LS-H, a black bimodal high-density polyethylene (available from Borealis AG).

[0415] PE3 is a reactor made bimodal high-density polyethylene, synthesised as described in section 2.1 and according to the parameters given in Table 1.

[0416] Purpolen PE is a mixed-plastic-polyethylene primary recycling blend available from MTM plastics. Many different samples, differing as to density and also rheology, can be used.

[0417] The properties of the Purpolen PE batch used in the present study, as well as PE2 and PE3 can be found in Table 2

[0418] 2.1. Synthesis of the Virgin High-Density Polyethylene

[0419] a) Preparation of the Solid Ziegler-Natta Catalyst Component

[0420] The solid Ziegler-Natta catalyst component based on an MgCl₂*3EtOH carrier was analogously prepared according to WO 2017/207493 with the exception that the resultant catalyst particle size was as follows: d₁₀=2.7 μm, d₅₀=9.5 μm, d₉₀=24.3 μm. The catalyst particle size can be obtained e.g. by sieving the carrier or catalyst in a suitable manner.

[0421] b) Offline Pre-Polymerization of the Solid Ziegler-Natta Catalyst Component

[0422] Diluted Ziegler-Natta catalyst oil slurry (37.37 kg containing 4.9 wt.-% of the solid Ziegler-Natta catalyst component as described above) was added to the reactor at 20° C. followed by 33 wt.-% solution of TEAL in heptane (0.87 kg; Al/Ti=1.0 mol/mol). Off-line pre-polymerization was initiated almost immediately after TEAL addition (stirring time−5 min) by continuous addition of propylene at 20-25° C. A target pre-polymerization degree was set equal to 2 g polymer/g_catand the desired degree of pre-polymerization was reached after 5 h 10 min. The pressure was released and the reactor was flushed five times with nitrogen and then dried under vacuum for 1 h. Dried off-line pre-polymerized Ziegler-Natta catalyst in oil was taken out into a catalyst drum. The yield was 42.97 kg containing 13.9 wt.-% of off-line pre-polymerized Ziegler-Natta catalyst with pre-polymerization degree of 2 polymer g/g_cat. The off-line pre-polymerized Ziegler-Natta catalyst had a particle size distribution in the range of d₁₀=5-18 μm, d₅₀=12-35 μm and d₉₀=26-50 μm.

[0423] c) Multi-Stage Polymerization of the Virgin High-Density Polyethylene (PE3)

[0424] A loop reactor having a volume of 50 dm³was operated at 60° C. and 57 bar pressure. For producing a first polymer fraction 52 kg/h of propane, 4 kg/h of ethylene and 10 g/h of hydrogen were introduced into the reactor having a volume of 50 dm³. In addition, the pre-polymerized solid Ziegler-Natta catalyst component prepared according to the description above was introduced into the reactor at a rate of 10.84 g/h, along with cocatalyst TEAL with a Al/Ti ratio of 15. The conditions in the reactor are shown in Table 1.

[0425] The polymer slurry was withdrawn from the loop reactor and transferred into a loop reactor having a volume of 150 dm³. This second loop reactor was operated at 95° C. and 54 bar pressure. Into the reactor were introduced ethylene and hydrogen so that the ratio of hydrogen to ethylene (H2/C2) in the reactor was 499 mol/kmol. No additional catalyst feed or comonomer feed was introduced into the reactor. The conditions in the reactor are shown in Table 1.

[0426] The polymer slurry was withdrawn from the second loop reactor and transferred into a further loop reactor having a volume of 350 dm³. This third loop reactor was operated at 95° C. and 53 bar pressure. Into the reactor were introduced ethylene and hydrogen so that the ratio of hydrogen to ethylene (H2/C2) in the reactor was 323 mol/kmol No additional catalyst feed was introduced into the reactor. The conditions in the reactor are shown in Table 2.

[0427] The polymer slurry was withdrawn from the third loop reactor and transferred into a flash vessel operated at 3 bar pressure and 40-60° C. temperature where the hydrocarbons were substantially removed from the polymer. The polymer was then introduced into a gas phase reactor operated at a temperature of 85° C. and a pressure of 20 bar. In addition, ethylene and 1-hexene were introduced into the reactor so that the ratio of hydrogen to ethylene (H2/C2) in the reactor was 14.9 mol/kmol and the ratio of 1-hexene to ethylene (C6/C2) in the reactor was 113.3 mol/kmol. The conditions are shown in Table 1.

[0428] The resulting polymer was purged with nitrogen (about 50 kg/h) for one hour, stabilised with 2200 ppm of Irganox B225 and 1500 ppm Ca-stearate and then extruded together with 5.75 wt % carbon black masterbatch that leads to 2.3 wt % carbon black in the final polymer composition to pellets in a counter-rotating twin screw extruder CIM90P (manufactured by Japan Steel Works) so that the throughput was 83 kg/h and the screw speed was 223 rpm.

[0429]

TABLE 1

Polymerization conditions for PE3
		PE3

	1^stLoop reactor (R1)
	Temperature (° C.)	60
	Catalyst feed (g/h)	10.84
	Al/Ti ratio	15
	C2 feed (kg/h)	4
	H2 feed (g/h)	10
	Split (wt.-%)	1.3
	2^ndLoop reactor (R2)
	Temperature (° C.)	95
	H2/C2 ratio (mol/kmol)	499
	C2 conc. (mol %)	2.38
	MFR₂(g/10 min)	50
	Split (wt.-%)	15.1
	3^rdLoop reactor (R3)
	Temperature (° C.)	95
	H2/C2 ratio (mol/kmol)	323
	C2 conc. (mol %)	3.69
	MFR₂(g/10 min)	80
	Split (wt.-%)	33.6
	Gas Phase Reactor (R4)
	Temperature (° C.)	85
	H2/C2 ratio (mol/kmol)	14.9
	C6/C2 ratio (mol/kmol)	113.3
	C2 conc. (mol %)	18.1
	Split (wt.-%)	50.0

[0430]

TABLE 2

PE properties
	Purpolen PE	PE2	PE3

C2 content (wt.-%)	87.42	98.14	97.0
Isolated C3 content (wt.-%)	0.17	0*	n.m.
C4 content (wt.-%)	0.39	0*	n.m.
C6 content (wt.-%)	0.48	1.86	3.0
C7 content (wt.-%)	0*	0*	n.m.
Continuous C3 content	11.53	0*	n.m.
(wt.-%)
Limonene content (ppm)	6	n.m.	n.m.
MFR₂(g/10 min)	0.80	n.m.	n.m.
MFR₅(g/10 min)	3.55	0.25	0.16
MFR₂₁(g/10 min)	n.m.	9.7	4.9
Density (kg/m³)	983	960	954
W_COP	67.5	0.75	0.73
PI	1.7	3.62	2.77
SHI_2.7/210	40.3	n.m.	n.m.
eta_0.05(Pa · s)	27600	167000	215500
eta₃₀₀(Pa · s)	560	1070	1370
XHU (wt.-%)	0.27	n.m.	n.m.
Water content (%)	262	n.m.	n.m.

*0 means lower than the limit of quantification.
n.m.: not measured

[0431] 3. Experiments

[0432] Compositions were prepared via melt blending on a co-rotating twin screw extruder (ZSK) according to the recipes given in Table 3. The polymer melt mixture was discharged and pelletized. Table 3 further shows the content of these compositions, as measured by quantitative ¹³C{¹H} NMR measurements. The mechanical properties of the compositions are given in Table 4.

[0433]

TABLE 3

Composition of Comparative and Inventive Examples
	CE1	CE2	CE3	IE1	IE2

PE1 (wt.-%)	50	50	50	50	50
PE2 (wt.-%)	—	5	10	—	—
PE3 (wt.-%)	—	—	—	5	10
Purpolen PE1 (wt.-%)	50	45	40	45	40
CB content (wt.-%)	1.29	1.47	1.64	1.52	1.64
C2 content (wt.-%)	91.8	92.0	93.2	92.3	92.3
Isolated C3 content	0*	0*	0*	0*	0*
(wt.-%)
C4 content (wt.-%)	1.3	1.3	1.2	1.1	1.5
C6 content (wt.-%)	0*	0*	0*	0*	0.4
C7 content (wt.-%)	0*	0*	0*	0*	0*
Continuous C3 content	6.9	6.7	5.6	6.6	5.8
(wt.-%)

*0 means lower than the limit of quantification.

[0434]

TABLE 4

Mechanical properties of Comparative and Inventive Examples
	CE1	CE2	CE3	IE1	IE2

MFR₂(g/10 min)	0.51	0.47	0.38	0.44	0.37
MFR₅(g/10 min)	2.34	1.94	1.70	1.93	1.60
MFR₂₁(g/10 min)	48.2	47.1	41.5	45.1	36.0
Density (kg/m³)	966	966	965	964	963
Impact strength,	4.69	5.37	6.62	6.10	8.55
23° C., (kJ/m²)
Impact strength,	4.06	4.35	4.22	4.43	4.65
0° C., (kJ/m²)
W_COP	22.6	16.4	12.5	15.8	11.2
PI (s⁻¹)	2.3	2.4	2.6	2.4	2.7
SHI_2.7/210	35.7	38.1	41.8	38.8	41.7
eta_0.05(Pa · s)	28300	32900	36900	34300	39400
eta₃₀₀(Pa · s)	670	710	730	720	760
Bell ESCR (h)	840	1632	>4000	>4000	>4000
Cable shrinkage (%)	1.08	1.12	1.22	1.09	1.26
Pressure deformation (%)	5	6	7	8	6
SH modulus (MPa)	16.2	17.3	19.3	18.2	21.1
Shore D 15 s (ISO 868)	61.1	61.2	61.4	61.2	60.8
Shore D 3 s (ISO 868)	63.4	63.3	63.3	63.1	63.2
Shore D 1 s (ISO)	64.5	64.7	64.9	64.7	64.4
Tensile Modulus (MPa)	1090	1100	1094	1081	1072
Tear resistance (N/mm)	22.8	22.8	23.1	22.6	23.2
Water content (%)	179	299	289	375	238

[0435] As can be seen from Table 4, the addition of PE3 to blends of PE1 with Purpolen PE has the effect of increasing the Charpy notched impact strength and ECSR (evaluated with Bell test and/or SH modulus) as is acceptable for cabling applications. By comparing IE1 with CE2 and IE2 with CE3, it is clear that the use of PE3 is superior to using PE2, with a greater effect on the ESCR, Charpy Notched Impact Strength and SH modulus observed. Through using such specific virgin high-density polyethylenes in small amounts, compositions can be obtained that have high levels of recycled content without unduly impacting the mechanical properties, as would otherwise be the case (see CE1 for example).

Claims

The invention claimed is:

1. A mixed-plastic-polyethylene composition comprising a mixed-plastic-polyethylene primary recycling blend (A), the mixed-plastic-polyethylene composition having:

a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min;

a density of from 956 to 965 kg/m³;

the mixed-plastic-polyethylene composition comprising:

a total amount of ethylene units (C2 units) of from 92.0 to 97.0 wt. %, and

a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.5 to 6.65 wt. %,

a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt. % to 2.20 wt. %;

with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C {¹H} NMR measurement and

wherein the mixed-plastic-polyethylene composition comprises one or more in any combination of:

a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt. % to 0.15 wt. %;

a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt. % to 0.50 wt. %;

a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt. % to 0.20 wt. %;

wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C {¹H} NMR measurement, wherein the mixed-plastic-polyethylene composition is obtained by blending and extruding

a) 30.0 to 60.0 wt. % of a mixed-plastic-polyethylene primary recycling blend (A)

wherein at least 90.0 wt. % of the mixed-plastic-polyethylene primary recycling blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm; and wherein the mixed-plastic-polyethylene primary recycling blend (A) has

a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min.,

a density of from 945 to 990 kg/m³,

optionally a shear thinning index SHI_2.7/210of 30 to 60,

optionally a polydispersity index from 1.2 to 2.5 s⁻¹, as obtained from rheological measurement,

and a content of units derived from ethylene of 70.0 to 95.0 wt. % as determined by quantitative ¹³C {¹H}-NMR,

b) 35.0 to 68.0 wt. % of a secondary component (B) being a first virgin high-density polyethylene (HDPE1) optionally blended with carbon black, the secondary component (B) having

a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min;

a density of from 940 to 970 kg/m³,

a shear thinning index SHI_2.7/210of 15 to 30,

a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,

optionally a carbon black content of 1.5 to 3.0 wt. % with respect to the secondary component (B), and

optionally a limonene content below 0.10 ppm,

c) 2.0 to 20.0 wt. % of a second virgin high-density polyethylene (C) having

a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of 0.05 to 0.5 g/10 min;

a density from 945 to 965 kg/m³,

a comonomer content in the range from 2.50 to 3.50 wt. %, as determined by quantitative ¹³C {¹H}-NMR, and

optionally a limonene content below 0.10 ppm.

2. The mixed-plastic-polyethylene composition of claim 1, comprising carbon black in an amount of 1.0 to 3.0 wt. % with respect to the total of the mixed-plastic-polyethylene composition.

3. The mixed-plastic-polyethylene composition according to claim 1, wherein the mixed-plastic-polyethylene primary recycling blend (A) has

an ESCR (Bell test failure time) of less than 1000 hours; and

optionally includes TiO₂in an amount of up to 3.0 wt. % with respect to mixed-plastic-polyethylene primary recycling blend (A).

4. The mixed-plastic-polyethylene composition according to claim 1, wherein the secondary component (B) has:

an ESCR (Bell test failure time) of at least 2500 hours.

5. The mixed-plastic-polyethylene composition according to claim 1, wherein the second virgin high-density polyethylene (C) has:

a melt flow rate (ISO 1133, 21 kg, 190° C.) of from 1.0 to 10.0 g/10 min; and/or

a polydispersity index (PI) of from 2.5 to 3.5 s⁻¹.

6. The mixed-plastic-polyethylene composition according to claim 1, wherein the composition has:

an ESCR (Bell test failure time) of at least 2000 hours.

7. The mixed-plastic-polyethylene composition according to claim 1, wherein:

the impact strength at 23° C. (according to ISO 179-1 eA) is from 6.0 to 15 KJ/m²and/or

wherein the impact strength at 0° C. (according to ISO 179-1 eA) is from 4.0 to 10.0 KJ/m².

8. The mixed-plastic-polyethylene composition according to claim 1, wherein the strain hardening modulus (SH modulus) is from 17.0 to 25.0 MPa.

9. The mixed-plastic-polyethylene composition according to claim 1, having:

a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.3 to 0.5 g/10 min, and/or

a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 1.2 to 2.0 g/10 min, and/or

a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 30.0 to 50.0 g/10 min.

10. The mixed-plastic-polyethylene composition according to claim 1, wherein the SHI_2.7/210is between 35.0 and 50.0.

11. The mixed-plastic-polyethylene composition according to claim 1, wherein the composition is a compression moulded plaque made from the composition having a thickness of 1 mm has a tear resistance of at least 22.0 N/mm and optionally up to 30.0 N/mm.

12. A process for preparing the mixed-plastic-polyethylene composition according to claim 11, comprising the steps of:

a) providing a mixed-plastic-polyethylene primary recycling blend (A) in an amount of 30.0 to 60.0 wt. % based on the overall weight of the composition,

wherein 90.0 wt. % of the mixed-plastic-polyethylene primary recycling blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm and wherein the mixed-plastic-polyethylene primary recycling blend (A) has

a melt flow rate (ISO 1133, 2.16 kg, 190°° C.) of from 0.1 to 1.5 g/10 min,

a density of from 945 to 990 kg/m³,

optionally a shear thinning index SHI_2.7/210of 30 to 60,

optionally a polydispersity index from 1.2 to 2.5 s⁻¹as obtained from rheological measurement,

and a content of units derived from ethylene of 70.0 to 95.0 wt. % as determined by quantitative ¹³C {¹H}-NMR,

b) providing a secondary component (B) being a first virgin high-density polyethylene (HDPE1) optionally blended with carbon black, in an amount of 35.0 to 68.0 wt. % based on the overall weight of the composition, the secondary component (B) having

a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min;

a density of from 940 to 970 kg/m³,

a shear thinning index SHI_2.7/210of 15 to 30,

a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement, and

optionally, a carbon black content of 1.5 to 3.0 wt. % with respect to the secondary component (B); and

c) providing a second virgin high-density polyethylene (C) in an amount of 2.0 to 20.0 wt. %, based on the overall weight of the composition, the second virgin high-density polyethylene having:

a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;

a density from 945 to 965 kg/m³,

a comonomer content in the range from 2.50 to 3.50 wt. %, as determined by quantitative ¹³C {¹H}-NMR, and

a limonene content below 0.10 ppm

d) melting and mixing a blend of mixed-plastic-polyethylene primary recycling blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) in an extruder, optionally a twin screw extruder, and

e) optionally pelletizing the obtained mixed-plastic-polyethylene composition.

13. An article, comprising the mixed-plastic-polyethylene composition according to claim 1, wherein the article is a cable jacket.

Patent Citations (6)

Patent	Date	Inventor	Cited By
US7867588(B2)	2011-01-01	Harris et al.	Applicant
US8981007(B2)	2015-03-01	Lee et al.	Applicant
US2003/0139530(A1)	2003-07-01	Starita	Applicant
DE102011108823(A1)	2001-08-01		Applicant
EP1676283(B1)	2006-07-01		Applicant
EP2917194(B1)	2015-09-01		Applicant

Non-Patent Literature (16)

Castignolles, et al., “Detection and quantification of branching in polyacrylates by size-exclusion chromatography (SEC) and melt-state 13C NMR spectroscopy” Polymer 5, 2009, 2373-2383.Applicant
Gurmeet Singh, et al., “Triad sequence determination of ethylene-propylene copolymers—application of quantitative 13C NMR” Polymer Testing 28 (2009) 475-479.Applicant
John M. Griffin, “Low-load rotor-synchronised Hahn-echo pulse train (RS-HEPT) 1H decoupling in solid-state NMR: factors affecting MAS spin-echo dephasing times”, Magnetic Reson. Chem. 2007; 45: S198-S208.Applicant
Katja Klimke, et al. “Optimisation and Application of Polyolefin Branch Quantification by Melt-State 13C NMR Spectroscopy” Macromol. Chem. Phys. 2006, 207, 382-395.Applicant
M. Pollard, et al. “Observation of Chain Branching in Polyethylene in the Solid State and Melt via 13C NMR Spectroscopy and Melt NMR Relaxation Time Measurements” Macromolecules 2004, 37, 813-825.Applicant
Matthew Parkinson, et al. “Effect of Branch Length on 13C NMR Relaxation Properties in Molten Poly[ethyleneco-(a-olefin)] Model Systems” Macromol. Chem Phys. 2007, 208, 2128-2133.Applicant
Xenia Filip, et al., “Heteronuclear decoupling under fast MAS by a rotor-synchronized Hahn-echo pulse train” Journal of Magentic Resonance 176, 2005, 239-243.Applicant
Zhe Zhou, et al., “A new decoupling method for accurate quantification of polyethylene copolymer composition and triad sequence distribution with 13C NMR” Journal of Magnetic Resonance 187 (2007) 225-233.Applicant
Anita J. Brandolini, NMR Spectra of Polymers and Polymer Additives, Marcel Dekker, Inc. New York, 2000 pp. 1-660.Applicant
Vincenzo Busico, et al., Alk-1-ene Polymerization in the Presence of a Monocyclopentadienyl Zirconium(IV) Acetamidinate Catalyst: Microstructural and Mechanistic Insightsa, Macromol. Rapid Commun. 2007, 28, 1128-1134.Applicant
Definition of terms relating to the non-ultimate mechanical properties—Pure & Appl. Chem. vol. 70, pp. 701-754, 1998.Applicant
E-L. Heino, et al., “Rheological Characterization of Polyethylene Fractions” Theoretical and Applied Rheology, Aug. 17-21, 1992, pp. 360-362.Applicant
Eeav-Leena Heino, “The Influence of molecular structure on some rheological properties of polyethylene” Annual transactions of the Nordic Rheology Society, vol. 3, 1995.Applicant
J. Randall, Macromol. Chem Phys. 1989, C29, 201_NPL.Applicant
L. Kurelec, et al., Strain hardening modulus as a measure of environmental stress crack resistance of high density polyethylene, Polymer 46 (2005) 6369-6379.Applicant
Indian Application No. 202217070083, Office Action dated Oct. 29, 2025.Applicant

Abstract

Mixed-plastic-polyethylene composition having a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min; and a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³.

Description

Field of the Invention

Background

Summary of the Invention

[0013] The present invention is based on the surprising finding that a good ESCR and strain hardening performance is obtained when various units in specific amounts are present.

[0015] The present invention provides a

- [0016] mixed-plastic-polyethylene composition comprising a mixed-plastic-polyethylene primary recycling blend (A), the mixed-plastic-polyethylene composition
  - [0017] having
    - [0018] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min;
    - [0019] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;
  - [0020] the mixed-plastic-polyethylene composition comprising
    - [0021] a total amount of ethylene units (C2 units) of from 92.0 to 97.0 wt.-%, and
    - [0022] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.5 to 6.65 wt.-%,
    - [0023] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
  - [0024] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0025] wherein the mixed-plastic-polyethylene composition comprises
  - [0026] one or more in any combination of, more preferably all of:
    - [0027] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
    - [0028] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
    - [0029] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
    - [0030] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0031] Further provided is a mixed-plastic-polyethylene composition

- [0032] obtainable by blending and extruding
- [0033] a. 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A) wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm; and wherein the mixed-plastic-polyethylene primary blend (A) has
  - [0034] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0035] a density of from 945 to 990 kg/m³,
  - [0036] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0037] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0038] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0039] b. 35.0 to 68.0 wt.-% of a secondary component (B) being a first virgin high-density polyethylene (HDPE1) optionally blended with carbon black, the secondary component (B) having
  - [0040] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0041] a density of from 940 to 970 kg/m³, preferably from 955 to 970 kg/m³,
  - [0042] a shear thinning index SHI_2.7/210of 15 to 30
  - [0043] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0044] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B), and
  - [0045] preferably a limonene content below 0.10 ppm,
- [0046] c. 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0047] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0048] a density from 945 to 965 kg/m³,
  - [0049] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0050] preferably a limonene content below 0.10 ppm.

[0051] The invention is further directed to an article, comprising the mixed-plastic-polyethylene composition of the present invention, preferably wherein the article is a cable jacket.

[0052] Also provided is a process for preparing the mixed-plastic-polyethylene composition of the invention, comprising the steps of:

- [0053] a. providing a mixed-plastic-polyethylene primary recycling blend (A) in an amount of 30.0 to 60.0 wt.-% based on the overall weight of the composition,
  - [0054] wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm and wherein the mixed-plastic-polyethylene primary blend has
  - [0055] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0056] a density of from 945 to 990 kg/m³,
  - [0057] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0058] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0059] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0060] b. providing a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, in an amount of 35.0 to 68.0 wt.-% based on the overall weight of the composition, the secondary component (B) having
  - [0061] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0062] a density of from 940 to 970 kg/m³, preferably from 955 to 970 kg/m³,
  - [0063] a shear thinning index SHI_2.7/210of 15 to 30
  - [0064] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0065] optionally a optional carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B); and
  - [0066] preferably a limonene content below 0.10 ppm,
- [0067] c. 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0068] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0069] a density from 945 to 965 kg/m³,
  - [0070] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR, Preferably a limonene content below 0.10 ppm.
- [0071] d. melting and mixing the blend of mixed-plastic-polyethylene primary blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) in an extruder, optionally a twin screw extruder, and
- [0072] e. optionally pelletizing the obtained mixed-plastic-polyethylene composition.

[0074] Unless clearly indicated otherwise, use of the terms “a,” “an,” and the like refers to one or more.

[0090] If not indicated otherwise “%” refers to weight-%.

Detailed Description

Natural Mixed-Plastic-Polyethylene Primary Recycling Blend (A)

[0093] Said post-consumer waste can be identified by its limonene content. It is preferred that the post-consumer waste has a limonene content of from 0.10 to 500 ppm.

[0098] The mixed-plastic-polyethylene primary recycling blend (A) preferably comprises one or more in any combination, preferably all of:

- [0099] a total amount of units having 3 carbon atoms as isolated C3 units (isolated C3 units) of from 0.01 wt.-% to 0.50 wt.-%, more preferably from 0.05 wt.-% to 0.45 wt.-%, still more preferably from 0.10 wt.-% to 0.40 wt.-% and most preferably from 0.15 wt.-% to 0.35 wt.-%;
- [0100] a total amount of units having 4 carbon atoms (C4 units) of from 0.01 to 0.60 wt.-%, more preferably from 0.05 wt.-% to 0.50 wt.-%, still more preferably from 0.10 wt.-% to 0.45 wt.-% and most preferably from 0.20 wt.-% to 0.40 wt.-%;
- [0101] a total amount of units having 6 carbon atoms (C6 units) of from 0.01 to 1.00 wt.-%, more preferably from 0.05 wt.-% to 0.80 wt.-%, still more preferably from 0.10 wt.-% to 0.60 wt.-% and most preferably from 0.15 wt.-% to 0.50 wt.-%; and
- [0102] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.50 wt.-%, of from 0.00 wt.-% to 0.20 wt.-%, still more preferably of from 0.00 to 0.10 wt.-% yet more preferably of from 0.00 wt.-% to 0.05 wt.-%, most preferably there are is no measureable content of units having 7 carbon atoms (C7 units).

[0105] It is preferred that the mixed-plastic-polyethylene primary recycling blend (A) has

- [0106] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, more preferably from 0.5 to 1.0 g/10 min; and/or
- [0107] a density of from 945 to 990 kg/m³, more preferably from 948 to 987 kg/m³, most preferably from 950 to 985 kg/m³.

[0108] The mixed-plastic-polyethylene primary recycling blend (A) may also include:

- [0109] a) 0 to 10.0 wt.-% units derived from olefin(s) comprising functional groups,
- [0110] b) 0 to 3.0 wt.-% stabilizers,
- [0111] c) 0 to 3.0 wt.-% talc,
- [0112] d) 0 to 3.0 wt.-% chalk,
- [0113] e) 0 to 3.0 wt.-% TiO₂, and
- [0114] f) 0 to 6.0 wt.-% further components
  all percentages with respect to the mixed-plastic-polyethylene primary recycling blend (A).

[0115] The mixed-plastic-polyethylene primary recycling blend (A) preferably has one or more, more preferably all, of the following properties in any combination:

- [0116] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 2.0 to 6.0 g/10 min, more preferably from 3.0 to 5.0 g/10 min;
- [0117] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 50.0 to 120.0 g/10 min, more preferably from 70.0 to 100.0 g/10 min;
- [0118] a polydispersity index PI of from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹, yet more preferably from 1.7 to 2.1 s⁻¹;
- [0119] a shear thinning index SHI_2.7/210of from 30 to 60, more preferably 35 to 50, yet more preferably from 38 to 47;
- [0120] a complex viscosity at the frequency of 300 rad/s, eta₃₀₀, of from 450 to 700 Pa·s, more preferably from 500 to 650 Pa·s;
- [0121] a complex viscosity at the frequency of 0.05 rad/s, eta_0.05, of from 20000 to 40000 Pa·s, more preferably from 25000 to 35000 Pa·s;
- [0122] a xylene hot insoluble content, XHU, of from 0.01 to 1.0 wt.-%, more preferably from 0.1 to 0.5 wt.-%, and/or
- [0123] a limonene content of from 0.10 to 500 ppm.

Secondary Component (B)

[0126] The mixed-plastic-polyethylene composition of the invention comprises a secondary component (B) being a virgin high-density polyethylene (HDPE1) and optionally blended with carbon black (CB).

[0127] The secondary component (B) preferably has:

- [0128] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min; and/or
- [0129] a density of from 940 to 970 kg/m3, more preferably 955 to 970 kg/m³, yet more preferably from 959 to 967 kg/m³; and/or
- [0130] a polydispersity index from 1.6 to 2.2 s⁻¹, more preferably from 1.8 to 2.1 s⁻¹,
- [0131] a shear thinning index SHI_2.7/210of 15 to 30, more preferably 20 to 27,
- [0132] optionally a carbon black content of 1.5 to 3.0 wt.-%, with respect to the secondary component (B), more preferably of 1.8 to 2.8 wt.-%, and
- [0133] a limonene content below 0.10 ppm.

[0136] The secondary component (B) preferably has one or more, more preferably all of the following properties in any combination:

- [0137] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 1.0 to 5.0 g/10 min, more preferably from 1.3 to 3.0 g/10 min;
- [0138] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 20.0 to 50.0 g/10 min, more preferably from 25.0 to 40.0 g/10 min;
- [0139] a complex viscosity at the frequency of 300 rad/s, eta₃₀₀, of from 500 to 900 Pa·s, more preferably from 600 to 850 Pa·s;
- [0140] a complex viscosity at the frequency of 0.05 rad/s, eta_0.05, of from 15000 to 30000 Pa·s, more preferably from 17500 to 27500 Pa·s;
- [0141] a Shore D hardness, measured after 15 s according to ISO 868, Shore D 15 s, of from 50.0 to 70.0, more preferably of from 55.0 to 65.0,
- [0142] a Shore D hardness, measured after 1 s according to ISO 868, Shore D 1 s, of from 55.0 to 75.0, more preferably of from 58.0 to 70.0,
- [0143] a Shore D hardness, measured after 3 s according to ISO 868, Shore D 3 s, of from 55.0 to 75.0, more preferably of from 58.0 to 70.0,
- [0144] a strain hardening modulus, SH modulus, of from 20.0 to 35.0 MPa, more preferably from 22.5 to 32.5 MPa,
- [0145] a Charpy notched impact strength at 23° C., Charpy NIS 23° C., of from 8.0 to 20.0 kJ/m², more preferably from 10.0 to 17.5 kJ/m²,
- [0146] a Charpy notched impact strength at 0° C., Charpy NIS 0° C., of from 4.0 to 15.0 kJ/m², more preferably from 6.0 to 12.5 kJ/m²,
- [0147] a tensile stress at break of from 25 to 50 MPa, more preferably from 28 to 40 MPa,
- [0148] a tensile strain at break of from 700 to 1000%, more preferably from 800 to 950%,
- [0149] an environmental stress crack resistance, ESCR, of at least 2500 hours, more preferably at least 3000 hours.

Second Virgin High-Density Polyethylene (C)

[0153] The mixed-plastic-polyethylene composition of the invention comprises a second virgin high-density polyethylene (C).

[0154] The second virgin high-density polyethylene (C) preferably has one or more, more preferably all of the following properties in any combination

- [0155] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
- [0156] a density from 945 to 965 kg/m³;
- [0157] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR;
- [0158] a limonene content below 0.10 ppm.

[0159] It is further preferred that the second virgin high-density polyethylene (C) has one or both of the following properties

- [0160] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 1.0 to 10.0 g/10 min, preferably from 3.0 to 8.0 g/10 min; and/or
- [0161] a polydispersity index (PI) of from 2.5 to 3.5 s⁻¹; and/or
- [0162] W_COPof from 0.5 to 5.0, more preferably from 0.5 to 2.0

Mixed-Plastic-Polyethylene Composition

[0166] The mixed-plastic-polyethylene composition as described herein is especially suitable for wire and cable applications, such as jacketing applications.

- [0168] having
  - [0169] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min;
  - [0170] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;
- [0171] the mixed-plastic-polyethylene composition comprising
  - [0172] a total amount of ethylene units (C2 units) of from 92.0 to 97.0 wt.-%, and
  - [0173] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.5 to 6.65 wt.-%,
  - [0174] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
- [0175] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0176] wherein the mixed-plastic-polyethylene composition comprises
- [0177] one or more in any combination of, more preferably all of:
  - [0178] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0179] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0180] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
- [0181] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0183] In said aspect the mixed-plastic-polyethylene composition is preferably obtainable by blending and extruding

- [0184] a) 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A) wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm; and wherein the mixed-plastic-polyethylene primary blend (A) has
  - [0185] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0186] a density of from 945 to 990 kg/m³,
  - [0187] optionally a shear thinning index SHI_2.7/210of 30 to 60, more preferably 35 to 50
  - [0188] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0189] and a content of units derived from ethylene of 70 to 95 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0190] b) 35.0 to 68.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, the secondary component (B) having
  - [0191] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min;
  - [0192] a density of from 940 to 970 kg/m³, preferably 955 to 970 kg/m³,
  - [0193] a shear thinning index SHI_2.7/210of 15 to 30
  - [0194] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0195] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B), and
  - [0196] preferably a limonene content below 0.10 ppm,
- [0197] c) 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C) having
  - [0198] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0199] a density from 945 to 965 kg/m³,
  - [0200] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0201] preferably a limonene content below 0.10 ppm.

[0202] The mixed-plastic-polyethylene composition preferably comprises

- [0203] a total amount of ethylene units (C2 units) of from 92.0 to 95.0 wt.-%, preferably from 92.0 to 93.0 wt.-%,
- [0204] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 2.50 to 6.65 wt.-%, more preferably from 4.0 wt.-% to 6.65 wt.-%, still more preferably from 5.0 wt.-% to 6.65 wt.-%,
- [0205] a total amount of units having 4 carbon atoms (C4 units) of from 0.50 wt.-% to 2.20 wt.-%, more preferably from 1.00 wt.-% to 2.00 wt.-%, still more preferably from 1.10 wt.-% to 1.50 wt.-%;
  - [0206] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0207] wherein the mixed-plastic-polyethylene composition comprises
- [0208] one or more in any combination of, more preferably all of:
  - [0209] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0210] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0211] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
- [0212] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0213] In a further preferred embodiment, the mixed-plastic-polyethylene composition comprises

- [0214] a total amount of ethylene units (C2 units) of from 91.0 to 94.0 wt.-%,
- [0215] a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 5.0 to 6.65 wt.-%, and
- [0216] a total amount of units having 4 carbon atoms (C4 units) of from 1.10 wt.-% to 1.50 wt.-%.
- [0217] with the total amounts of C2 units, continuous C3 units and units having 4 carbon atoms being based on the total weight amount of monomer units in the composition and measured according to quantitative ¹³C{¹H} NMR measurement and
- [0218] wherein the mixed-plastic-polyethylene composition comprises
- [0219] one or more in any combination of, more preferably all of:
  - [0220] a total amount of units having 3 carbon atoms as isolated peaks in the NMR spectrum (isolated C3 units) of from 0.00 wt.-% to 0.15 wt.-%, more preferably from 0.00 wt.-% to 0.10 wt.-%, still more preferably from 0.00 wt.-% to 0.05 wt.-%;
  - [0221] a total amount of units having 6 carbon atoms (C6 units) of from 0.00 wt.-% to 0.50 wt.-%, more preferably from 0.00 wt.-% to 0.45 wt.-%, still more preferably from 0.00 wt.-% to 0.40 wt.-%;
  - [0222] a total amount of units having 7 carbon atoms (C7 units) of from 0.00 wt.-% to 0.20 wt.-%, more preferably from 0.00 wt.-% to 0.15 wt.-%, still more preferably from 0.00 wt.-% to 0.10 wt.-%;
  - [0223] wherein the total amounts of isolated C3 units, C4 units, C6 units, C7 units are based on the total weight amount of monomer units in the composition and are measured or calculated according to quantitative ¹³C{¹H} NMR measurement.

[0225] The mixed-plastic polyethylene composition according to the present invention has a

- [0226] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min, preferably from 0.3 to 0.5 g/10 min;
- [0227] a density of from 956 to 965 kg/m³, preferably from 958 to 964 kg/m³;

[0231] The mixed-plastic-polyethylene composition according to the present invention is preferably obtainable by blending and extruding

- [0232] a) 30.0 to 60.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0233] b) 35.0 to 68.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0234] c) 2.0 to 20.0 wt.-% of a second virgin high-density polyethylene (C).

[0235] In a preferable embodiment, the composition is obtainable by blending and extruding

- [0236] a) 34.0 to 55.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0237] b) 40.0 to 63.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0238] c) 3.0 to 18.0 wt.-% of a second virgin high-density polyethylene (C).

[0239] In a further preferable embodiment, the composition is obtainable by blending and extruding

- [0240] a) 37.0 to 52.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0241] b) 42.0 to 59.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0242] c) 4.0 to 16.0 wt.-% of a second virgin high-density polyethylene (C).

[0243] In a yet further preferable embodiment, the composition is obtainable by blending and extruding

- [0244] a) 40.0 to 50.0 wt.-% of a mixed-plastic-polyethylene primary recycling blend (A)
- [0245] b) 45.0 to 55.0 wt.-% of a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, and
- [0246] c) 5.0 to 15.0 wt.-% of a second virgin high-density polyethylene (C).

[0247] The mixed-plastic-polyethylene primary recycling blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) are generally defined as described above or below.

[0248] The mixed plastic polyethylene composition preferably has an impact strength at 23° C. (ISO 179-1 eA) of from 6.0 to 15.0 kJ/m², preferably from 6.0 to 10.0 kJ/m².

[0249] Further, the mixed plastic polyethylene composition preferably has an impact strength at 0° C. (according to ISO 179-1 eA) of from 4.0 to 10.0 kJ/m², more preferably from 4.0 to 8.0 kJ/m².

[0251] It is preferred that that the mixed-plastic-polyethylene composition preferably has

- [0252] a Shore D hardness, measured according to ISO 868 with a measuring time of 1 s, Shore D 1 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0, and/or
- [0253] a Shore D hardness, measured according to ISO 868 with a measuring time of 3 s, Shore D 3 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0, and/or
- [0254] a Shore D hardness, measured according to ISO 868 with a measuring time of 15 s, Shore D 15 s, of from 55.0 to 70.0, more preferably from 57.0 to 68.0 and most preferably from 60.0 to 65.0.

[0255] The mixed-plastic-polyethylene composition preferably has one or more, preferably all of the following rheological properties, in any combination:

- [0256] a shear thinning index SHI_2.7/210of from 35.0 to 50.0, more preferably from 37 to 45 and/or
- [0257] a complex viscosity at 0.05 rad/s, eta_0.05, of from 29000 to 45000 Pa·s, more preferably from 33000 to 42000 Pa·s, and/or
- [0258] a complex viscosity at 300 rad/s, eta₃₀₀, of from 650 to 850 Pa·s, more preferably from 700 to 800 Pa·s, and/or
- [0259] a polydispersity index PI of from 2.2 to 3.0 s⁻¹, more preferably from 2.4 to 2.8 s⁻¹.

[0260] Further, the mixed-plastic-polyethylene composition preferably has one or more, preferably all of the following melt flow rate properties, in any combination:

- [0261] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.3 to 0.5 g/10 min, and/or
- [0262] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 1.2 to 2.0 g/10 min, and/or
- [0263] a melt flow rate (ISO 1133, 21.6 kg, 190° C.) of from 30.0 to 50.0 g/10 min.

[0268] The mixed-plastic-polyethylene composition preferably also has an ESCR (Bell test failure time of at least 2000 hours, preferably at least 2500 hours, most preferably at least 3000 hours.

Article

[0269] The present application is further directed to an article comprising the mixed-plastic-polyethylene composition as described above.

[0272] All preferred aspects and embodiments as described above shall also hold for the article.

Process

[0274] The process according to the present invention comprises the steps of:

- [0275] a. providing a mixed-plastic-polyethylene primary recycling blend (A) in an amount of 30.0 to 60.0 wt.-% based on the overall weight of the composition,
  - [0276] wherein 90.0 wt.-%, preferably 95.0 wt.-%, more preferably 100.0 wt.-% of the mixed-plastic-polyethylene primary blend (A) originates from post-consumer waste having a limonene content of from 0.10 to 500 ppm and wherein the mixed-plastic-polyethylene primary blend has
  - [0277] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.5 g/10 min, preferably from 0.4 to 1.3 g/10 min,
  - [0278] a density of from 945 to 990 kg/m³,
  - [0279] optionally a shear thinning index SHI_2.7/210of 30 to 60, preferably 35 to 50
  - [0280] optionally a polydispersity index from 1.2 to 2.5 s⁻¹, more preferably 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0281] and a content of units derived from ethylene of 70.0 to 95.0 wt.-% as determined by quantitative ¹³C{¹H}-NMR,
- [0282] b. providing a secondary component (B) being a virgin high-density polyethylene (HDPE1) optionally blended with carbon black, in an amount of 35.0 to 68.0 wt.-% based on the overall weight of the composition, the secondary component (B) having
  - [0283] a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 1.2 g/10 min, preferably from 0.2 to 0.6 g/10 min,
  - [0284] a density of from 940 to 970 kg/m³, preferably 955 to 970 kg/m³,
  - [0285] a shear thinning index SHI_2.7/210of 15 to 30,
  - [0286] a polydispersity index from 1.6 to 2.2 s⁻¹as obtained from rheological measurement,
  - [0287] optionally a carbon black content of 1.5 to 3.0 wt.-% with respect to the secondary component (B); and
  - [0288] preferably, a limonene content below 0.10 ppm.
- [0289] c. providing a second virgin high-density polyethylene (C) in an amount of 2.0 to 20.0 wt.-%, based on the overall weight of the composition, the second virgin high-density polyethylene having
  - [0290] a melt flow rate (ISO 1133, 5.0 kg, 190° C.) of from 0.05 to 0.5 g/10 min, preferably from 0.10 to 0.3 g/10 min;
  - [0291] a density from 945 to 965 kg/m³,
  - [0292] a comonomer content in the range from 2.50 to 3.50 wt.-%, as determined by quantitative ¹³C{¹H}-NMR,
  - [0293] preferably a limonene content below 0.10 ppm
- [0294] d. melting and mixing the blend of mixed-plastic-polyethylene primary blend (A), the secondary component (B) and the second virgin high-density polyethylene (C) in an extruder, optionally a twin screw extruder, and
- [0295] e. optionally pelletizing the obtained mixed-plastic-polyethylene composition.

[0296] All preferred aspects, definitions and embodiments as described above shall also hold for the process.

Experimental Part

1. Test Methods

[0297] a) Melt Flow Rate

[0299] b) Density

[0300] Density is measured according to ISO 1183-187. Sample preparation is done by compression moulding in accordance with ISO 17855-2.

[0301] c) Comonomer Content

[0302] Quantification of C6 in the Reactor-Made Virgin High-Density Polyethylene (PE3)

[0303] Quantitative nuclear-magnetic resonance (NMR) spectroscopy was used to quantify the comonomer content of the polymer.

[0308] The amount of ethylene was quantified using the integral of the bulk methylene (I_δ) sites at 30.00 ppm. This integral included the γ site as well as the 3B4 sites from 1-hexene.

[0311] J. Randall, Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, C29, 201.
klimke06
[0312] Klimke, K., Parkinson, M., Piel, C., Kaminsky, W., Spiess, H. W., Wilhelm, M., Macromol. Chem. Phys. 2006; 207:382.
parkinson07
[0313] Parkinson, M., Klimke, K., Spiess, H. W., Wilhelm, M., Macromol. Chem. Phys. 2007; 208:2128.
pollard04
[0314] Pollard, M., Klimke, K., Graf, R., Spiess, H. W., Wilhelm, M., Sperber, O., Piel, C., Kaminsky, W., Macromolecules 2004; 37:813.
filip05
[0315] Filip, X., Tripon, C., Filip, C., J. Mag. Resn. 2005, 176, 239
griffin07
[0316] Griffin, J. M., Tripon, C., Samoson, A., Filip, C., and Brown, S. P., Mag. Res. in Chem. 2007 45, S1, S198
castignolles09
[0317] Castignolles, P., Graf, R., Parkinson, M., Wilhelm, M., Gaborieau, M., Polymer 50 (2009) 2373
Quantification of C2, iPP (Continuous C3), LDPE and Polyethylene Short Chain Branches in the Commercially Prepared Polethylenes

[0322] The weight percent of the C2 fraction and the polypropylene can be quantified according following equations:
wt_C2fraction=fC_C2total*100/(fC_C2total+fC_PP)
wt_PP=fC_PP*100/(fC_C2total+fC_PP)

References

[0326] zhou07 Zhou, Z., Kuemmerle, R., Qiu, X., Redwine, D., Cong, R., Taha, A., Baugh, D. Winniford, B., J. Mag. Reson. 187 (2007) 225
[0327] busico07 Busico, V., Carbonniere, P., Cipullo, R., Pellecchia, R., Severn, J., Talarico, G., Macromol. Rapid Commun. 2007, 28, 1128
[0328] singh09 Singh, G., Kothari, A., Gupta, V., Polymer Testing 28 5 (2009), 475
[0329] randall89 J. Randall, Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, C29, 201.
[0330] brandolini00 A. J. Brandolini, D. D. Hills, NMR Spectra of Polymers and Polymer Additives, Marcel Dekker Inc., 2000

[0331] d) Impact Strength

[0333] e) Tensile Testing of 5A Specimen

[0335] f) Rheological Measurements

[0336] Dynamic Shear Measurements (Frequency Sweep Measurements)

[0339] If the applied strain is within the linear viscoelastic regime, the resulting sinusoidal stress response can be given by
σ(t)=σ₀sin(ωt+δ) (2)

[0340] where

[0341] σ₀and γ₀are the stress and strain amplitudes, respectively

[0342] ω is the angular frequency

[0343] δ is the phase shift (loss angle between applied strain and stress response)

[0344] t is the time

[0346]

\begin{matrix} G^{'} = \frac{σ_{0}}{γ_{0}} \cos δ [Pa] & (3) \end{matrix}

\begin{matrix} G^{″} = \frac{σ_{0}}{γ_{0}} \sin δ [Pa] & (4) \end{matrix}

\begin{matrix} G^{*} = G^{'} + {iG}^{″} [Pa] & (5) \end{matrix}

\begin{matrix} η^{*} = η^{'} - i η^{″} [Pa . s] & (6) \end{matrix}

\begin{matrix} η^{'} = \frac{G^{″}}{ω} [Pa . s] & (7) \end{matrix}

\begin{matrix} η^{″} = \frac{G^{'}}{ω} [Pa . s] & (8) \end{matrix}

[0347] The determination of so-called Shear Thinning Index, which correlates with MWD and is independent of Mw, is done as described in equation 9.

[0348]

\begin{matrix} {SHI}_{(x / y)} = \frac{{Eta}^{*} for (G^{*} = x kPa)}{{Eta}^{*} for (G^{*} = y kPa)} & (9) \end{matrix}

[0350] The values of storage modulus (G′), loss modulus (G″), complex modulus (G*) and complex viscosity (η*) were obtained as a function of frequency (ω).

[0353] The elasticity balance tan_0.05/tan₃₀₀is defined as the ratio of the loss tangent tan_0.05and the loss tangent tan₃₀₀.

[0355] The polydispersity index, PI, is defined by equation 11.

[0356]

\begin{matrix} PI = \frac{10^{5}}{G^{'} (ω_{COP})}, ω_{COP} = ω for (G^{'} = G^{″}) & (11) \end{matrix}

where ω_COPis the cross-over angular frequency, determined as the angular frequency for which the storage modulus, G′, equals the loss modulus, G″.

References

[0358] [1] Rheological characterization of polyethylene fractions” Heino, E. L., Lehtinen, A., Tanner J., Seppälä, J., Neste Oy, Porvoo, Finland, Theor. Appl. Rheol., Proc. Int. Congr. Rheol, 11th (1992), 1, 360-362
[0359] [2] The influence of molecular structure on some rheological properties of polyethylene”, Heino, E. L., Borealis Polymers Oy, Porvoo, Finland, Annual Transactions of the Nordic Rheology Society, 1995).
[0360] [3] Definition of terms relating to the non-ultimate mechanical properties of polymers, Pure & Appl. Chem., Vol. 70, No. 3, pp. 701-754, 1998.

[0361] g) ESCR (Bell Test, h)

[0363] h) Shore D Hardness

[0364] Two different Shore D hardness measurements were conducted:

[0366] Secondly, Shore D hardness is determined according to ASTM D2240-03. The same samples as for the Shore D hardness according to ISO 868 were used.

[0367] i) Strain Hardening (SH) Modulus

[0369] The true strain, λ, is calculated from the length, I (mm), and the gauge length, I0 (mm), as shown by Equation 1.

[0370]

\begin{matrix} λ = \frac{l}{l_{0}} = 1 + \frac{Δ l}{l_{0}} & (1) \end{matrix}

[0371] The Neo-Hookean constitutive model (Equation 3) is used to fit the true strain-true stress data from which <Gp> (MPa) for 8<λ<12 is calculated.

[0372]

\begin{matrix} σ_{true} = \frac{〈 Gp 〉}{20} (λ^{2} - \frac{1}{λ}) + C & (3) \end{matrix}

where C is a mathematical parameter of the constitutive model describing the yield stress extrapolated to λ=0.

[0374] The PE granules of materials were compression molded in sheets of 0.30 mm thickness according to the press parameters as provided in ISO 17855-2.

[0376] Next, the test pieces were punched from the pressed sheets. The specimen geometry of the modified ISO 37:1994 Type 3 (FIG. 3) was used.

[0377] The sample has a large clamping area to prevent grip slip, dimensions given in Table 1.

[0378]

TABLE 1

Dimensions of Modified ISO 37:1994 Type 3
Dimension		Size (mm)

L	start length between clamps	30.0 +/− 0.5
I0	Gauge length	12.5 +/− 0.1
I1	Prismatic length	16.0 +/− 1.0
I3	Total length	70
R1	Radius	10.0 +/− 0.03
R2	Radius	8.06 +/− 0.03
b1	Prismatic width	4.0 +/− 0.01
b2	Clamp width	20.0 +/− 1.0
h	Thickness	0.30 + 0.05/0.30 − 0.03

[0379] The punching procedure is carried out in such a way that no deformation, crazes or other irregularities are present in the test pieces.

[0380] The thickness of the samples was measured at three points of the parallel area of the specimen; the lowest measured value of the thickness of these measurements was used for data treatment.

- [0381] 1. The following procedure is performed on a universal tensile testing machine having controlled temperature chamber and non-contact extensometer:
- [0382] 2. Condition the test specimens for at least 30 min in the temperature chamber at a temperature of (80±1) ° C. prior to starting the test.
- [0383] 3. Clamp the test piece on the upper side.
- [0384] 4. Close the temperature chamber.
- [0385] 5. Close the lower clamp after reaching the temperature of (80±1) ° C.
- [0386] 6. Equilibrate the sample for 1 min between the clamps, before the load is applied and measurement starts.
- [0387] 7. Add a pre-load of 0.5 N at a speed of 5 mm/min.
- [0388] 8. Extend the test specimen along its major axis at a constant traverse speed (20 mm/min) until the sample breaks.
- [0389] During the test, the load sustained by the specimen is measured with a load cell of 200 N. The elongation is measured with a non-contact extensometer.